DuPont™ Surlyn® 1601 Sodium Ionomer Resin for Blown and Cast Film

Category Polymer , Film , Thermoplastic , Ionomer , Ionomer, Film Grade
Manufacturer DuPont
Trade Name Surlyn®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Surlyn® 1601 Sodium Ionomer Resin for Blown and Cast Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Surlyn® 1601 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, seafood and cheese packaging; Cereal liners; Medical/pharmaceutical packaging; Powdered/granular food and nonfood pouches; Carded display/skin packaging films; Edible oil, motor oil, and other liquid product pouches; Snack structuresData provided by the manufacturer, DuPont Packaging.
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
ASTM D792
Melt Flow 1.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 350 %
350 %
ASTM D882
Film Elongation at Break, TD 400 %
400 %
ASTM D882
Secant Modulus, MD 0.250 GPa
36.3 ksi
ASTM D882
Secant Modulus, TD 0.0450 GPa
6.53 ksi
ASTM D882
Impact 310
310
Spencer Impact in J/cm; ASTM D3420
Elmendorf Tear Strength, MD 0.700 g/micron
17.8 g/mil
Elmendorf Tear Strength, TD 0.700 g/micron
17.8 g/mil
Dart Drop 11.8 g/micron
300 g/mil
ASTM D1709B
Seal Strength 2000 g/25 mm
2000 g/in
Seal Bar Temp approx. 115-145°C
Hot Tack Strength 2000 g/25 mm
2000 g/in
Seal Bar Temp approx. 115-145°C; Packforsk Method
Film Tensile Strength at Break, MD 33.8 MPa
4900 psi
ASTM D882
Film Tensile Strength at Break, TD 40.7 MPa
5900 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 98.0 °C
208 °F
DSC; ASTM D3418
Vicat Softening Point 74.0 °C
165 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 3.0 %
3.0 %
ASTM D1003
Gloss 75 %
75 %
20°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 204 °C
399 °F