DuPont Performance Polymers Zytel® ST800HSL BK152 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® ST800HSL BK152 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® ST800HSL BK152 is a heat stabilized Super Tough black polyamide 66 resin. It offers outstanding impact resistance, high productivity and laser markability.Information provided by DuPont
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Thickness 2.00 mm
0.018 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.018 cm/cm

@Thickness 2.00 mm
0.018 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 51.0 MPa

@Temperature 23.0 °C
7400 psi

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Break 38 %

@Temperature 23.0 °C
38 %

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Yield 6.0 %

@Temperature 23.0 °C
6.0 %

@Temperature 73.4 °F
DAM; ISO 527
Tensile Modulus 2.003 GPa

@Temperature 23.0 °C
290.5 ksi

@Temperature 73.4 °F
DAM; ISO 527
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
DAM; ISO 179/1eU
Charpy Impact, Notched 7.20 J/cm²

@Temperature 23.0 °C
34.3 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature 23.0 - 55.0 °C
61.1 µin/in-°F

@Temperature 73.4 - 131 °F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 120 µm/m-°C

@Temperature 23.0 - 55.0 °C
66.7 µin/in-°F

@Temperature 73.4 - 131 °F
DAM; ISO 11359-1/-2
Melting Point 263 °C
505 °F
DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 61.0 °C
142 °F
DAM; ISO 75-1/-2
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
DAM; IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
DAM; UL94
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
DAM; IEC 60695-11-10
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
DAM; UL94
Processing Properties Metric English Comments
Melt Temperature 290 °C
554 °F
DAM; optimum
280 - 300 °C
536 - 572 °F
DAM
Mold Temperature 70.0 °C
158 °F
DAM; Optimum
50.0 - 90.0 °C
122 - 194 °F
DAM
Drying Temperature 80.0 °C
176 °F
DAM
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
DAM; Dehumidified Dryer
Moisture Content <= 0.20 %
<= 0.20 %
DAM
Descriptive Properties Value Comments
Appearance Black Color
Forms Pellets
Generic Nylon 66
Material Status Preliminary Data
Part Marking Code >PA66-HI<
ISO 11469
Processing Method injection Molding
Product Category Toughened Resins
Region Available - Americas Yes
Resin Identification PA66-HI
ISO 1043
RoHS Compliance Contact Manufacturer