DuPont Performance Polymers Zytel® RS LC3060 NC010 Nylon 610  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer DuPont Performance Polymers
Trade Name Zytel® RS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® RS LC3060 NC010 Nylon 610  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced Renewably Sourced Medium Viscosity Polyamide 610 Developed for Extrusion Zytel RS LC3060 NC010 is a renewable sourced polyamide 610 containing a minimum of 60% renewable sourced ingredient by weight. It is an unreinforced medium viscosityInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
DAM; ISO 1183
Water Absorption 3.3 %

@Thickness 2.00 mm
 3.3 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.40 %

@Thickness 2.00 mm
 1.40 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 150 cm³/g
150 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 49.8 MPa

@Strain 10.0 %
 7220 psi

@Strain 10.0 %
 DAM; ISO 527-1/-2
0.940 MPa

@Strain 0.230 %,
Temperature 90.0 °C
 136 psi

@Strain 0.230 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
3.04 MPa

@Strain 1.20 %,
Temperature 150 °C
 441 psi

@Strain 1.20 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3.27 MPa

@Strain 0.230 %,
Temperature 23.0 °C
 474 psi

@Strain 0.230 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
4.71 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 683 psi

@Strain 0.200 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
4.90 MPa

@Strain 0.200 %,
Temperature -20.0 °C
 711 psi

@Strain 0.200 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
5.13 MPa

@Strain 1.15 %,
Temperature 90.0 °C
 744 psi

@Strain 1.15 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
5.49 MPa

@Strain 0.310 %,
Temperature 40.0 °C
 796 psi

@Strain 0.310 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
5.79 MPa

@Strain 0.210 %,
Temperature -20.0 °C
 840 psi

@Strain 0.210 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
6.03 MPa

@Strain 0.240 %,
Temperature 0.000 °C
 875 psi

@Strain 0.240 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
7.57 MPa

@Strain 0.300 %,
Temperature 0.000 °C
 1100 psi

@Strain 0.300 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
10.57 MPa

@Strain 0.450 %,
Temperature -40.0 °C
 1533 psi

@Strain 0.450 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
12.18 MPa

@Strain 1.45 %,
Temperature 40.0 °C
 1767 psi

@Strain 1.45 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
12.5 MPa

@Strain 11.67 %,
Temperature 150 °C
 1810 psi

@Strain 11.67 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
14.23 MPa

@Strain 23.18 %,
Temperature 150 °C
 2064 psi

@Strain 23.18 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
14.86 MPa

@Strain 35.5 %,
Temperature 150 °C
 2155 psi

@Strain 35.5 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
15.19 MPa

@Strain 19.25 %,
Temperature 150 °C
 2203 psi

@Strain 19.25 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
18.17 MPa

@Strain 9.13 %,
Temperature 90.0 °C
 2635 psi

@Strain 9.13 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
21.99 MPa

@Strain 0.890 %,
Temperature -40.0 °C
 3189 psi

@Strain 0.890 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
22.24 MPa

@Strain 21.15 %,
Temperature 90.0 °C
 3226 psi

@Strain 21.15 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
23.32 MPa

@Strain 34.44 %,
Temperature 90.0 °C
 3382 psi

@Strain 34.44 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
33.19 MPa

@Strain 11.16 %,
Temperature 40.0 °C
 4814 psi

@Strain 11.16 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
33.99 MPa

@Strain 1.54 %,
Temperature -20.0 °C
 4930 psi

@Strain 1.54 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
36.77 MPa

@Strain 22.45 %,
Temperature 40.0 °C
 5333 psi

@Strain 22.45 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
43.29 MPa

@Strain 8.09 %,
Temperature 23.0 °C
 6279 psi

@Strain 8.09 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
47.72 MPa

@Strain 18.98 %,
Temperature 23.0 °C
 6921 psi

@Strain 18.98 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
58.6 MPa

@Strain 2.83 %,
Temperature -20.0 °C
 8500 psi

@Strain 2.83 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
63.72 MPa

@Strain 4.75 %,
Temperature 23.0 °C
 9242 psi

@Strain 4.75 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
65.39 MPa

@Strain 7.37 %,
Temperature 0.000 °C
 9484 psi

@Strain 7.37 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
65.99 MPa

@Strain 17.08 %,
Temperature 0.000 °C
 9571 psi

@Strain 17.08 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
68.57 MPa

@Strain 3.50 %,
Temperature -40.0 °C
 9945 psi

@Strain 3.50 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
69.76 MPa

@Strain 3.89 %,
Temperature 0.000 °C
 10120 psi

@Strain 3.89 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
77.7 MPa

@Strain 8.87 %,
Temperature -20.0 °C
 11300 psi

@Strain 8.87 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
78.53 MPa

@Strain 4.44 %,
Temperature -40.0 °C
 11390 psi

@Strain 4.44 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
82.6 MPa

@Strain 8.14 %,
Temperature -20.0 °C
 12000 psi

@Strain 8.14 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
91.95 MPa

@Strain 9.00 %,
Temperature -40.0 °C
 13340 psi

@Strain 9.00 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
93.2 MPa

@Strain 7.10 %,
Temperature -40.0 °C
 13500 psi

@Strain 7.10 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Tensile Strength, Yield 58.0 MPa
8410 psi
DAM; ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
DAM; Nominal; ISO 527-1/-2
Elongation at Yield 5.0 %
5.0 %
DAM; ISO 527-1/-2
Tensile Modulus 1.20 GPa
174 ksi
50%RH; ISO 527-1/-2
2.00 GPa
290 ksi
DAM; ISO 527-1/-2
Secant Modulus 0.139 GPa

@Strain 26.54 %,
Temperature 40.0 °C
 20.2 ksi

@Strain 26.54 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.21014 GPa

@Strain 22.78 %,
Temperature 23.0 °C
 30.479 ksi

@Strain 22.78 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.297 GPa

@Strain 11.16 %,
Temperature 40.0 °C
 43.1 ksi

@Strain 11.16 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.535 GPa

@Strain 8.09 %,
Temperature 23.0 °C
 77.6 ksi

@Strain 8.09 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.689 GPa

@Strain 11.28 %,
Temperature -20.0 °C
 100 ksi

@Strain 11.28 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
0.840 GPa

@Strain 1.45 %,
Temperature 40.0 °C
 122 ksi

@Strain 1.45 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.853 GPa

@Strain 10.82 %,
Temperature -40.0 °C
 124 ksi

@Strain 10.82 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
0.887 GPa

@Strain 7.37 %,
Temperature 0.000 °C
 129 ksi

@Strain 7.37 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
1.09 GPa

@Strain 8.71 %,
Temperature -40.0 °C
 157 ksi

@Strain 8.71 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
1.34 GPa

@Strain 4.75 %,
Temperature 23.0 °C
 195 ksi

@Strain 4.75 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
1.42 GPa

@Strain 0.230 %,
Temperature 23.0 °C
 206 ksi

@Strain 0.230 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1.77 GPa

@Strain 4.44 %,
Temperature -40.0 °C
 257 ksi

@Strain 4.44 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
1.77 GPa

@Strain 0.310 %,
Temperature 40.0 °C
 257 ksi

@Strain 0.310 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
1.79 GPa

@Strain 3.89 %,
Temperature 0.000 °C
 260 ksi

@Strain 3.89 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
1.96 GPa

@Strain 3.50 %,
Temperature -40.0 °C
 284 ksi

@Strain 3.50 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
2.07 GPa

@Strain 2.83 %,
Temperature -20.0 °C
 300 ksi

@Strain 2.83 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
2.21 GPa

@Strain 1.54 %,
Temperature -20.0 °C
 320 ksi

@Strain 1.54 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2