DuPont Performance Polymers Zytel® RS LC1000 BK385 Nylon 1010

Category Polymer , Thermoplastic , Nylon
Manufacturer DuPont Performance Polymers
Trade Name Zytel® RS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® RS LC1000 BK385 Nylon 1010.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
UV Stabilized Renewably Sourced Polyamide 1010 Developed for Extrusion Zytel RS LC1000 BK385 is a renewable sourced Polyamide 1010 containing a minimum of 90% renewably sourced ingredient by weight. The material is flexible unreinforced UV and heat staInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
DAM; ISO 1183
Moisture Absorption 1.00 %

@Thickness 2.00 mm
 1.00 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 130 cm³/g
130 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 0.270 MPa

@Strain 0.0700 %,
Temperature 150 °C
 39.2 psi

@Strain 0.0700 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
0.300 MPa

@Strain 0.0800 %,
Temperature 150 °C
 43.5 psi

@Strain 0.0800 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
0.450 MPa

@Strain 0.0300 %,
Temperature -40.0 °C
 65.3 psi

@Strain 0.0300 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
0.450 MPa

@Strain 0.100 %,
Temperature 90.0 °C
 65.3 psi

@Strain 0.100 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
0.480 MPa

@Strain 0.0200 %,
Temperature -40.0 °C
 69.6 psi

@Strain 0.0200 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
0.490 MPa

@Strain 0.0900 %,
Temperature 90.0 °C
 71.1 psi

@Strain 0.0900 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
0.750 MPa

@Strain 0.0400 %,
Temperature -20.0 °C
 109 psi

@Strain 0.0400 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
0.840 MPa

@Strain 0.0800 %,
Temperature 40.0 °C
 122 psi

@Strain 0.0800 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.840 MPa

@Strain 0.0500 %,
Temperature -20.0 °C
 122 psi

@Strain 0.0500 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
0.930 MPa

@Strain 0.0200 %,
Temperature 0.000 °C
 135 psi

@Strain 0.0200 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
1.03 MPa

@Strain 0.0700 %,
Temperature 40.0 °C
 149 psi

@Strain 0.0700 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
1.29 MPa

@Strain 0.0600 %,
Temperature 23.0 °C
 187 psi

@Strain 0.0600 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1.39 MPa

@Strain 0.0500 %,
Temperature 0.000 °C
 202 psi

@Strain 0.0500 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
1.70 MPa

@Strain 0.0600 %,
Temperature 23.0 °C
 247 psi

@Strain 0.0600 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
1.78 MPa

@Strain 0.100 %,
Temperature -40.0 °C
 258 psi

@Strain 0.100 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
1.92 MPa

@Strain 0.110 %,
Temperature -40.0 °C
 278 psi

@Strain 0.110 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
2.85 MPa

@Strain 0.110 %,
Temperature 0.000 °C
 413 psi

@Strain 0.110 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
3.15 MPa

@Strain 0.170 %,
Temperature -20.0 °C
 457 psi

@Strain 0.170 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
3.37 MPa

@Strain 0.140 %,
Temperature -20.0 °C
 489 psi

@Strain 0.140 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
3.69 MPa

@Strain 0.180 %,
Temperature -40.0 °C
 535 psi

@Strain 0.180 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
3.72 MPa

@Strain 0.180 %,
Temperature -40.0 °C
 540 psi

@Strain 0.180 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
4.22 MPa

@Strain 0.250 %,
Temperature 23.0 °C
 612 psi

@Strain 0.250 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
4.37 MPa

@Strain 0.180 %,
Temperature 0.000 °C
 634 psi

@Strain 0.180 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
4.71 MPa

@Strain 0.190 %,
Temperature 0.000 °C
 683 psi

@Strain 0.190 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
4.78 MPa

@Strain 2.86 %,
Temperature 150 °C
 693 psi

@Strain 2.86 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
5.09 MPa

@Strain 0.230 %,
Temperature 23.0 °C
 738 psi

@Strain 0.230 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
5.35 MPa

@Strain 0.250 %,
Temperature -40.0 °C
 776 psi

@Strain 0.250 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
5.45 MPa

@Strain 0.250 %,
Temperature -40.0 °C
 790 psi

@Strain 0.250 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
5.74 MPa

@Strain 0.230 %,
Temperature -20.0 °C
 833 psi

@Strain 0.230 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
5.84 MPa

@Strain 3.20 %,
Temperature 150 °C
 847 psi

@Strain 3.20 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
6.48 MPa

@Strain 0.430 %,
Temperature 40.0 °C
 940 psi

@Strain 0.430 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
10.0 MPa

@Strain 13.37 %,
Temperature 150 °C
 1450 psi

@Strain 13.37 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
11.04 MPa

@Strain 2.94 %,
Temperature 90.0 °C
 1601 psi

@Strain 2.94 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
11.12 MPa

@Strain 14.0 %,
Temperature 150 °C
 1613 psi

@Strain 14.0 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
11.26 MPa

@Strain 24.48 %,
Temperature 150 °C
 1633 psi

@Strain 24.48 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
11.43 MPa

@Strain 70.4 %,
Temperature 150 °C
 1658 psi

@Strain 70.4 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
11.6 MPa

@Strain 100.03 %,
Temperature 150 °C
 1680 psi

@Strain 100.03 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
12.25 MPa

@Strain 25.96 %,
Temperature 150 °C
 1777 psi

@Strain 25.96 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
12.31 MPa

@Strain 71.22 %,
Temperature 150 °C
 1785 psi

@Strain 71.22 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
12.48 MPa

@Strain 100.05 %,
Temperature 150 °C
 1810 psi

@Strain 100.05 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
12.64 MPa

@Strain 4.33 %,
Temperature 90.0 °C
 1833 psi

@Strain 4.33 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
19.82 MPa

@Strain 14.51 %,
Temperature 90.0 °C
 2875 psi

@Strain 14.51 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
19.95 MPa

@Strain 2.38 %,
Temperature 40.0 °C
 2894 psi

@Strain 2.38 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
21.17 MPa

@Strain 73.09 %,
Temperature 90.0 °C
 3070 psi

@Strain 73.09 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
21.22 MPa

@Strain 26.5 %,
Temperature 90.0 °C
 3078 psi

@Strain 26.5 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
21.41 MPa

@Strain 13.33 %,
Temperature 90.0 °C
 3105 psi

@Strain 13.33 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
21.59 MPa

@Strain 100.03 %,
Temperature 90.0 °C
 3131 psi

@Strain 100.03 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
22.9 MPa

@Strain 72.74 %,
Temperature 90.0 °C
 3320 psi

@Strain 72.74 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
22.97 MPa

@Strain 25.83 %,
Temperature 90.0 °C
 3332 psi

@Strain 25.83 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
23.42 MPa

@Strain 100.03 %,
Temperature 90.0 °C
 3397 psi

@Strain 100.03 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
24.01 MPa

@Strain 1.04 %,
Temperature -20.0 °C
 3482 psi

@Strain 1.04 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
30.88 MPa

@Strain 1.41 %,
Temperature 0.000 °C
 4479 psi

@Strain 1.41 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
34.21 MPa

@Strain 70.99 %,
Temperature 40.0 °C
 4962 psi

@Strain 70.99 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
34.57 MPa

@Strain 100.03 %,
Temperature 40.0 °C
 5014 psi

@Strain 100.03 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
36.0 MPa

@Strain 12.5 %,
Temperature 40.0 °C
 5220 psi

@Strain 12.5 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
37.15 MPa

@Strain 24.59 %,
Temperature 40.0 °C
 5388 psi

@Strain 24.59 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
38.31 MPa

@Strain 68.85 %,
Temperature 40.0 °C
 5556 psi

@Strain 68.85 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
39.49 MPa

@Strain 100.05 %,
Temperature 40.0 °C
 5728 psi

@Strain 100.05 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
39.52 MPa

@Strain 70.06 %,
Temperature 23.0 °C
 5732 psi

@Strain 70.06 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2