DuPont Performance Polymers Zytel® RS 32CG20HSL BK409 Nylon 610  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer DuPont Performance Polymers
Trade Name Zytel® RS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® RS 32CG20HSL BK409 Nylon 610  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Carbon/Glass Reinforced Renewably Sourced Polyamide 610 Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
DAM; ISO 1183
Moisture Absorption 1.10 %

@Thickness 2.00 mm
 1.10 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
50%RH; ISO 527-1/-2
150 MPa
21800 psi
DAM; ISO 527-1/-2
Tensile Stress 6.46 MPa

@Strain 0.190 %,
Temperature 150 °C
 937 psi

@Strain 0.190 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
6.82 MPa

@Strain 0.250 %,
Temperature 150 °C
 989 psi

@Strain 0.250 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
9.93 MPa

@Strain 0.190 %,
Temperature 90.0 °C
 1440 psi

@Strain 0.190 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
12.41 MPa

@Strain 0.200 %,
Temperature 40.0 °C
 1800 psi

@Strain 0.200 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
15.26 MPa

@Strain 0.360 %,
Temperature 90.0 °C
 2213 psi

@Strain 0.360 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
18.97 MPa

@Strain 0.220 %,
Temperature 23.0 °C
 2751 psi

@Strain 0.220 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
19.98 MPa

@Strain 0.240 %,
Temperature 40.0 °C
 2898 psi

@Strain 0.240 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
24.41 MPa

@Strain 1.58 %,
Temperature 150 °C
 3540 psi

@Strain 1.58 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
24.51 MPa

@Strain 0.230 %,
Temperature 0.000 °C
 3555 psi

@Strain 0.230 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
28.23 MPa

@Strain 1.52 %,
Temperature 150 °C
 4094 psi

@Strain 1.52 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
32.88 MPa

@Strain 0.280 %,
Temperature 23.0 °C
 4769 psi

@Strain 0.280 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
33.05 MPa

@Strain 3.10 %,
Temperature 150 °C
 4794 psi

@Strain 3.10 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
33.07 MPa

@Strain 1.04 %,
Temperature 90.0 °C
 4796 psi

@Strain 1.04 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
34.07 MPa

@Strain 0.300 %,
Temperature 0.000 °C
 4941 psi

@Strain 0.300 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
37.08 MPa

@Strain 0.330 %,
Temperature -40.0 °C
 5378 psi

@Strain 0.330 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
38.7 MPa

@Strain 4.67 %,
Temperature 150 °C
 5610 psi

@Strain 4.67 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
39.37 MPa

@Strain 3.30 %,
Temperature 150 °C
 5710 psi

@Strain 3.30 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
43.06 MPa

@Strain 0.900 %,
Temperature 40.0 °C
 6245 psi

@Strain 0.900 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
45.28 MPa

@Strain 1.70 %,
Temperature 90.0 °C
 6567 psi

@Strain 1.70 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
46.27 MPa

@Strain 5.21 %,
Temperature 150 °C
 6711 psi

@Strain 5.21 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
48.46 MPa

@Strain 2.25 %,
Temperature 90.0 °C
 7029 psi

@Strain 2.25 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
57.93 MPa

@Strain 0.830 %,
Temperature 23.0 °C
 8402 psi

@Strain 0.830 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
58.12 MPa

@Strain 3.66 %,
Temperature 90.0 °C
 8430 psi

@Strain 3.66 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
60.1 MPa

@Strain 0.600 %,
Temperature 0.000 °C
 8720 psi

@Strain 0.600 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
60.39 MPa

@Strain 0.920 %,
Temperature 40.0 °C
 8759 psi

@Strain 0.920 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
60.53 MPa

@Strain 3.23 %,
Temperature 90.0 °C
 8779 psi

@Strain 3.23 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
66.11 MPa

@Strain 1.88 %,
Temperature 40.0 °C
 9588 psi

@Strain 1.88 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
70.36 MPa

@Strain 4.98 %,
Temperature 90.0 °C
 10200 psi

@Strain 4.98 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
73.41 MPa

@Strain 0.720 %,
Temperature 23.0 °C
 10650 psi

@Strain 0.720 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
77.81 MPa

@Strain 0.750 %,
Temperature 0.000 °C
 11290 psi

@Strain 0.750 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
81.14 MPa

@Strain 3.15 %,
Temperature 40.0 °C
 11770 psi

@Strain 3.15 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
84.22 MPa

@Strain 0.760 %,
Temperature -40.0 °C
 12220 psi

@Strain 0.760 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
85.28 MPa

@Strain 1.61 %,
Temperature 23.0 °C
 12370 psi

@Strain 1.61 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
87.57 MPa

@Strain 1.87 %,
Temperature 40.0 °C
 12700 psi

@Strain 1.87 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
88.98 MPa

@Strain 0.720 %,
Temperature -40.0 °C
 12910 psi

@Strain 0.720 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
94.99 MPa

@Strain 1.08 %,
Temperature 0.000 °C
 13780 psi

@Strain 1.08 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
102.6 MPa

@Strain 3.19 %,
Temperature 40.0 °C
 14880 psi

@Strain 3.19 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
103.08 MPa

@Strain 2.68 %,
Temperature 23.0 °C
 14951 psi

@Strain 2.68 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
106.47 MPa

@Strain 1.23 %,
Temperature 23.0 °C
 15442 psi

@Strain 1.23 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
113.94 MPa

@Strain 1.22 %,
Temperature 0.000 °C
 16526 psi

@Strain 1.22 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
123.68 MPa

@Strain 1.75 %,
Temperature 0.000 °C
 17938 psi

@Strain 1.75 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
127.4 MPa

@Strain 1.24 %,
Temperature -40.0 °C
 18480 psi

@Strain 1.24 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
129.46 MPa

@Strain 2.04 %,
Temperature 23.0 °C
 18777 psi

@Strain 2.04 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
131.91 MPa

@Strain 1.12 %,
Temperature -40.0 °C
 19132 psi

@Strain 1.12 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
143.2 MPa

@Strain 1.89 %,
Temperature 0.000 °C
 20770 psi

@Strain 1.89 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
161.04 MPa

@Strain 1.76 %,
Temperature -40.0 °C
 23357 psi

@Strain 1.76 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
167.64 MPa

@Strain 1.62 %,
Temperature -40.0 °C
 24314 psi

@Strain 1.62 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
189.16 MPa

@Strain 2.39 %,
Temperature -40.0 °C
 27435 psi

@Strain 2.39 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Elongation at Break 5.0 %
5.0 %
DAM; ISO 527-1/-2
5.0 %
5.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 8.00 GPa
1160 ksi
50%RH; ISO 527-1/-2
11.0 GPa
1600 ksi
DAM; ISO 527-1/-2
Flexural Modulus 9.90 GPa
1440 ksi
DAM; ISO 178
Secant Modulus 0.811 GPa

@Strain 9.29 %,
Temperature 100 °C
 118 ksi

@Strain 9.29 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
0.868 GPa

@Strain 7.25 %,
Temperature 100 °C
 126 ksi

@Strain 7.25 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
1.10 GPa

@Strain 6.39 %,
Temperature 100 °C
 160 ksi

@Strain 6.39 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
1.19 GPa

@Strain 4.91 %,
Temperature 100 °C
 172 ksi

@Strain 4.91 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
1.43 GPa

@Strain 6.56 %,
Temperature 40.0 °C
 207 ksi

@Strain 6.56 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
1.55 GPa

@Strain 3.87 %,
Temperature 100 °C
 225 ksi

@Strain 3.87 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
1.65 GPa

@Strain 6.71 %,
Temperature 40.0 °C
 240 ksi

@Strain 6.71 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
1.65 GPa

@Strain 2.96 %,
Temperature 100 °C
 240 ksi

@Strain 2.96 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2