DuPont Performance Polymers Zytel® RS 3261TL NC010 Nylon 610  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer DuPont Performance Polymers
Trade Name Zytel® RS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® RS 3261TL NC010 Nylon 610  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Toughened Renewably Sourced Polyamide 610 Developed for Injection Molding Zytel RS 3261TL NC010 is a renewably sourced polyamide 610 resin containing a minimum of 47% renewably sourced ingredient by weight. It is an unreinforced and toughened resin forInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
DAM; ISO 1183
Moisture Absorption 1.20 %

@Thickness 2.00 mm
 1.20 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.018 cm/cm
0.018 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 0.480 MPa

@Strain 0.260 %,
Temperature 150 °C
 69.6 psi

@Strain 0.260 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
0.940 MPa

@Strain 0.250 %,
Temperature 90.0 °C
 136 psi

@Strain 0.250 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
0.970 MPa

@Strain 0.240 %,
Temperature 90.0 °C
 141 psi

@Strain 0.240 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
1.39 MPa

@Strain 0.950 %,
Temperature 150 °C
 202 psi

@Strain 0.950 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
1.42 MPa

@Strain 0.200 %,
Temperature 40.0 °C
 206 psi

@Strain 0.200 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
2.90 MPa

@Strain 0.280 %,
Temperature 23.0 °C
 421 psi

@Strain 0.280 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3.75 MPa

@Strain 0.200 %,
Temperature 0.000 °C
 544 psi

@Strain 0.200 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
3.91 MPa

@Strain 0.240 %,
Temperature 23.0 °C
 567 psi

@Strain 0.240 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
5.01 MPa

@Strain 0.250 %,
Temperature 0.000 °C
 727 psi

@Strain 0.250 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
6.28 MPa

@Strain 4.92 %,
Temperature 150 °C
 911 psi

@Strain 4.92 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
6.29 MPa

@Strain 6.01 %,
Temperature 150 °C
 912 psi

@Strain 6.01 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
7.14 MPa

@Strain 0.710 %,
Temperature 40.0 °C
 1040 psi

@Strain 0.710 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
8.52 MPa

@Strain 11.52 %,
Temperature 150 °C
 1240 psi

@Strain 11.52 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
8.78 MPa

@Strain 9.81 %,
Temperature 150 °C
 1270 psi

@Strain 9.81 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
9.81 MPa

@Strain 4.08 %,
Temperature 90.0 °C
 1420 psi

@Strain 4.08 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
9.85 MPa

@Strain 19.43 %,
Temperature 150 °C
 1430 psi

@Strain 19.43 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
10.49 MPa

@Strain 4.49 %,
Temperature 90.0 °C
 1521 psi

@Strain 4.49 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
10.63 MPa

@Strain 20.26 %,
Temperature 150 °C
 1542 psi

@Strain 20.26 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
12.55 MPa

@Strain 0.560 %,
Temperature -40.0 °C
 1820 psi

@Strain 0.560 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
13.27 MPa

@Strain 0.680 %,
Temperature -40.0 °C
 1925 psi

@Strain 0.680 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
13.97 MPa

@Strain 8.87 %,
Temperature 90.0 °C
 2026 psi

@Strain 8.87 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
14.61 MPa

@Strain 9.21 %,
Temperature 90.0 °C
 2119 psi

@Strain 9.21 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
15.67 MPa

@Strain 3.72 %,
Temperature 40.0 °C
 2273 psi

@Strain 3.72 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
16.47 MPa

@Strain 17.43 %,
Temperature 90.0 °C
 2389 psi

@Strain 17.43 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
17.0 MPa

@Strain 15.9 %,
Temperature 90.0 °C
 2470 psi

@Strain 15.9 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
22.06 MPa

@Strain 8.44 %,
Temperature 40.0 °C
 3200 psi

@Strain 8.44 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
25.33 MPa

@Strain 15.31 %,
Temperature 40.0 °C
 3674 psi

@Strain 15.31 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
25.76 MPa

@Strain 5.15 %,
Temperature 40.0 °C
 3736 psi

@Strain 5.15 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
27.31 MPa

@Strain 1.70 %,
Temperature 0.000 °C
 3961 psi

@Strain 1.70 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
28.94 MPa

@Strain 10.26 %,
Temperature 40.0 °C
 4197 psi

@Strain 10.26 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
29.08 MPa

@Strain 1.97 %,
Temperature 23.0 °C
 4218 psi

@Strain 1.97 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
30.0 MPa

@Strain 1.61 %,
Temperature -40.0 °C
 4350 psi

@Strain 1.61 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
30.65 MPa

@Strain 1.48 %,
Temperature -40.0 °C
 4445 psi

@Strain 1.48 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
31.03 MPa

@Strain 21.01 %,
Temperature 40.0 °C
 4501 psi

@Strain 21.01 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
31.52 MPa

@Strain 1.95 %,
Temperature 0.000 °C
 4572 psi

@Strain 1.95 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
33.07 MPa

@Strain 10.8 %,
Temperature 23.0 °C
 4796 psi

@Strain 10.8 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
40.94 MPa

@Strain 3.73 %,
Temperature 0.000 °C
 5938 psi

@Strain 3.73 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
41.94 MPa

@Strain 4.38 %,
Temperature 23.0 °C
 6083 psi

@Strain 4.38 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
43.55 MPa

@Strain 2.55 %,
Temperature -40.0 °C
 6316 psi

@Strain 2.55 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
44.36 MPa

@Strain 6.26 %,
Temperature 0.000 °C
 6434 psi

@Strain 6.26 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
48.88 MPa

@Strain 3.94 %,
Temperature 0.000 °C
 7089 psi

@Strain 3.94 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
51.03 MPa

@Strain 2.89 %,
Temperature -40.0 °C
 7401 psi

@Strain 2.89 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
63.04 MPa

@Strain 4.77 %,
Temperature -40.0 °C
 9143 psi

@Strain 4.77 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
66.22 MPa

@Strain 4.81 %,
Temperature -40.0 °C
 9604 psi

@Strain 4.81 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
Tensile Strength, Yield 32.0 MPa
4640 psi
50%RH; ISO 527-1/-2
40.0 MPa
5800 psi
DAM; ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
DAM; Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 5.5 %
5.5 %
DAM; ISO 527-1/-2
30 %
30 %
50%RH; ISO 527-1/-2
Tensile Modulus 0.800 GPa
116 ksi
50%RH; ISO 527-1/-2
1.50 GPa
218 ksi
DAM; ISO 527-1/-2
Secant Modulus 0.0517 GPa

@Strain 31.47 %,
Temperature 100 °C
 7.50 ksi

@Strain 31.47 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
0.0531 GPa

@Strain 33.11 %,
Temperature 100 °C
 7.70 ksi

@Strain 33.11 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
0.090024 GPa

@Strain 16.64 %,
Temperature 100 °C
 13.057 ksi

@Strain 16.64 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
0.0977 GPa

@Strain 16.26 %,
Temperature 100 °C
 14.2 ksi

@Strain 16.26 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
0.107 GPa

@Strain 24.76 %,
Temperature 40.0 °C
 15.5 ksi

@Strain 24.76 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.198 GPa

@Strain 4.87 %,
Temperature 100 °C
 28.8 ksi

@Strain 4.87 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
0.217 GPa

@Strain 4.47 %,
Temperature 100 °C
 31.4 ksi

@Strain 4.47 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
0.230 GPa

@Strain 10.1 %,
Temperature 40.0 °C
 33.4 ksi

@Strain 10.1 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.246 GPa

@Strain 12.0 %,
Temperature 40.0 °C
 35.7 ksi

@Strain 12.0 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.306 GPa

@Strain 10.8 %,
Temperature 23.0 °C
 44.4 ksi

@Strain 10.8 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2