- DuPont Performance Polymers Zytel® PLUS PLS95G35DH1 BK031 Nylon
DuPont Performance Polymers Zytel® PLUS PLS95G35DH1 BK031 Nylon
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® PLUS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® PLUS PLS95G35DH1 BK031 Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® PLS95G35DH1 BK031is a high flow 35% glass reinforced PA using SHIELD Technology, only from DuPont, combining excellent surface appearance, excellent welding and fatigue retention, exceptional resistance in hot air & hot engine oil.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | DAM; ISO 1183 |
| Filler Content | 35 % | 35 % | DAM |
| Water Absorption | 1.8 % @Temperature 23.0 °C |
1.8 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm |
0.0020 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa @Temperature 23.0 °C |
19600 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 210 MPa @Temperature 23.0 °C |
30500 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 7.0 % @Temperature 23.0 °C |
7.0 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 7.50 GPa @Temperature 23.0 °C |
1090 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 11.0 GPa @Temperature 23.0 °C |
1600 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Strength | 316 MPa @Temperature 23.0 °C |
45800 psi @Temperature 73.4 °F |
DAM; ISO 178 |
| Flexural Modulus | 9.80 GPa @Temperature 23.0 °C |
1420 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
| Charpy Impact Unnotched | 6.80 J/cm² @Temperature -30.0 °C |
32.4 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU |
| 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |
| 8.70 J/cm² @Temperature 23.0 °C |
41.4 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
52.8 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
| Melting Point | 266 °C | 511 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C | 505 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DAM; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.70e+14 ohm-cm @Temperature 23.0 °C |
6.70e+14 ohm-cm @Temperature 73.4 °F |
50%RH; IEC 60093 |
| 7.00e+14 ohm-cm @Temperature 23.0 °C |
7.00e+14 ohm-cm @Temperature 73.4 °F |
50%RH; ASTM D257 | |
| 3.00e+16 ohm-cm @Temperature 23.0 °C |
3.00e+16 ohm-cm @Temperature 73.4 °F |
DAM; ASTM D257 | |
| 3.00e+16 ohm-cm @Temperature 23.0 °C |
3.00e+16 ohm-cm @Temperature 73.4 °F |
DAM; IEC 60093 | |
| Surface Resistance | 4.50e+14 ohm @Temperature 23.0 °C |
4.50e+14 ohm @Temperature 73.4 °F |
50%RH; IEC 60093 |
| 5.00e+14 ohm @Temperature 23.0 °C |
5.00e+14 ohm @Temperature 73.4 °F |
50%RH; ASTM D257 | |
| 1.00e+15 ohm @Temperature 23.0 °C |
1.00e+15 ohm @Temperature 73.4 °F |
DAM; ASTM D257 | |
| 1.00e+15 ohm @Temperature 23.0 °C |
1.00e+15 ohm @Temperature 73.4 °F |
DAM; IEC 60093 | |
| Comparative Tracking Index | >= 600 V @Temperature 23.0 °C |
>= 600 V @Temperature 73.4 °F |
DAM; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum |
| 280 - 300 °C | 536 - 572 °F | DAM | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Features | Copolymer | DAM |
| Flow, Good | DAM | |
| Thermal Stability, Good | DAM | |
| Filler | Glass Reinforced | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 6 | DAM |
| Material Status | Preliminary Data | DAM |
| Part Marking Code | >PA-GF35< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Glass Reinforced Resins | DAM |
| SHIELD Technology Resins | DAM | |
| Region Available - Global | Yes | DAM |
| Resin Identification | PA-GF35 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
| Uses | Automotive Applications | DAM |
| Automotive Under the Hood | DAM | |
| High Temperature Applications | DAM |