DuPont Performance Polymers Zytel® PLS 95G50DH2 BK261 Nylon 6  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel® PLS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® PLS 95G50DH2 BK261 Nylon 6  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass Reinforced Heat Stabilized Polyamide Zytel PLS95G50DH2 BK261is a high flow 50% glass reinforced PA nylon resin using SHIELD Technology only from DuPont providing exceptional Heat ResistanceInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
DAM; ISO 1183
Water Absorption 1.3 %

@Thickness 2.00 mm
 1.3 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.30 %

@Thickness 2.00 mm
 1.30 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 175 MPa
25400 psi
50%RH; ISO 527-1/-2
247 MPa
35800 psi
DAM; ISO 527-1/-2
Tensile Stress 13.89 MPa

@Strain 0.230 %,
Temperature 150 °C
 2015 psi

@Strain 0.230 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
23.81 MPa

@Strain 0.290 %,
Temperature 90.0 °C
 3453 psi

@Strain 0.290 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
25.3 MPa

@Strain 0.280 %,
Temperature 90.0 °C
 3670 psi

@Strain 0.280 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
25.84 MPa

@Strain 0.240 %,
Temperature 40.0 °C
 3748 psi

@Strain 0.240 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
26.59 MPa

@Strain 0.490 %,
Temperature 180 °C
 3857 psi

@Strain 0.490 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
30.95 MPa

@Strain 0.230 %,
Temperature 23.0 °C
 4489 psi

@Strain 0.230 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
34.0 MPa

@Strain 0.580 %,
Temperature 150 °C
 4930 psi

@Strain 0.580 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
40.36 MPa

@Strain 1.01 %,
Temperature 150 °C
 5854 psi

@Strain 1.01 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
49.43 MPa

@Strain 1.35 %,
Temperature 180 °C
 7169 psi

@Strain 1.35 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
55.12 MPa

@Strain 1.89 %,
Temperature 150 °C
 7994 psi

@Strain 1.89 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
56.75 MPa

@Strain 1.01 %,
Temperature 90.0 °C
 8231 psi

@Strain 1.01 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
57.07 MPa

@Strain 0.610 %,
Temperature 40.0 °C
 8277 psi

@Strain 0.610 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
57.56 MPa

@Strain 1.34 %,
Temperature 150 °C
 8348 psi

@Strain 1.34 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
60.9 MPa

@Strain 0.830 %,
Temperature 90.0 °C
 8830 psi

@Strain 0.830 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
61.68 MPa

@Strain 2.33 %,
Temperature 180 °C
 8946 psi

@Strain 2.33 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
61.83 MPa

@Strain 0.520 %,
Temperature 23.0 °C
 8968 psi

@Strain 0.520 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
65.38 MPa

@Strain 2.87 %,
Temperature 150 °C
 9483 psi

@Strain 2.87 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
69.9 MPa

@Strain 3.39 %,
Temperature 180 °C
 10100 psi

@Strain 3.39 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
72.42 MPa

@Strain 2.24 %,
Temperature 150 °C
 10500 psi

@Strain 2.24 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
75.57 MPa

@Strain 1.75 %,
Temperature 90.0 °C
 10960 psi

@Strain 1.75 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
79.73 MPa

@Strain 0.530 %,
Temperature 40.0 °C
 11560 psi

@Strain 0.530 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
83.11 MPa

@Strain 3.32 %,
Temperature 150 °C
 12050 psi

@Strain 3.32 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
83.55 MPa

@Strain 7.15 %,
Temperature 150 °C
 12120 psi

@Strain 7.15 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
83.98 MPa

@Strain 6.94 %,
Temperature 180 °C
 12180 psi

@Strain 6.94 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
86.04 MPa

@Strain 1.42 %,
Temperature 90.0 °C
 12480 psi

@Strain 1.42 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
86.31 MPa

@Strain 1.14 %,
Temperature 40.0 °C
 12520 psi

@Strain 1.14 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
90.04 MPa

@Strain 2.64 %,
Temperature 90.0 °C
 13060 psi

@Strain 2.64 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
96.96 MPa

@Strain 0.650 %,
Temperature 0.000 °C
 14060 psi

@Strain 0.650 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
97.6 MPa

@Strain 0.980 %,
Temperature 23.0 °C
 14200 psi

@Strain 0.980 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
99.98 MPa

@Strain 7.22 %,
Temperature 150 °C
 14500 psi

@Strain 7.22 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
107.12 MPa

@Strain 2.18 %,
Temperature 90.0 °C
 15536 psi

@Strain 2.18 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
110.72 MPa

@Strain 6.08 %,
Temperature 90.0 °C
 16059 psi

@Strain 6.08 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
111.51 MPa

@Strain 1.83 %,
Temperature 40.0 °C
 16173 psi

@Strain 1.83 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
114.67 MPa

@Strain 0.750 %,
Temperature -20.0 °C
 16632 psi

@Strain 0.750 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
117.29 MPa

@Strain 0.840 %,
Temperature 40.0 °C
 17012 psi

@Strain 0.840 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
128.35 MPa

@Strain 1.56 %,
Temperature 23.0 °C
 18616 psi

@Strain 1.56 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
136.48 MPa

@Strain 0.990 %,
Temperature 0.000 °C
 19795 psi

@Strain 0.990 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
140.88 MPa

@Strain 5.84 %,
Temperature 90.0 °C
 20433 psi

@Strain 5.84 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
148.97 MPa

@Strain 5.04 %,
Temperature 40.0 °C
 21606 psi

@Strain 5.04 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
149.18 MPa

@Strain 0.990 %,
Temperature 23.0 °C
 21637 psi

@Strain 0.990 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
151.05 MPa

@Strain 1.21 %,
Temperature 40.0 °C
 21908 psi

@Strain 1.21 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
158.89 MPa

@Strain 1.11 %,
Temperature -20.0 °C
 23045 psi

@Strain 1.11 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
171.57 MPa

@Strain 1.40 %,
Temperature 0.000 °C
 24884 psi

@Strain 1.40 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
171.65 MPa

@Strain 1.12 %,
Temperature -20.0 °C
 24896 psi

@Strain 1.12 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
173.12 MPa

@Strain 1.14 %,
Temperature 0.000 °C
 25109 psi

@Strain 1.14 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
180.4 MPa

@Strain 1.71 %,
Temperature 40.0 °C
 26160 psi

@Strain 1.71 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
185.01 MPa

@Strain 1.35 %,
Temperature 23.0 °C
 26833 psi

@Strain 1.35 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
200.73 MPa

@Strain 1.89 %,
Temperature 0.000 °C
 29113 psi

@Strain 1.89 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
208.47 MPa

@Strain 1.63 %,
Temperature -20.0 °C
 30236 psi

@Strain 1.63 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
212.81 MPa

@Strain 1.53 %,
Temperature 0.000 °C
 30866 psi

@Strain 1.53 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
216.06 MPa

@Strain 1.81 %,
Temperature 23.0 °C
 31337 psi

@Strain 1.81 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
239.51 MPa

@Strain 2.40 %,
Temperature 23.0 °C
 34738 psi

@Strain 2.40 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
240.38 MPa

@Strain 2.08 %,
Temperature -20.0 °C
 34864 psi

@Strain 2.08 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
247.32 MPa

@Strain 2.00 %,
Temperature 0.000 °C
 35871 psi

@Strain 2.00 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
251.79 MPa

@Strain 1.92 %,
Temperature -20.0 °C
 36519 psi

@Strain 1.92 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
275.33 MPa

@Strain 2.59 %,
Temperature 0.000 °C
 39933 psi

@Strain 2.59 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
304.62 MPa

@Strain 2.85 %,
Temperature -20.0 °C
 44181 psi

@Strain 2.85 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
Users viewing this material also viewed the following: