DuPont Performance Polymers Zytel® HTN 53G60LRHF BK083 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 53G60LRHF BK083 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
60% Glass Reinforced High Performance Polyamide with High Stiffness and Improved Flow Zytel HTN53G60LRHF BK083 is a 60% glass reinforced lubricated high performance polyamide resin with improved flow. It was developed for structural applications requirInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.72 g/cc
0.0621 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 225 MPa
32600 psi
50%RH; ISO 527-1/-2
265 MPa
38400 psi
DAM; ISO 527-1/-2
Tensile Stress 4.08 MPa

@Strain 0.0600 %,
Temperature 150 °C
592 psi

@Strain 0.0600 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
4.40 MPa

@Strain 0.0600 %,
Temperature 180 °C
638 psi

@Strain 0.0600 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
5.17 MPa

@Strain 0.0600 %,
Temperature 150 °C
750 psi

@Strain 0.0600 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
5.69 MPa

@Strain 0.0400 %,
Temperature 0.000 °C
825 psi

@Strain 0.0400 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
5.88 MPa

@Strain 0.0500 %,
Temperature 23.0 °C
853 psi

@Strain 0.0500 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
5.98 MPa

@Strain 0.0600 %,
Temperature 90.0 °C
867 psi

@Strain 0.0600 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
7.13 MPa

@Strain 0.0600 %,
Temperature -20.0 °C
1030 psi

@Strain 0.0600 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
7.38 MPa

@Strain 0.0500 %,
Temperature 0.000 °C
1070 psi

@Strain 0.0500 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
7.56 MPa

@Strain 0.0500 %,
Temperature 90.0 °C
1100 psi

@Strain 0.0500 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
7.63 MPa

@Strain 0.0600 %,
Temperature -20.0 °C
1110 psi

@Strain 0.0600 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
8.40 MPa

@Strain 0.0400 %,
Temperature 40.0 °C
1220 psi

@Strain 0.0400 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
9.24 MPa

@Strain 0.0400 %,
Temperature 23.0 °C
1340 psi

@Strain 0.0400 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
10.59 MPa

@Strain 0.0400 %,
Temperature 40.0 °C
1536 psi

@Strain 0.0400 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
11.75 MPa

@Strain 0.200 %,
Temperature 150 °C
1704 psi

@Strain 0.200 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
12.49 MPa

@Strain 0.220 %,
Temperature 180 °C
1812 psi

@Strain 0.220 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
15.02 MPa

@Strain 0.230 %,
Temperature 150 °C
2178 psi

@Strain 0.230 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
17.25 MPa

@Strain 0.200 %,
Temperature 90.0 °C
2502 psi

@Strain 0.200 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
22.5 MPa

@Strain 0.210 %,
Temperature 90.0 °C
3260 psi

@Strain 0.210 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
25.67 MPa

@Strain 0.150 %,
Temperature 40.0 °C
3723 psi

@Strain 0.150 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
28.51 MPa

@Strain 0.140 %,
Temperature 23.0 °C
4135 psi

@Strain 0.140 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
29.52 MPa

@Strain 0.130 %,
Temperature 23.0 °C
4282 psi

@Strain 0.130 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
29.75 MPa

@Strain 0.760 %,
Temperature 150 °C
4315 psi

@Strain 0.760 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
30.63 MPa

@Strain 0.800 %,
Temperature 180 °C
4443 psi

@Strain 0.800 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
31.13 MPa

@Strain 0.150 %,
Temperature 0.000 °C
4515 psi

@Strain 0.150 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
31.52 MPa

@Strain 0.150 %,
Temperature 0.000 °C
4572 psi

@Strain 0.150 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
32.16 MPa

@Strain 0.140 %,
Temperature 40.0 °C
4664 psi

@Strain 0.140 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
37.36 MPa

@Strain 0.170 %,
Temperature -20.0 °C
5419 psi

@Strain 0.170 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
37.9 MPa

@Strain 0.240 %,
Temperature 40.0 °C
5500 psi

@Strain 0.240 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
38.73 MPa

@Strain 0.150 %,
Temperature -20.0 °C
5617 psi

@Strain 0.150 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
40.49 MPa

@Strain 0.200 %,
Temperature 23.0 °C
5873 psi

@Strain 0.200 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
40.61 MPa

@Strain 1.01 %,
Temperature 150 °C
5890 psi

@Strain 1.01 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
40.78 MPa

@Strain 1.62 %,
Temperature 150 °C
5915 psi

@Strain 1.62 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
41.26 MPa

@Strain 0.170 %,
Temperature 23.0 °C
5984 psi

@Strain 0.170 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
41.27 MPa

@Strain 1.69 %,
Temperature 180 °C
5986 psi

@Strain 1.69 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
43.31 MPa

@Strain 0.720 %,
Temperature 90.0 °C
6282 psi

@Strain 0.720 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
44.86 MPa

@Strain 0.200 %,
Temperature 40.0 °C
6506 psi

@Strain 0.200 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
46.01 MPa

@Strain 0.210 %,
Temperature 0.000 °C
6673 psi

@Strain 0.210 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
47.63 MPa

@Strain 0.230 %,
Temperature 0.000 °C
6908 psi

@Strain 0.230 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
52.16 MPa

@Strain 0.220 %,
Temperature 23.0 °C
7565 psi

@Strain 0.220 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
52.67 MPa

@Strain 0.210 %,
Temperature -20.0 °C
7639 psi

@Strain 0.210 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
53.08 MPa

@Strain 1.99 %,
Temperature 150 °C
7699 psi

@Strain 1.99 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
54.46 MPa

@Strain 0.260 %,
Temperature 23.0 °C
7899 psi

@Strain 0.260 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
55.7 MPa

@Strain 5.04 %,
Temperature 180 °C
8080 psi

@Strain 5.04 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
56.01 MPa

@Strain 4.77 %,
Temperature 150 °C
8124 psi

@Strain 4.77 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
56.33 MPa

@Strain 0.630 %,
Temperature 90.0 °C
8170 psi

@Strain 0.630 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
56.48 MPa

@Strain 0.200 %,
Temperature -20.0 °C
8192 psi

@Strain 0.200 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
56.96 MPa

@Strain 0.250 %,
Temperature 40.0 °C
8261 psi

@Strain 0.250 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
58.58 MPa

@Strain 7.15 %,
Temperature 180 °C
8496 psi

@Strain 7.15 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
59.14 MPa

@Strain 6.74 %,
Temperature 150 °C
8578 psi

@Strain 6.74 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
60.57 MPa

@Strain 1.49 %,
Temperature 90.0 °C
8785 psi

@Strain 1.49 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
63.55 MPa

@Strain 0.280 %,
Temperature 0.000 °C
9217 psi

@Strain 0.280 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
65.21 MPa

@Strain 0.250 %,
Temperature -20.0 °C
9458 psi

@Strain 0.250 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
70.92 MPa

@Strain 5.53 %,
Temperature 150 °C
10290 psi

@Strain 5.53 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
71.95 MPa

@Strain 0.260 %,
Temperature -20.0 °C
10440 psi

@Strain 0.260 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
74.29 MPa

@Strain 7.80 %,
Temperature 150 °C
10770 psi

@Strain 7.80 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
74.49 MPa

@Strain 0.540 %,
Temperature 40.0 °C
10800 psi

@Strain 0.540 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
82.47 MPa

@Strain 0.390 %,
Temperature 0.000 °C
11960 psi

@Strain 0.390 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
84.81 MPa

@Strain 1.25 %,
Temperature 90.0 °C
12300 psi

@Strain 1.25 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
85.83 MPa

@Strain 4.65 %,
Temperature 90.0 °C
12450 psi

@Strain 4.65 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2