DuPont Performance Polymers Zytel® FR7026V0F NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® FR7026V0F NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® FR7026V0F NC010 is a flame retardant, heat stabilized, polyamide 66 resin for injection molding. It does not contain elemental phosphorous, halogens or heavy metals.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
DAM; ASTM D792
Density 1.16 g/cc
0.0419 lb/in³
DAM; ISO 1183
Water Absorption 2.4 %

@Thickness 1.00 mm,
Temperature 23.0 °C
 2.4 %

@Thickness 0.0394 in,
Temperature 73.4 °F
 Equilibrium 50%RH; DAM; ISO 62, Similar to
8.0 %

@Thickness 1.00 mm,
Temperature 23.0 °C
 8.0 %

@Thickness 0.0394 in,
Temperature 73.4 °F
 Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Thickness 2.00 mm
 0.0090 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 2.00 mm
 0.010 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa

@Temperature 23.0 °C
 11600 psi

@Temperature 73.4 °F
 DAM; ISO 527
Tensile Strength 89.6 MPa

@Temperature 23.0 °C
 13000 psi

@Temperature 73.4 °F
 DAM; ASTM D638
Tensile Stress 1.62 MPa

@Strain 0.100 %,
Temperature 80.0 °C
 235 psi

@Strain 0.100 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
2.87 MPa

@Strain 0.200 %,
Temperature 80.0 °C
 416 psi

@Strain 0.200 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
3.12 MPa

@Strain 0.100 %,
Temperature 60.0 °C
 453 psi

@Strain 0.100 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
3.57 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 518 psi

@Strain 0.100 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
4.01 MPa

@Strain 0.100 %,
Temperature -40.0 °C
 582 psi

@Strain 0.100 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
4.02 MPa

@Strain 0.300 %,
Temperature 80.0 °C
 583 psi

@Strain 0.300 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
4.54 MPa

@Strain 0.100 %,
Temperature 0.000 °C
 658 psi

@Strain 0.100 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
5.11 MPa

@Strain 0.200 %,
Temperature 60.0 °C
 741 psi

@Strain 0.200 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
5.43 MPa

@Strain 0.400 %,
Temperature 80.0 °C
 788 psi

@Strain 0.400 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
6.54 MPa

@Strain 0.500 %,
Temperature 80.0 °C
 949 psi

@Strain 0.500 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
7.04 MPa

@Strain 0.300 %,
Temperature 60.0 °C
 1020 psi

@Strain 0.300 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
7.17 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 1040 psi

@Strain 0.200 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
7.51 MPa

@Strain 0.200 %,
Temperature -40.0 °C
 1090 psi

@Strain 0.200 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
7.56 MPa

@Strain 0.600 %,
Temperature 80.0 °C
 1100 psi

@Strain 0.600 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
8.52 MPa

@Strain 0.400 %,
Temperature 60.0 °C
 1240 psi

@Strain 0.400 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
8.57 MPa

@Strain 0.700 %,
Temperature 80.0 °C
 1240 psi

@Strain 0.700 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
9.17 MPa

@Strain 0.200 %,
Temperature 0.000 °C
 1330 psi

@Strain 0.200 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
9.58 MPa

@Strain 0.800 %,
Temperature 80.0 °C
 1390 psi

@Strain 0.800 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
10.53 MPa

@Strain 0.900 %,
Temperature 80.0 °C
 1527 psi

@Strain 0.900 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
10.68 MPa

@Strain 0.500 %,
Temperature 60.0 °C
 1549 psi

@Strain 0.500 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
10.83 MPa

@Strain 0.300 %,
Temperature 23.0 °C
 1571 psi

@Strain 0.300 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
11.34 MPa

@Strain 0.300 %,
Temperature -40.0 °C
 1645 psi

@Strain 0.300 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
11.67 MPa

@Strain 1.00 %,
Temperature 80.0 °C
 1693 psi

@Strain 1.00 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
12.72 MPa

@Strain 0.600 %,
Temperature 60.0 °C
 1845 psi

@Strain 0.600 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
12.74 MPa

@Strain 1.10 %,
Temperature 80.0 °C
 1848 psi

@Strain 1.10 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
13.62 MPa

@Strain 1.20 %,
Temperature 80.0 °C
 1975 psi

@Strain 1.20 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
13.77 MPa

@Strain 0.300 %,
Temperature 0.000 °C
 1997 psi

@Strain 0.300 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
13.88 MPa

@Strain 0.400 %,
Temperature 23.0 °C
 2013 psi

@Strain 0.400 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
14.43 MPa

@Strain 1.30 %,
Temperature 80.0 °C
 2093 psi

@Strain 1.30 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
14.66 MPa

@Strain 0.700 %,
Temperature 60.0 °C
 2126 psi

@Strain 0.700 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
15.24 MPa

@Strain 1.40 %,
Temperature 80.0 °C
 2210 psi

@Strain 1.40 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
15.3 MPa

@Strain 0.400 %,
Temperature -40.0 °C
 2220 psi

@Strain 0.400 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
16.03 MPa

@Strain 1.50 %,
Temperature 80.0 °C
 2325 psi

@Strain 1.50 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
16.66 MPa

@Strain 0.800 %,
Temperature 60.0 °C
 2416 psi

@Strain 0.800 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
16.76 MPa

@Strain 1.60 %,
Temperature 80.0 °C
 2431 psi

@Strain 1.60 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
17.68 MPa

@Strain 1.70 %,
Temperature 80.0 °C
 2564 psi

@Strain 1.70 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
18.15 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 2632 psi

@Strain 0.500 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
18.28 MPa

@Strain 0.400 %,
Temperature 0.000 °C
 2651 psi

@Strain 0.400 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
18.3 MPa

@Strain 0.900 %,
Temperature 60.0 °C
 2650 psi

@Strain 0.900 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
18.53 MPa

@Strain 1.80 %,
Temperature 80.0 °C
 2688 psi

@Strain 1.80 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
19.17 MPa

@Strain 1.90 %,
Temperature 80.0 °C
 2780 psi

@Strain 1.90 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
19.37 MPa

@Strain 0.500 %,
Temperature -40.0 °C
 2809 psi

@Strain 0.500 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
19.8 MPa

@Strain 2.00 %,
Temperature 80.0 °C
 2870 psi

@Strain 2.00 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
19.81 MPa

@Strain 1.00 %,
Temperature 60.0 °C
 2873 psi

@Strain 1.00 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
20.42 MPa

@Strain 2.10 %,
Temperature 80.0 °C
 2962 psi

@Strain 2.10 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
20.97 MPa

@Strain 2.20 %,
Temperature 80.0 °C
 3041 psi

@Strain 2.20 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
21.32 MPa

@Strain 1.10 %,
Temperature 60.0 °C
 3092 psi

@Strain 1.10 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
21.55 MPa

@Strain 2.30 %,
Temperature 80.0 °C
 3126 psi

@Strain 2.30 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
21.74 MPa

@Strain 0.600 %,
Temperature 23.0 °C
 3153 psi

@Strain 0.600 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
22.04 MPa

@Strain 2.40 %,
Temperature 80.0 °C
 3197 psi

@Strain 2.40 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
22.39 MPa

@Strain 0.500 %,
Temperature 0.000 °C
 3247 psi

@Strain 0.500 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
22.6 MPa

@Strain 2.50 %,
Temperature 80.0 °C
 3280 psi

@Strain 2.50 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
23.01 MPa

@Strain 2.60 %,
Temperature 80.0 °C
 3337 psi

@Strain 2.60 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
23.01 MPa

@Strain 1.20 %,
Temperature 60.0 °C
 3337 psi

@Strain 1.20 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
23.53 MPa

@Strain 0.600 %,
Temperature -40.0 °C
 3413 psi

@Strain 0.600 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
23.54 MPa

@Strain 2.70 %,
Temperature 80.0 °C
 3414 psi

@Strain 2.70 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2