DuPont Performance Polymers Zytel® FG70G50HSLA BK309 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® FG70G50HSLA BK309 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass Reinforced Heat Stabilized Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
1.57 g/cc
0.0567 lb/in³
DAM; ISO 1183
Water Absorption 4.2 %

@Thickness 2.00 mm
 4.2 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.20 %

@Thickness 2.00 mm
 1.20 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 100 cm³/g
100 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
50%RH; ISO 527-1/-2
250 MPa
36300 psi
DAM; ISO 527-1/-2
Elongation at Break 2.3 %
2.3 %
DAM; ISO 527-1/-2
3.2 %
3.2 %
50%RH; ISO 527-1/-2
Tensile Modulus 13.0 GPa
1890 ksi
50%RH; ISO 527-1/-2
17.0 GPa
2470 ksi
DAM; ISO 527-1/-2
Charpy Impact Unnotched 10.0 J/cm²
47.6 ft-lb/in²
DAM; ISO 179/1eU
11.0 J/cm²
52.3 ft-lb/in²
50%RH; ISO 179/1eU
9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eU
9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eU
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
DAM; ISO 179/1eA
2.00 J/cm²
9.52 ft-lb/in²
50%RH; ISO 179/1eA
1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour 10000 MPa

@Time 3600 sec
 1.45e+6 psi

@Time 1.00 hour
 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours 8000 MPa

@Time 3.60e+6 sec
 1.16e+6 psi

@Time 1000 hour
 50%RH; ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C
8.33 µin/in-°F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 75.0 µm/m-°C
41.7 µin/in-°F
DAM; ISO 11359-1/-2
Specific Heat Capacity 1.87 J/g-°C
0.447 BTU/lb-°F
Thermal Conductivity 0.310 W/m-K
2.15 BTU-in/hr-ft²-°F
of melt
0.460 W/m-K
3.19 BTU-in/hr-ft²-°F
of solid
Melting Point 262 °C
504 °F
DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 262 °C
504 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
DAM; ISO 75-1/-2
Vicat Softening Point 255 °C
491 °F
DAM; 50°C/h 50N; ISO 306
Glass Transition Temp, Tg 80.0 °C
176 °F
DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 DAM; IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 DAM; IEC 60695-11-10
Oxygen Index 24 %
24 %
DAM; ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
DAM; IEC 60093
Surface Resistance 4.00e+14 ohm
4.00e+14 ohm
50%RH; IEC 60093
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Emission of organic compounds 6.5 µgC/g
VDA 277
Odour class 3
VDA 270
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Special Characteristics Heat stabilised or stable to heat
UL recognition UL
DAM