DuPont Performance Polymers Zytel® E53 NC010 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® E53 NC010 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced High Viscosity Polyamide 66 Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
| Water Absorption | 8.5 % @Thickness 2.00 mm |
8.5 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Moisture Absorption | 2.70 % @Thickness 2.00 mm |
2.70 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Viscosity Test | 350 cm³/g | 350 cm³/g | DAM; ISO 307 1157 1628 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | DAM; ISO 294-4 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50%RH; ISO 527-1/-2 |
| 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 | |
| Elongation at Break | >= 50 % | >= 50 % | DAM; Nominal; ISO 527-1/-2 |
| >= 50 % | >= 50 % | 50%RH; Nominal; ISO 527-1/-2 | |
| Elongation at Yield | 4.4 % | 4.4 % | DAM; ISO 527-1/-2 |
| 30 % | 30 % | 50%RH; ISO 527-1/-2 | |
| Tensile Modulus | 1.20 GPa | 174 ksi | 50%RH; ISO 527-1/-2 |
| 3.00 GPa | 435 ksi | DAM; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DAM; ISO 179/1eA |
| 4.00 J/cm² | 19.0 ft-lb/in² | 50%RH; ISO 179/1eA | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | DAM; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | DAM; ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | DAM; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | DAM; IEC 60093 |
| Dielectric Constant | 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
DAM; IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Delivery Form | Pellets | |
| Processing | Casting | |
| Coatable | ||
| Film Extrusion | ||
| Other Extrusion | ||
| Profile Extrusion | ||
| Sheet Extrusion | ||
| Regional Availability | Europe | |
| Near East/Africa |
Users viewing this material also viewed the following:
- Nye Lubricants 774LF (NG) Synthetic Oil
- Polimeri Europa Europrene® N 3960 Acrylonitrile-Butadiene Rubber
- SABIC Innovative Plastics Lexan® LUX1814N PC
- Styrolution Luran® S 778 Q42 Colored ASA
- Hexcel® HexWeb® HRP - 3/16 - 12.0 Fiberglass/Phenolic Honeycomb
- A. Schulman COMTUF® 420 Impact Modified PBT
- Carmel Olefins IPETHENE® 470 Low Density Polyethylene
- Overview of materials for Acrylic, UV Stabilized, Molded
Copyright © lookpolymers.com All Rights Reserved