DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
43% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G43HS1L BK104 is a 43% glass fiber reinforced heat stabilized black polyamide 66 resin with superior impact resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
DAM; ISO 1183
Water Absorption 4.9 %

@Thickness 2.00 mm
 4.9 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.50 %

@Thickness 2.00 mm
 1.50 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 137 cm³/g
137 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 169 MPa
24500 psi
DAM; ISO 527-1/-2
Tensile Stress 8.6609 MPa

@Strain 0.200 %,
Temperature 150 °C
 1256.2 psi

@Strain 0.200 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
12.0 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 1740 psi

@Strain 0.100 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
12.2 MPa

@Strain 0.100 %,
Temperature -40.0 °C
 1770 psi

@Strain 0.100 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
18.66 MPa

@Strain 0.500 %,
Temperature 150 °C
 2706 psi

@Strain 0.500 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
25.98 MPa

@Strain 0.800 %,
Temperature 150 °C
 3768 psi

@Strain 0.800 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
38.83 MPa

@Strain 1.60 %,
Temperature 150 °C
 5632 psi

@Strain 1.60 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
61.66 MPa

@Strain 7.00 %,
Temperature 150 °C
 8943 psi

@Strain 7.00 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
66.96 MPa

@Strain 0.600 %,
Temperature 23.0 °C
 9712 psi

@Strain 0.600 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
78.69 MPa

@Strain 0.700 %,
Temperature -40.0 °C
 11410 psi

@Strain 0.700 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
93.42 MPa

@Strain 0.900 %,
Temperature 23.0 °C
 13550 psi

@Strain 0.900 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
114.9 MPa

@Strain 1.20 %,
Temperature 23.0 °C
 16660 psi

@Strain 1.20 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
125.4 MPa

@Strain 1.20 %,
Temperature -40.0 °C
 18180 psi

@Strain 1.20 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
156.6 MPa

@Strain 1.60 %,
Temperature -40.0 °C
 22710 psi

@Strain 1.60 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
227.4 MPa

@Strain 3.10 %,
Temperature -40.0 °C
 32980 psi

@Strain 3.10 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Elongation at Break 3.3 %
3.3 %
DAM; ISO 527-1/-2
Tensile Modulus 11.7 GPa
1700 ksi
DAM; ISO 527-1/-2
Flexural Modulus 10.3 GPa
1490 ksi
DAM; ISO 178
Secant Modulus 2.59 GPa

@Strain 2.90 %,
Temperature 100 °C
 376 ksi

@Strain 2.90 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
3.63 GPa

@Strain 1.50 %,
Temperature 100 °C
 527 ksi

@Strain 1.50 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
4.53 GPa

@Strain 0.800 %,
Temperature 100 °C
 658 ksi

@Strain 0.800 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
5.30 GPa

@Strain 0.400 %,
Temperature 100 °C
 769 ksi

@Strain 0.400 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
5.90 GPa

@Strain 0.100 %,
Temperature 100 °C
 856 ksi

@Strain 0.100 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
7.51 GPa

@Strain 2.00 %,
Temperature 23.0 °C
 1090 ksi

@Strain 2.00 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
8.12 GPa

@Strain 2.60 %,
Temperature -40.0 °C
 1180 ksi

@Strain 2.60 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
9.04 GPa

@Strain 1.40 %,
Temperature 23.0 °C
 1310 ksi

@Strain 1.40 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
9.11 GPa

@Strain 2.00 %,
Temperature -40.0 °C
 1320 ksi

@Strain 2.00 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
10.103 GPa

@Strain 1.00 %,
Temperature 23.0 °C
 1465.3 ksi

@Strain 1.00 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
10.3 GPa

@Strain 1.30 %,
Temperature -40.0 °C
 1490 ksi

@Strain 1.30 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
11.2 GPa

@Strain 0.600 %,
Temperature 23.0 °C
 1620 ksi

@Strain 0.600 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
11.2 GPa

@Strain 0.700 %,
Temperature -40.0 °C
 1630 ksi

@Strain 0.700 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
12.0 GPa

@Strain 0.100 %,
Temperature 23.0 °C
 1740 ksi

@Strain 0.100 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
12.2 GPa

@Strain 0.100 %,
Temperature -40.0 °C
 1770 ksi

@Strain 0.100 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Izod Impact, Notched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
DAM; ISO 180/1A
14.0 kJ/m²

@Temperature -40.0 °C
 6.66 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) 78.0 kJ/m²
37.1 ft-lb/in²
DAM; ISO 180/1U
Charpy Impact Unnotched 9.00 J/cm²
42.8 ft-lb/in²
DAM; ISO 179/1eU
Charpy Impact, Notched 2.30 J/cm²
10.9 ft-lb/in²
DAM; ISO 179/1eA
1.50 J/cm²

@Temperature -40.0 °C
 7.14 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 262 °C
504 °F
DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 261 °C
502 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
DAM; ISO 75-1/-2
Vicat Softening Point 215 °C
419 °F
DAM; 50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 DAM; IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 DAM; IEC 60695-11-10
Oxygen Index 27 %
27 %
DAM; ISO 4589-1/-2
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >PA66-IGF43<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification PA66-IGF43
Special Characteristics Heat stabilised or stable to heat
Users viewing this material also viewed the following: