DuPont Performance Polymers Zytel® 80G14A NC010A Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 80G14A NC010A Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
14% Glass Reinforced Toughened Polyamide 66 Zytel 80G14A NC010A is a 14% glass fiber reinforced toughened high flow polyamide 66 resin. It offers outstanding performance in injection molding applications.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
DAM; ISO 1183
Water Absorption 6.2 %

@Thickness 2.00 mm
 6.2 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.80 %

@Thickness 2.00 mm
 1.80 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 137 cm³/g
137 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 66.0 MPa
9570 psi
50%RH; ISO 527-1/-2
108 MPa
15700 psi
DAM; ISO 527-1/-2
Tensile Stress 3.00 MPa

@Strain 0.0960 %,
Time 3600 sec
 435 psi

@Strain 0.0960 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.103 %,
Time 36000 sec
 435 psi

@Strain 0.103 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.111 %,
Time 360000 sec
 435 psi

@Strain 0.111 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.121 %,
Time 3.60e+6 sec
 435 psi

@Strain 0.121 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.130 %,
Time 3.60e+7 sec
 435 psi

@Strain 0.130 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
9.00 MPa

@Strain 0.349 %,
Time 360000 sec
 1310 psi

@Strain 0.349 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.528 %,
Time 3.60e+6 sec
 1740 psi

@Strain 0.528 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.571 %,
Time 3.60e+7 sec
 1740 psi

@Strain 0.571 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.443 %,
Time 36000 sec
 1740 psi

@Strain 0.443 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.403 %,
Time 3600 sec
 1740 psi

@Strain 0.403 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break 3.8 %
3.8 %
DAM; ISO 527-1/-2
10 %
10 %
50%RH; ISO 527-1/-2
Tensile Modulus 3.40 GPa
493 ksi
50%RH; ISO 527-1/-2
4.80 GPa
696 ksi
DAM; ISO 527-1/-2
1.844 GPa

@Temperature 120 °C
 267.5 ksi

@Temperature 248 °F
 50%RH; ISO 11403-1 -2
1.979 GPa

@Temperature 120 °C
 287.0 ksi

@Temperature 248 °F
 DAM; ISO 11403-1 -2
2.753 GPa

@Temperature 40.0 °C
 399.3 ksi

@Temperature 104 °F
 50%RH; ISO 11403-1 -2
4.597 GPa

@Temperature 40.0 °C
 666.7 ksi

@Temperature 104 °F
 DAM; ISO 11403-1 -2
5.598 GPa

@Temperature -40.0 °C
 811.9 ksi

@Temperature -40.0 °F
 DAM; ISO 11403-1 -2
6.113 GPa

@Temperature -40.0 °C
 886.6 ksi

@Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
Flexural Modulus 4.40 GPa
638 ksi
DAM; ISO 178
Shear Modulus 0.253 GPa

@Temperature 160 °C
 36.7 ksi

@Temperature 320 °F
 DAM; Dynamic; ISO 11403-1 -2
0.287 GPa

@Temperature 120 °C
 41.6 ksi

@Temperature 248 °F
 DAM; Dynamic; ISO 11403-1 -2
0.486 GPa

@Temperature 70.0 °C
 70.5 ksi

@Temperature 158 °F
 DAM; Dynamic; ISO 11403-1 -2
1.00 GPa

@Temperature 20.0 °C
 145 ksi

@Temperature 68.0 °F
 DAM; Dynamic; ISO 11403-1 -2
1.08 GPa

@Temperature -20.0 °C
 157 ksi

@Temperature -4.00 °F
 DAM; Dynamic; ISO 11403-1 -2
1.26 GPa

@Temperature -50.0 °C
 183 ksi

@Temperature -58.0 °F
 DAM; Dynamic; ISO 11403-1 -2
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
DAM; ISO 180/1A
6.00 kJ/m²

@Temperature -40.0 °C
 2.86 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 180/1A
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
DAM; ISO 179/1eU
7.60 J/cm²
36.2 ft-lb/in²
50%RH; ISO 179/1eU
7.10 J/cm²

@Temperature -30.0 °C
 33.8 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eU
9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
DAM; ISO 179/1eA
1.70 J/cm²
8.09 ft-lb/in²
50%RH; ISO 179/1eA
0.600 J/cm²

@Temperature -40.0 °C
 2.86 ft-lb/in²

@Temperature -40.0 °F
 50%RH; ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour 2590 MPa

@Pressure 20.0 MPa,
Temperature 23.0 °C
 376000 psi

@Pressure 2900 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
2830 MPa

@Pressure 15.0 MPa,
Temperature 23.0 °C
 411000 psi

@Pressure 2180 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3030 MPa

@Pressure 10.0 MPa,
Temperature 23.0 °C
 439000 psi

@Pressure 1450 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3110 MPa

@Pressure 5.00 MPa,
Temperature 23.0 °C
 451000 psi

@Pressure 725 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3100 MPa

@Time 3600 sec
 450000 psi

@Time 1.00 hour
 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours 1920 MPa

@Pressure 20.0 MPa,
Temperature 23.0 °C
 279000 psi

@Pressure 2900 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
2130 MPa

@Pressure 15.0 MPa,
Temperature 23.0 °C
 309000 psi

@Pressure 2180 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
2330 MPa

@Pressure 10.0 MPa,
Temperature 23.0 °C
 339000 psi

@Pressure 1450 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
2440 MPa

@Pressure 5.00 MPa,
Temperature 23.0 °C
 354000 psi

@Pressure 725 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
2500 MPa

@Time 3.60e+6 sec
 363000 psi

@Time 1000 hour
 50%RH; ISO 899-1
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
50%RH; IEC 60093
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
DAM; IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
50%RH; IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
 3.5

@Frequency 1.00e+6 Hz
 DAM; IEC 60250
3.8

@Frequency 100 Hz
 3.8

@Frequency 100 Hz
 DAM; IEC 60250
3.9

@Frequency 1.00e+6 Hz
 3.9

@Frequency 1.00e+6 Hz
 50%RH; IEC 60250
7.3

@Frequency 100 Hz
 7.3

@Frequency 100 Hz
 50%RH; IEC 60250
Dielectric Strength 36.0 kV/mm
914 kV/in
DAM; IEC 60243-1
36.5 kV/mm
927 kV/in
50%RH; IEC 60243-1
Dissipation Factor 0.018

@Frequency 100 Hz
 0.018

@Frequency 100 Hz
 50%RH; IEC 60250
0.027

@Frequency 100 Hz
 0.027

@Frequency 100 Hz
 DAM; IEC 60250
0.058

@Frequency 1.00e+6 Hz
 0.058

@Frequency 1.00e+6 Hz
 DAM; IEC 60250