- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Nylon 6
- Nylon 6, 30% Glass Fiber Filled
- DuPont Performance Polymers Zytel® 73G30HSL BK261 Nylon 6 (Unverified Data**)
DuPont Performance Polymers Zytel® 73G30HSL BK261 Nylon 6 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® 73G30HSL BK261 Nylon 6
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® 73G30HSL BK261 is a 30% glass fiber reinforced, heat stabilized, lubricated, black polyamide 6 for injection molding. It has excellent surface appearance and gloss.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | DAM; ISO 1183 |
| Filler Content | 30 % | 30 % | DAM |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 5.70 GPa @Temperature 23.0 °C |
827 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 9.50 GPa @Temperature 23.0 °C |
1380 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Modulus | 6.00 GPa @Temperature 23.0 °C |
870 ksi @Temperature 73.4 °F |
50%RH; ISO 178 |
| 9.00 GPa @Temperature 23.0 °C |
1310 ksi @Temperature 73.4 °F |
DAM; ISO 178 | |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 |
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
DAM; UL 746B |
| 65.0 °C @Thickness 0.800 mm |
149 °F @Thickness 0.0315 in |
DAM; UL 746B | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.800 mm |
149 °F @Thickness 0.0315 in |
DAM; UL 746B |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.800 mm |
149 °F @Thickness 0.0315 in |
DAM; UL 746B |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
DAM; UL 746B | |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; UL94 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; UL94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 °C | 518 °F | DAM; Optimum |
| 260 - 280 °C | 500 - 536 °F | DAM | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Glass fiber reinforcement | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 6 | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA6-GF30< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA6 | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Glass Reinforced Resins | DAM |
| Resin Identification | PA6-GF30 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |