DuPont Performance Polymers Zytel® 70G50HSLA BK039B Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G50HSLA BK039B Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass Reinforced Heat Stabilized Polyamide 66 Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
1.57 g/cc
0.0567 lb/in³
DAM; ISO 1183
Water Absorption 4.2 %

@Thickness 2.00 mm
4.2 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Moisture Absorption 1.20 %

@Thickness 2.00 mm
1.20 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Viscosity 31200 cP

@Shear Rate 5000 1/s,
Temperature 305 °C
31200 cP

@Shear Rate 5000 1/s,
Temperature 581 °F
ISO 11403-1 -2
38800 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
38800 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
ISO 11403-1 -2
49290 cP

@Shear Rate 5000 1/s,
Temperature 285 °C
49290 cP

@Shear Rate 5000 1/s,
Temperature 545 °F
ISO 11403-1 -2
103100 cP

@Shear Rate 500 1/s,
Temperature 305 °C
103100 cP

@Shear Rate 500 1/s,
Temperature 581 °F
ISO 11403-1 -2
130500 cP

@Shear Rate 500 1/s,
Temperature 295 °C
130500 cP

@Shear Rate 500 1/s,
Temperature 563 °F
ISO 11403-1 -2
167800 cP

@Shear Rate 500 1/s,
Temperature 285 °C
167800 cP

@Shear Rate 500 1/s,
Temperature 545 °F
ISO 11403-1 -2
Viscosity Test 100 cm³/g
100 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 210 MPa
30500 psi
50%RH; ISO 527-1/-2
260 MPa
37700 psi
DAM; ISO 527-1/-2
Tensile Stress 16.06 MPa

@Strain 0.250 %,
Temperature 150 °C
2329 psi

@Strain 0.250 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
16.27 MPa

@Strain 0.230 %,
Temperature 180 °C
2360 psi

@Strain 0.230 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
24.39 MPa

@Strain 0.330 %,
Temperature 150 °C
3537 psi

@Strain 0.330 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
37.38 MPa

@Strain 0.320 %,
Temperature 23.0 °C
5422 psi

@Strain 0.320 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
39.23 MPa

@Strain 0.400 %,
Temperature 40.0 °C
5690 psi

@Strain 0.400 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
40.3 MPa

@Strain 0.490 %,
Temperature 90.0 °C
5850 psi

@Strain 0.490 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
40.82 MPa

@Strain 0.450 %,
Temperature 90.0 °C
5920 psi

@Strain 0.450 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
46.14 MPa

@Strain 0.980 %,
Temperature 150 °C
6692 psi

@Strain 0.980 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
50.97 MPa

@Strain 1.05 %,
Temperature 180 °C
7393 psi

@Strain 1.05 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
56.85 MPa

@Strain 0.380 %,
Temperature 40.0 °C
8245 psi

@Strain 0.380 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
58.16 MPa

@Strain 1.03 %,
Temperature 150 °C
8435 psi

@Strain 1.03 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
62.02 MPa

@Strain 1.75 %,
Temperature 150 °C
8995 psi

@Strain 1.75 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
68.69 MPa

@Strain 1.93 %,
Temperature 180 °C
9963 psi

@Strain 1.93 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
69.06 MPa

@Strain 1.06 %,
Temperature 90.0 °C
10020 psi

@Strain 1.06 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
72.29 MPa

@Strain 2.59 %,
Temperature 150 °C
10480 psi

@Strain 2.59 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
73.76 MPa

@Strain 0.420 %,
Temperature -20.0 °C
10700 psi

@Strain 0.420 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
76.36 MPa

@Strain 0.860 %,
Temperature 40.0 °C
11080 psi

@Strain 0.860 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
77.8 MPa

@Strain 1.78 %,
Temperature 150 °C
11300 psi

@Strain 1.78 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
80.2 MPa

@Strain 2.95 %,
Temperature 180 °C
11600 psi

@Strain 2.95 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
81.87 MPa

@Strain 1.11 %,
Temperature 90.0 °C
11870 psi

@Strain 1.11 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
84.37 MPa

@Strain 0.800 %,
Temperature 23.0 °C
12240 psi

@Strain 0.800 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
86.56 MPa

@Strain 1.63 %,
Temperature 90.0 °C
12550 psi

@Strain 1.63 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
87.17 MPa

@Strain 5.71 %,
Temperature 150 °C
12640 psi

@Strain 5.71 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
87.47 MPa

@Strain 0.560 %,
Temperature 23.0 °C
12690 psi

@Strain 0.560 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
91.1 MPa

@Strain 2.66 %,
Temperature 150 °C
13200 psi

@Strain 2.66 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
95.38 MPa

@Strain 0.630 %,
Temperature 0.000 °C
13830 psi

@Strain 0.630 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
95.71 MPa

@Strain 0.670 %,
Temperature 40.0 °C
13880 psi

@Strain 0.670 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
97.7 MPa

@Strain 6.73 %,
Temperature 180 °C
14200 psi

@Strain 6.73 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
99.43 MPa

@Strain 2.33 %,
Temperature 90.0 °C
14420 psi

@Strain 2.33 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
100.54 MPa

@Strain 1.30 %,
Temperature 40.0 °C
14582 psi

@Strain 1.30 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
103.18 MPa

@Strain 1.62 %,
Temperature 90.0 °C
14965 psi

@Strain 1.62 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
105.85 MPa

@Strain 0.640 %,
Temperature -20.0 °C
15352 psi

@Strain 0.640 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
110.54 MPa

@Strain 6.10 %,
Temperature 150 °C
16033 psi

@Strain 6.10 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
112.46 MPa

@Strain 1.21 %,
Temperature 23.0 °C
16311 psi

@Strain 1.21 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
115.46 MPa

@Strain 0.710 %,
Temperature 0.000 °C
16746 psi

@Strain 0.710 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
119.26 MPa

@Strain 1.78 %,
Temperature 40.0 °C
17297 psi

@Strain 1.78 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
120.07 MPa

@Strain 2.19 %,
Temperature 90.0 °C
17415 psi

@Strain 2.19 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
130.16 MPa

@Strain 0.930 %,
Temperature 0.000 °C
18878 psi

@Strain 0.930 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
134.23 MPa

@Strain 1.65 %,
Temperature 23.0 °C
19468 psi

@Strain 1.65 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
134.58 MPa

@Strain 0.890 %,
Temperature 23.0 °C
19519 psi

@Strain 0.890 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
136.34 MPa

@Strain 1.05 %,
Temperature 40.0 °C
19774 psi

@Strain 1.05 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
158.96 MPa

@Strain 1.25 %,
Temperature 0.000 °C
23055 psi

@Strain 1.25 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
164.86 MPa

@Strain 1.40 %,
Temperature 40.0 °C
23911 psi

@Strain 1.40 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
165.48 MPa

@Strain 1.08 %,
Temperature 0.000 °C
24001 psi

@Strain 1.08 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
167.1 MPa

@Strain 1.17 %,
Temperature 23.0 °C
24240 psi

@Strain 1.17 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
184.66 MPa

@Strain 1.23 %,
Temperature -20.0 °C
26783 psi

@Strain 1.23 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
185.69 MPa

@Strain 1.15 %,
Temperature -20.0 °C
26932 psi

@Strain 1.15 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
186.31 MPa

@Strain 1.64 %,
Temperature 0.000 °C
27022 psi

@Strain 1.64 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
198.07 MPa

@Strain 1.36 %,
Temperature 0.000 °C
28728 psi

@Strain 1.36 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
198.66 MPa

@Strain 1.53 %,
Temperature 23.0 °C
28813 psi

@Strain 1.53 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2