DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
13% Glass Reinforced Polyamide 66Zytel 70G13L NC010 is a 13% glass fiber reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
DAM; ISO 1183
Water Absorption 7.6 %

@Thickness 2.00 mm
 7.6 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 2.20 %

@Thickness 2.00 mm
 2.20 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Water Absorption at Saturation 1.7 %
1.7 %
DAM; Immersion 24h; ASTM D570
Viscosity Test 150 cm³/g
150 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
50%RH; ISO 527-1/-2
120 MPa
17400 psi
DAM; ISO 527-1/-2
Tensile Stress 16.074 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 2331.3 psi

@Strain 0.500 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
25.09 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 3639 psi

@Strain 0.500 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
27.636 MPa

@Strain 0.900 %,
Temperature 23.0 °C
 4008.3 psi

@Strain 0.900 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
28.1 MPa

@Strain 0.500 %,
Temperature 0.000 °C
 4080 psi

@Strain 0.500 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
31.4 MPa

@Strain 0.500 %,
Temperature -40.0 °C
 4550 psi

@Strain 0.500 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
32.8 MPa

@Strain 0.500 %,
Temperature -40.0 °C
 4760 psi

@Strain 0.500 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
41.172 MPa

@Strain 1.50 %,
Temperature 23.0 °C
 5971.5 psi

@Strain 1.50 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
50.6 MPa

@Strain 0.900 %,
Temperature 0.000 °C
 7340 psi

@Strain 0.900 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
57.7 MPa

@Strain 1.10 %,
Temperature 0.000 °C
 8370 psi

@Strain 1.10 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
58.02 MPa

@Strain 1.20 %,
Temperature 23.0 °C
 8415 psi

@Strain 1.20 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
59.314 MPa

@Strain 2.60 %,
Temperature 23.0 °C
 8602.8 psi

@Strain 2.60 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
61.9 MPa

@Strain 1.00 %,
Temperature -40.0 °C
 8980 psi

@Strain 1.00 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
66.8 MPa

@Strain 1.20 %,
Temperature 0.000 °C
 9690 psi

@Strain 1.20 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
73.8 MPa

@Strain 1.50 %,
Temperature 0.000 °C
 10700 psi

@Strain 1.50 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
74.8 MPa

@Strain 1.20 %,
Temperature -40.0 °C
 10800 psi

@Strain 1.20 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
76.234 MPa

@Strain 7.00 %,
Temperature 23.0 °C
 11057 psi

@Strain 7.00 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
78.4 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 11400 psi

@Strain 1.30 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
79.3 MPa

@Strain 1.70 %,
Temperature 23.0 °C
 11500 psi

@Strain 1.70 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
86.5 MPa

@Strain 1.60 %,
Temperature 0.000 °C
 12500 psi

@Strain 1.60 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
89.0 MPa

@Strain 2.00 %,
Temperature 0.000 °C
 12900 psi

@Strain 2.00 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
94.05 MPa

@Strain 2.10 %,
Temperature 23.0 °C
 13640 psi

@Strain 2.10 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
98.5 MPa

@Strain 1.70 %,
Temperature -40.0 °C
 14300 psi

@Strain 1.70 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
99.8 MPa

@Strain 1.90 %,
Temperature 0.000 °C
 14500 psi

@Strain 1.90 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
100.6 MPa

@Strain 1.70 %,
Temperature -40.0 °C
 14590 psi

@Strain 1.70 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
119.91 MPa

@Strain 3.10 %,
Temperature 23.0 °C
 17392 psi

@Strain 3.10 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
121 MPa

@Strain 4.50 %,
Temperature 0.000 °C
 17500 psi

@Strain 4.50 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
127.2 MPa

@Strain 2.30 %,
Temperature -40.0 °C
 18450 psi

@Strain 2.30 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Elongation at Break 3.0 %
3.0 %
DAM; ISO 527-1/-2
13 %
13 %
50%RH; ISO 527-1/-2
Tensile Modulus 3.50 GPa
508 ksi
50%RH; ISO 527-1/-2
5.50 GPa
798 ksi
DAM; ISO 527-1/-2
Flexural Strength 100 MPa
14500 psi
50%RH; ISO 178
190 MPa
27600 psi
DAM; ISO 178
Flexural Modulus 2.90 GPa
421 ksi
50%RH; ISO 178
4.80 GPa
696 ksi
DAM; ISO 178
Secant Modulus 0.833 GPa

@Strain 6.00 %,
Temperature 80.0 °C
 121 ksi

@Strain 6.00 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
0.927 GPa

@Strain 7.50 %,
Temperature 80.0 °C
 134 ksi

@Strain 7.50 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
1.22 GPa

@Strain 3.70 %,
Temperature 80.0 °C
 177 ksi

@Strain 3.70 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
1.5125 GPa

@Strain 4.00 %,
Temperature 80.0 °C
 219.37 ksi

@Strain 4.00 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
1.58 GPa

@Strain 2.10 %,
Temperature 80.0 °C
 229 ksi

@Strain 2.10 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
1.70 GPa

@Strain 4.40 %,
Temperature 23.0 °C
 246 ksi

@Strain 4.40 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1.86 GPa

@Strain 2.30 %,
Temperature 80.0 °C
 269 ksi

@Strain 2.30 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
1.88 GPa

@Strain 0.900 %,
Temperature 80.0 °C
 272 ksi

@Strain 0.900 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
1.94 GPa

@Strain 0.500 %,
Temperature 80.0 °C
 281 ksi

@Strain 0.500 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
2.09 GPa

@Strain 3.20 %,
Temperature 23.0 °C
 302 ksi

@Strain 3.20 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
2.27 GPa

@Strain 1.00 %,
Temperature 80.0 °C
 329 ksi

@Strain 1.00 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
2.42 GPa

@Strain 0.500 %,
Temperature 80.0 °C
 351 ksi

@Strain 0.500 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
2.65 GPa

@Strain 1.70 %,
Temperature 23.0 °C
 384 ksi

@Strain 1.70 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3.07 GPa

@Strain 0.900 %,
Temperature 23.0 °C
 445 ksi

@Strain 0.900 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3.2148 GPa

@Strain 0.500 %,
Temperature 23.0 °C
 466.27 ksi

@Strain 0.500 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3.35 GPa

@Strain 3.40 %,
Temperature 0.000 °C
 486 ksi

@Strain 3.40 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
4.008 GPa

@Strain 2.50 %,
Temperature 0.000 °C
 581.3 ksi

@Strain 2.50 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
4.07 GPa

@Strain 2.80 %,
Temperature 23.0 °C
 590 ksi

@Strain 2.80 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
4.37 GPa

@Strain 2.30 %,
Temperature 23.0 °C
 634 ksi

@Strain 2.30 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
4.58 GPa

@Strain 1.90 %,
Temperature 23.0 °C
 664 ksi

@Strain 1.90 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
4.74 GPa

@Strain 1.70 %,
Temperature 0.000 °C
 688 ksi

@Strain 1.70 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
4.835 GPa

@Strain 1.20 %,
Temperature 23.0 °C
 701.3 ksi

@Strain 1.20 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2