DuPont Performance Polymers Zytel® 42A NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 42A NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced High Viscosity Polyamide 66Zytel 42A NC010 is a high viscosity polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
1.14 g/cc
0.0412 lb/in³
DAM; ISO 1183
Water Absorption 8.5 %

@Thickness 2.00 mm
 8.5 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 2.60 %

@Thickness 2.00 mm
 2.60 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 84550 cP

@Shear Rate 5000 1/s,
Temperature 300 °C
 84550 cP

@Shear Rate 5000 1/s,
Temperature 572 °F
 ISO 11403-1 -2
95850 cP

@Shear Rate 5000 1/s,
Temperature 290 °C
 95850 cP

@Shear Rate 5000 1/s,
Temperature 554 °F
 ISO 11403-1 -2
108800 cP

@Shear Rate 5000 1/s,
Temperature 280 °C
 108800 cP

@Shear Rate 5000 1/s,
Temperature 536 °F
 ISO 11403-1 -2
286300 cP

@Shear Rate 500 1/s,
Temperature 300 °C
 286300 cP

@Shear Rate 500 1/s,
Temperature 572 °F
 ISO 11403-1 -2
369600 cP

@Shear Rate 500 1/s,
Temperature 290 °C
 369600 cP

@Shear Rate 500 1/s,
Temperature 554 °F
 ISO 11403-1 -2
438700 cP

@Shear Rate 10.0 1/s,
Temperature 300 °C
 438700 cP

@Shear Rate 10.0 1/s,
Temperature 572 °F
 ISO 11403-1 -2
471600 cP

@Shear Rate 500 1/s,
Temperature 280 °C
 471600 cP

@Shear Rate 500 1/s,
Temperature 536 °F
 ISO 11403-1 -2
655100 cP

@Shear Rate 10.0 1/s,
Temperature 290 °C
 655100 cP

@Shear Rate 10.0 1/s,
Temperature 554 °F
 ISO 11403-1 -2
1.013e+6 cP

@Shear Rate 10.0 1/s,
Temperature 280 °C
 1.013e+6 cP

@Shear Rate 10.0 1/s,
Temperature 536 °F
 ISO 11403-1 -2
Viscosity Test 280 cm³/g
280 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 2.00 MPa

@Strain 0.1575 %,
Time 3600 sec
 290 psi

@Strain 0.1575 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.183167 %,
Time 36000 sec
 290 psi

@Strain 0.183167 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.224 %,
Time 360000 sec
 290 psi

@Strain 0.224 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.278833 %,
Time 3.60e+6 sec
 290 psi

@Strain 0.278833 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.355833 %,
Time 3.60e+7 sec
 290 psi

@Strain 0.355833 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 2.91667 %,
Time 3.60e+7 sec
 1740 psi

@Strain 2.91667 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 2.275 %,
Time 3.60e+6 sec
 1740 psi

@Strain 2.275 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 1.77333 %,
Time 360000 sec
 1740 psi

@Strain 1.77333 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 1.45833 %,
Time 36000 sec
 1740 psi

@Strain 1.45833 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Time 3600 sec,
Strain 1.19 %
 1740 psi

@Time 1.00 hour,
Strain 1.19 %
 50%RH; isochronous; ISO 11403-1 -2
Tensile Strength, Yield 55.0 MPa
7980 psi
50%RH; ISO 527-1/-2
83.0 MPa
12000 psi
DAM; ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
DAM; Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 4.4 %
4.4 %
DAM; ISO 527-1/-2
27 %
27 %
50%RH; ISO 527-1/-2
Tensile Modulus 1.30 GPa
189 ksi
50%RH; ISO 527-1/-2
3.10 GPa
450 ksi
DAM; ISO 527-1/-2
Flexural Modulus 1.07 GPa
155 ksi
50%RH; ISO 178
2.80 GPa
406 ksi
DAM; ISO 178
Shear Modulus 0.1393 GPa

@Temperature 150 °C
 20.20 ksi

@Temperature 302 °F
 DAM; Dynamic; ISO 11403-1 -2
0.1594 GPa

@Temperature 110 °C
 23.12 ksi

@Temperature 230 °F
 DAM; Dynamic; ISO 11403-1 -2
0.4312 GPa

@Temperature 60.0 °C
 62.54 ksi

@Temperature 140 °F
 DAM; Dynamic; ISO 11403-1 -2
0.9147 GPa

@Temperature 10.0 °C
 132.7 ksi

@Temperature 50.0 °F
 DAM; Dynamic; ISO 11403-1 -2
0.9608 GPa

@Temperature -20.0 °C
 139.4 ksi

@Temperature -4.00 °F
 DAM; Dynamic; ISO 11403-1 -2
1.0372 GPa

@Temperature -50.0 °C
 150.44 ksi

@Temperature -58.0 °F
 DAM; Dynamic; ISO 11403-1 -2
Shear Strength 0.004387 MPa

@Shear Rate 10.0 1/s,
Temperature 300 °C
 0.6363 psi

@Shear Rate 10.0 1/s,
Temperature 572 °F
 ISO 11403-1 -2
0.006551 MPa

@Shear Rate 10.0 1/s,
Temperature 290 °C
 0.9501 psi

@Shear Rate 10.0 1/s,
Temperature 554 °F
 ISO 11403-1 -2
0.01013 MPa

@Shear Rate 10.0 1/s,
Temperature 280 °C
 1.469 psi

@Shear Rate 10.0 1/s,
Temperature 536 °F
 ISO 11403-1 -2
0.1432 MPa

@Shear Rate 500 1/s,
Temperature 300 °C
 20.76 psi

@Shear Rate 500 1/s,
Temperature 572 °F
 ISO 11403-1 -2
0.1848 MPa

@Shear Rate 500 1/s,
Temperature 290 °C
 26.80 psi

@Shear Rate 500 1/s,
Temperature 554 °F
 ISO 11403-1 -2
0.2358 MPa

@Shear Rate 500 1/s,
Temperature 280 °C
 34.20 psi

@Shear Rate 500 1/s,
Temperature 536 °F
 ISO 11403-1 -2
0.4228 MPa

@Shear Rate 5000 1/s,
Temperature 300 °C
 61.32 psi

@Shear Rate 5000 1/s,
Temperature 572 °F
 ISO 11403-1 -2
0.4793 MPa

@Shear Rate 5000 1/s,
Temperature 290 °C
 69.51 psi

@Shear Rate 5000 1/s,
Temperature 554 °F
 ISO 11403-1 -2
0.5440 MPa

@Shear Rate 5000 1/s,
Temperature 280 °C
 78.91 psi

@Shear Rate 5000 1/s,
Temperature 536 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
DAM; ISO 180/1A
23.0 kJ/m²
10.9 ft-lb/in²
50%RH; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
DAM; ISO 180/1U
NB
NB
50%RH; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 DAM; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 50%RH; ISO 180/1U
Charpy Impact Unnotched NB
NB
DAM; ISO 179/1eU
NB
NB
50%RH; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 DAM; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 50%RH; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
DAM; ISO 179/1eA
2.00 J/cm²
9.52 ft-lb/in²
50%RH; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour 968 MPa

@Pressure 14.0 MPa,
Temperature 23.0 °C
 140000 psi

@Pressure 2030 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1008.4 MPa

@Pressure 12.0 MPa,
Temperature 23.0 °C
 146260 psi

@Pressure 1740 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2