DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 153HSL NC010 Nylon 612  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced Heat Stabilized Polyamide 612 Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
DAM; ISO 1183
Water Absorption 3.0 %

@Thickness 2.00 mm
 3.0 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.30 %

@Thickness 2.00 mm
 1.30 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 66500 cP

@Shear Rate 5000 1/s,
Temperature 270 °C
 66500 cP

@Shear Rate 5000 1/s,
Temperature 518 °F
 ISO 11403-1 -2
71900 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 71900 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
78800 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 78800 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
135700 cP

@Shear Rate 500 1/s,
Temperature 270 °C
 135700 cP

@Shear Rate 500 1/s,
Temperature 518 °F
 ISO 11403-1 -2
163900 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 163900 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
193900 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 193900 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 115 cm³/g
115 cm³/g
DAM; sulphuric acid 96%; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 12.05 MPa

@Strain 0.490 %,
Temperature 23.0 °C
 1748 psi

@Strain 0.490 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
13.32 MPa

@Strain 3.00 %,
Temperature 90.0 °C
 1932 psi

@Strain 3.00 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
13.4 MPa

@Strain 3.43 %,
Temperature 90.0 °C
 1940 psi

@Strain 3.43 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
19.6 MPa

@Strain 3.02 %,
Temperature 40.0 °C
 2840 psi

@Strain 3.02 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
24.39 MPa

@Strain 13.51 %,
Temperature 90.0 °C
 3537 psi

@Strain 13.51 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
25.74 MPa

@Strain 11.4 %,
Temperature 90.0 °C
 3733 psi

@Strain 11.4 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
26.86 MPa

@Strain 23.59 %,
Temperature 90.0 °C
 3896 psi

@Strain 23.59 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
27.61 MPa

@Strain 33.27 %,
Temperature 90.0 °C
 4004 psi

@Strain 33.27 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
28.22 MPa

@Strain 19.4 %,
Temperature 90.0 °C
 4093 psi

@Strain 19.4 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
28.4 MPa

@Strain 2.60 %,
Temperature 23.0 °C
 4120 psi

@Strain 2.60 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
28.63 MPa

@Strain 27.8 %,
Temperature 90.0 °C
 4152 psi

@Strain 27.8 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
30.04 MPa

@Strain 3.02 %,
Temperature 40.0 °C
 4357 psi

@Strain 3.02 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
37.63 MPa

@Strain 11.09 %,
Temperature 40.0 °C
 5458 psi

@Strain 11.09 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
42.32 MPa

@Strain 19.15 %,
Temperature 40.0 °C
 6138 psi

@Strain 19.15 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
43.09 MPa

@Strain 11.09 %,
Temperature 40.0 °C
 6250 psi

@Strain 11.09 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
43.33 MPa

@Strain 27.22 %,
Temperature 40.0 °C
 6284 psi

@Strain 27.22 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
44.23 MPa

@Strain 2.12 %,
Temperature 23.0 °C
 6415 psi

@Strain 2.12 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
46.39 MPa

@Strain 19.15 %,
Temperature 40.0 °C
 6728 psi

@Strain 19.15 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
47.15 MPa

@Strain 27.22 %,
Temperature 40.0 °C
 6839 psi

@Strain 27.22 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
47.43 MPa

@Strain 10.2 %,
Temperature 23.0 °C
 6879 psi

@Strain 10.2 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
52.66 MPa

@Strain 17.4 %,
Temperature 23.0 °C
 7638 psi

@Strain 17.4 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
53.79 MPa

@Strain 24.6 %,
Temperature 23.0 °C
 7802 psi

@Strain 24.6 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
56.99 MPa

@Strain 3.43 %,
Temperature 23.0 °C
 8266 psi

@Strain 3.43 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
58.39 MPa

@Strain 4.74 %,
Temperature 23.0 °C
 8469 psi

@Strain 4.74 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
Tensile Strength, Yield 53.0 MPa
7690 psi
50%RH; ISO 527-1/-2
62.0 MPa
8990 psi
DAM; ISO 527-1/-2
Elongation at Break 30 %
30 %
DAM; Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 4.4 %
4.4 %
DAM; ISO 527-1/-2
4.4 %
4.4 %
DAM; ISO 527-3
19 %
19 %
50%RH; ISO 527-1/-2
Tensile Modulus 1.60 GPa
232 ksi
50%RH; ISO 527-1/-2
2.40 GPa
348 ksi
DAM; ISO 527-1/-2
Flexural Modulus 1.45 GPa
210 ksi
50%RH; ISO 178
2.10 GPa
305 ksi
DAM; ISO 178
Shear Strength 0.00742 MPa

@Shear Rate 50.0 1/s,
Temperature 270 °C
 1.08 psi

@Shear Rate 50.0 1/s,
Temperature 518 °F
 ISO 11403-1 -2
0.010215 MPa

@Shear Rate 50.0 1/s,
Temperature 250 °C
 1.4816 psi

@Shear Rate 50.0 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.01394 MPa

@Shear Rate 50.0 1/s,
Temperature 240 °C
 2.022 psi

@Shear Rate 50.0 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.06785 MPa

@Shear Rate 500 1/s,
Temperature 270 °C
 9.841 psi

@Shear Rate 500 1/s,
Temperature 518 °F
 ISO 11403-1 -2
0.08195 MPa

@Shear Rate 500 1/s,
Temperature 250 °C
 11.89 psi

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.09695 MPa

@Shear Rate 500 1/s,
Temperature 240 °C
 14.06 psi

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.3325 MPa

@Shear Rate 5000 1/s,
Temperature 270 °C
 48.23 psi

@Shear Rate 5000 1/s,
Temperature 518 °F
 ISO 11403-1 -2
0.3595 MPa

@Shear Rate 5000 1/s,
Temperature 250 °C
 52.14 psi

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.394 MPa

@Shear Rate 5000 1/s,
Temperature 240 °C
 57.1 psi

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Secant Modulus 0.199 GPa

@Strain 21.57 %,
Temperature 40.0 °C
 28.8 ksi

@Strain 21.57 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.213 GPa

@Strain 21.98 %,
Temperature 40.0 °C
 30.9 ksi

@Strain 21.98 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.269 GPa

@Strain 19.8 %,
Temperature 23.0 °C
 39.0 ksi

@Strain 19.8 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.339 GPa

@Strain 11.09 %,
Temperature 40.0 °C
 49.2 ksi

@Strain 11.09 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.389 GPa

@Strain 11.09 %,
Temperature 40.0 °C
 56.4 ksi

@Strain 11.09 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.465 GPa

@Strain 10.2 %,
Temperature 23.0 °C
 67.4 ksi

@Strain 10.2 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.649 GPa

@Strain 3.02 %,
Temperature 40.0 °C
 94.1 ksi

@Strain 3.02 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.995 GPa

@Strain 3.02 %,
Temperature 40.0 °C
 144 ksi

@Strain 3.02 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
1.09 GPa

@Strain 2.60 %,
Temperature 23.0 °C
 158 ksi

@Strain 2.60 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1.5375 GPa

@Strain 3.76 %,
Temperature 23.0 °C
 223.00 ksi

@Strain 3.76 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
2.09 GPa

@Strain 2.12 %,
Temperature 23.0 °C
 303 ksi

@Strain 2.12 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2