DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced Heat Stabilized Polyamide 66 Zytel 103FHS NC010 is a heat stabilized internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
1.14 g/cc
0.0412 lb/in³
DAM; ISO 1183
Water Absorption 8.5 %

@Thickness 2.00 mm
8.5 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Moisture Absorption 2.60 %

@Thickness 2.00 mm
2.60 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Viscosity 42210 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
42210 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
ISO 11403-1 -2
86460 cP

@Shear Rate 500 1/s,
Temperature 295 °C
86460 cP

@Shear Rate 500 1/s,
Temperature 563 °F
ISO 11403-1 -2
Viscosity Test 145 cm³/g
145 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
50%RH; ISO 527-1/-2
85.0 MPa
12300 psi
DAM; ISO 527-1/-2
Elongation at Break 20 %
20 %
DAM; Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 4.5 %
4.5 %
DAM; ISO 527-1/-2
4.5 %
4.5 %
DAM; ISO 527-3
25 %
25 %
50%RH; ISO 527-1/-2
Tensile Modulus 1.40 GPa
203 ksi
50%RH; ISO 527-1/-2
3.10 GPa
450 ksi
DAM; ISO 527-1/-2
0.168 GPa

@Temperature 250 °C
24.4 ksi

@Temperature 482 °F
DAM; ISO 11403-1 -2
0.3845 GPa

@Temperature 170 °C
55.77 ksi

@Temperature 338 °F
DAM; Dynamic; ISO 11403-1 -2
0.445 GPa

@Temperature 170 °C
64.6 ksi

@Temperature 338 °F
DAM; ISO 11403-1 -2
0.552 GPa

@Temperature 110 °C
80.1 ksi

@Temperature 230 °F
DAM; Dynamic; ISO 11403-1 -2
0.688 GPa

@Temperature 90.0 °C
99.8 ksi

@Temperature 194 °F
DAM; ISO 11403-1 -2
2.40 GPa

@Temperature 50.0 °C
348 ksi

@Temperature 122 °F
DAM; ISO 11403-1 -2
3.095 GPa

@Temperature 30.0 °C
448.9 ksi

@Temperature 86.0 °F
DAM; Dynamic; ISO 11403-1 -2
3.10 GPa

@Temperature 20.0 °C
450 ksi

@Temperature 68.0 °F
DAM; ISO 11403-1 -2
3.256 GPa

@Temperature -20.0 °C
472.2 ksi

@Temperature -4.00 °F
DAM; Dynamic; ISO 11403-1 -2
3.29 GPa

@Temperature -10.0 °C
477 ksi

@Temperature 14.0 °F
DAM; ISO 11403-1 -2
3.5348 GPa

@Temperature -50.0 °C
512.68 ksi

@Temperature -58.0 °F
DAM; ISO 11403-1 -2
3.628 GPa

@Temperature -70.0 °C
526.2 ksi

@Temperature -94.0 °F
DAM; Dynamic; ISO 11403-1 -2
3.871 GPa

@Temperature -100 °C
561.4 ksi

@Temperature -148 °F
DAM; Dynamic; ISO 11403-1 -2
Flexural Modulus 1.30 GPa
189 ksi
50%RH; ISO 178
2.80 GPa
406 ksi
DAM; ISO 178
Izod Impact, Notched (ISO) 5.50 kJ/m²
2.62 ft-lb/in²
DAM; ISO 180/1A
11.0 kJ/m²
5.23 ft-lb/in²
50%RH; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
50%RH; ISO 180/1A
5.50 kJ/m²

@Temperature -40.0 °C
2.62 ft-lb/in²

@Temperature -40.0 °F
DAM; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) 300 kJ/m²
143 ft-lb/in²
DAM; ISO 180/1U
NB
NB
50%RH; ISO 180/1U
300 kJ/m²

@Temperature -30.0 °C
143 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
50%RH; ISO 180/1U
Charpy Impact Unnotched NB
NB
DAM; ISO 179/1eU
NB
NB
50%RH; ISO 179/1eU
35.0 J/cm²

@Temperature -30.0 °C
167 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
50%RH; ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
DAM; ISO 179/1eA
1.10 J/cm²
5.23 ft-lb/in²
50%RH; ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
50%RH; ISO 179/1eA
0.450 J/cm²

@Temperature -30.0 °C
2.14 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
DAM; ISO 11359-1/-2
Specific Heat Capacity 2.79 J/g-°C
0.667 BTU/lb-°F
Thermal Conductivity 0.160 W/m-K
1.11 BTU-in/hr-ft²-°F
of melt
Melting Point 262 °C
504 °F
DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
DAM; ISO 75-1/-2
Glass Transition Temp, Tg 60.0 °C
140 °F
DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
DAM; IEC 60695-11-10
V-2

@Thickness 0.700 mm
V-2

@Thickness 0.0276 in
DAM; IEC 60695-11-10
Oxygen Index 28 %
28 %
DAM; ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
50%RH; IEC 60093
1.00e+14 ohm-cm
1.00e+14 ohm-cm
DAM; IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
DAM; ASTM D150
3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
DAM; ASTM D150
3.4

@Frequency 1000 Hz
3.4

@Frequency 1000 Hz
DAM; ASTM D150
Dissipation Factor 0.010

@Frequency 100 Hz
0.010

@Frequency 100 Hz
DAM; ASTM D150
0.010

@Frequency 1000 Hz
0.010

@Frequency 1000 Hz
DAM; ASTM D150
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
DAM; ASTM D150
Comparative Tracking Index 600 V
600 V
DAM; IEC 60112
>= 600 V

@Thickness 3.00 mm
>= 600 V

@Thickness 0.118 in
DAM; UL 746A
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Eff. thermal diffusivity 5.00E-08 m²/s
Part Marking Code >PA66<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification PA66