DuPont Performance Polymers Zytel® 101F BKB009 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 101F BKB009 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® 101F BKB009 is an internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.014 cm/cm

@Thickness 2.00 mm
0.014 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm

@Thickness 2.00 mm
0.013 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 82.0 MPa

@Temperature 23.0 °C
11900 psi

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Break 18 %

@Temperature 23.0 °C
18 %

@Temperature 73.4 °F
DAM; nominal; ISO 527
Elongation at Yield 4.5 %

@Temperature 23.0 °C
4.5 %

@Temperature 73.4 °F
DAM; ISO 527
Tensile Modulus 3.10 GPa

@Temperature 23.0 °C
450 ksi

@Temperature 73.4 °F
DAM; ISO 527
Flexural Modulus 2.80 GPa

@Temperature 23.0 °C
406 ksi

@Temperature 73.4 °F
DAM; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -40.0 °C
2.38 ft-lb/in²

@Temperature -40.0 °F
DAM; ISO 180/1A
5.50 kJ/m²

@Temperature 23.0 °C
2.62 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 180/1A
Charpy Impact, Notched 0.550 J/cm²

@Temperature 23.0 °C
2.62 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 262 °C
504 °F
10°C/min; DAM; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
DAM; ISO 75-1/-2
UL RTI, Electrical 65.0 °C

@Thickness 0.400 mm
149 °F

@Thickness 0.0157 in
DAM; UL 746B
130 °C

@Thickness 6.00 mm
266 °F

@Thickness 0.236 in
DAM; UL 746B
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
DAM; UL 746B
130 °C

@Thickness 0.710 mm
266 °F

@Thickness 0.0280 in
DAM; UL 746B
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
DAM; UL 746B
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.400 mm
149 °F

@Thickness 0.0157 in
DAM; UL 746B
75.0 °C

@Thickness 0.710 mm
167 °F

@Thickness 0.0280 in
DAM; UL 746B
75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
DAM; UL 746B
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
DAM; UL 746B
75.0 °C

@Thickness 6.00 mm
167 °F

@Thickness 0.236 in
DAM; UL 746B
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.400 mm
149 °F

@Thickness 0.0157 in
DAM; UL 746B
85.0 °C

@Thickness 6.00 mm
185 °F

@Thickness 0.236 in
DAM; UL 746B
85.0 °C

@Thickness 1.50 mm
185 °F

@Thickness 0.0591 in
DAM; UL 746B
85.0 °C

@Thickness 0.710 mm
185 °F

@Thickness 0.0280 in
DAM; UL 746B
85.0 °C

@Thickness 3.00 mm
185 °F

@Thickness 0.118 in
DAM; UL 746B
Flammability, UL94 V-2

@Thickness 6.00 mm
V-2

@Thickness 0.236 in
DAM; IEC 60695-11-10
V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
DAM; IEC 60695-11-10
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
DAM; IEC 60695-11-10
V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
DAM; IEC 60695-11-10
V-2

@Thickness 0.710 mm
V-2

@Thickness 0.0280 in
DAM; IEC 60695-11-10
V-2

@Thickness 6.00 mm
V-2

@Thickness 0.236 in
DAM; UL94
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
DAM; UL94
V-2

@Thickness 0.710 mm
V-2

@Thickness 0.0280 in
DAM; UL94
V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
DAM; UL94
V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
DAM; UL94
Glow Wire Test 725 °C

@Thickness 0.710 mm
1340 °F

@Thickness 0.0280 in
DAM; Ignition; IEC 60695-2-13
750 °C

@Thickness 1.50 mm
1380 °F

@Thickness 0.0591 in
DAM; Ignition; IEC 60695-2-13
800 °C

@Thickness 3.00 mm
1470 °F

@Thickness 0.118 in
DAM; Ignition; IEC 60695-2-13
900 °C

@Thickness 0.400 mm
1650 °F

@Thickness 0.0157 in
DAM; Ignition; IEC 60695-2-13
960 °C

@Thickness 0.400 mm
1760 °F

@Thickness 0.0157 in
DAM; IEC 60695-2-12
960 °C

@Thickness 0.710 mm
1760 °F

@Thickness 0.0280 in
DAM; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
DAM; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
DAM; IEC 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 290 °C
554 °F
DAM; Optimum
280 - 300 °C
536 - 572 °F
DAM
Mold Temperature 70.0 °C
158 °F
DAM; optimum
50.0 - 90.0 °C
122 - 194 °F
DAM
Drying Temperature 80.0 °C
176 °F
DAM
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
DAM
Moisture Content <= 0.20 %
<= 0.20 %
DAM
Descriptive Properties Value Comments
Additive Lubricant
DAM
Mold Release
DAM
Appearance Black Color
DAM
Drying Recommended Yes, if moisture content of resin exceeds recommended level
DAM
Features Chemical Resistance, Good
DAM
Cycle (Production), Fast
DAM
Electrical Properties, Good
DAM
Fatigue Resistant
DAM
Flow, High
DAM
Fuel Resistant
DAM
Grease Resistant
DAM
Lubricated
DAM
Mold Release, Good
DAM
Moldability, Good
DAM
Molding Cycle, Fast
DAM
Molecular Wt., Low
DAM
Oil Resistant
DAM
Processability, Good
DAM
Forms Pellets
DAM
Generic Nylon 66
DAM
Material Status Current
DAM
Part Marking Code >PA66<
ISO 11469; DAM
Polymer Family Polyamide
DAM
Polymer Type PA66
DAM
Processing Method Injection Molding
DAM
Product Category Unreinforced Resins
DAM
Region Available - Global Yes
DAM
Resin Identification PA66
ISO 1043; DAM
RoHS Compliance Contact Manufacturer
DAM
Uses Appliance Components
DAM
Automotive Applications
DAM
Connectors
DAM
Electrical/Electronic Applications
DAM
Fasteners
DAM