DuPont Performance Polymers Rynite® FR515 BK507 PET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® FR515 BK507 PET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rynite® FR515 BK507 is a flame retardant 15% glass reinforced modified polyethtylene terephthalate. Recognized by UL as UL94V-0 at 0.8mm(0.03in). Has a 140C temp index. Excellent balance of electrical and mechanical prop. High temp. resistance and flow.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Filler Content 15 %
15 %
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa

@Temperature 23.0 °C
 14500 psi

@Temperature 73.4 °F
 ISO 527
125 MPa

@Temperature -40.0 °C
 18100 psi

@Temperature -40.0 °F
 ISO 527
Elongation at Break 2.0 %

@Temperature -40.0 °C
 2.0 %

@Temperature -40.0 °F
 ISO 527
2.2 %

@Temperature 23.0 °C
 2.2 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 3.59 GPa

@Temperature 150 °C
 521 ksi

@Temperature 302 °F
 ISO 527
6.135 GPa

@Temperature 23.0 °C
 889.8 ksi

@Temperature 73.4 °F
 ISO 527
7.721 GPa

@Temperature -40.0 °C
 1120 ksi

@Temperature -40.0 °F
 ISO 527
Flexural Strength 160 MPa

@Temperature 23.0 °C
 23200 psi

@Temperature 73.4 °F
 ISO 178
180 MPa

@Temperature -40.0 °C
 26100 psi

@Temperature -40.0 °F
 ISO 178
Flexural Modulus 6.00 GPa

@Temperature 23.0 °C
 870 ksi

@Temperature 73.4 °F
 ISO 178
6.737 GPa

@Temperature -40.0 °C
 977.1 ksi

@Temperature -40.0 °F
 ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -40.0 °C
 2.38 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
5.50 kJ/m²

@Temperature 23.0 °C
 2.62 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 18.0 kJ/m²

@Temperature -40.0 °C
 8.57 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1U
26.0 kJ/m²

@Temperature 23.0 °C
 12.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1U
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -40.0 °C
 9.52 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eU
3.20 J/cm²

@Temperature 23.0 °C
 15.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -40.0 °C
 2.86 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eA
0.620 J/cm²

@Temperature 23.0 °C
 2.95 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 160 °C
 278 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 74.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 41.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
95.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 52.8 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
125 µm/m-°C

@Temperature 55.0 - 160 °C
 69.4 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
Melting Point 254 °C
489 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 238 °C
460 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
UL RTI, Electrical 140 °C

@Thickness 0.860 mm
 284 °F

@Thickness 0.0339 in
 UL 746B
UL RTI, Mechanical with Impact 140 °C

@Thickness 0.860 mm
 284 °F

@Thickness 0.0339 in
 UL 746B
UL RTI, Mechanical without Impact 140 °C

@Thickness 0.860 mm
 284 °F

@Thickness 0.0339 in
 UL 746B
Flammability, UL94 V-0

@Thickness 0.860 mm
 V-0

@Thickness 0.0339 in
 IEC 60695-11-10
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 IEC 60695-11-10
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 UL94
V-0

@Thickness 0.860 mm
 V-0

@Thickness 0.0339 in
 UL94
5VA

@Thickness 1.50 mm
 5VA

@Thickness 0.0591 in
 IEC 60695-11-20
5VA

@Thickness 1.50 mm
 5VA

@Thickness 0.0591 in
 IEC 60695-11-10
5VA

@Thickness 1.50 mm
 5VA

@Thickness 0.0591 in
 UL94
Electrical Properties Metric English Comments
Comparative Tracking Index 175 - 250 V

@Temperature 23.0 °C
 175 - 250 V

@Temperature 73.4 °F
 UL 746A
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Optimum
270 - 290 °C
518 - 554 °F
Mold Temperature >= 95.0 °C
>= 203 °F
110 °C
230 °F
optimum
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Descriptive Properties Value Comments
Additive Flame Retardant
Appearance Black Color
Drying Recommended Yes
Features Dimensional Stability, Good
Electrical Properties, Good
Flame Retardant
Stiffness, Good
Strength, Good
Thermal Aging Resistance, Good
Filler Glass fiber reinforcement
Glass Reinforced
Forms Pellets
Generic PET
Material Status Current
Part Marking Code >PET-GF15FR(17)<
ISO 11469
Processing Method Injection Molding
Product Category Flame Retardant Resins
Glass Reinforced Resins
Region Available - Global Yes
Resin Identification PET-GF15FR(17)
ISO 1043
RoHS Compliance Contact Manufacturer
Uses Appliances
Electrical Parts
Electrical/Electronic Applications
Phenolic Replacement
Structural Parts