DuPont Performance Polymers Rynite® 935 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® 935 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass Reinforced Polyethylene Terephthalate Rynite 935 NC010 is a 35% mica/glass reinforced modified polyethylene terephthalate resin with exceptionally low warpage excellent electrical properties high stiffness and high heat resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
ASTM D792
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Water Absorption 0.83 %

@Thickness 2.00 mm
 0.83 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.130 %

@Thickness 2.00 mm
 0.130 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 37000 cP

@Shear Rate 5000 1/s,
Temperature 315 °C
 37000 cP

@Shear Rate 5000 1/s,
Temperature 599 °F
 ISO 11403-1 -2
57000 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
 57000 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
 ISO 11403-1 -2
93000 cP

@Shear Rate 5000 1/s,
Temperature 275 °C
 93000 cP

@Shear Rate 5000 1/s,
Temperature 527 °F
 ISO 11403-1 -2
130000 cP

@Shear Rate 500 1/s,
Temperature 315 °C
 130000 cP

@Shear Rate 500 1/s,
Temperature 599 °F
 ISO 11403-1 -2
203000 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 203000 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
327000 cP

@Shear Rate 500 1/s,
Temperature 275 °C
 327000 cP

@Shear Rate 500 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4 2577
Melt Flow 5.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 5.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 75
75
ISO 2039-2
Hardness, Rockwell R 115
115
ISO 2039-2
Tensile Strength at Break 85.0 MPa
12300 psi
ISO 527-1/-2
Tensile Stress 16.9 MPa

@Strain 0.200 %,
Temperature 40.0 °C
 2450 psi

@Strain 0.200 %,
Temperature 104 °F
 ISO 11403-1 -2
17.7 MPa

@Strain 0.610 %,
Temperature 90.0 °C
 2570 psi

@Strain 0.610 %,
Temperature 194 °F
 ISO 11403-1 -2
19.5 MPa

@Strain 0.210 %,
Temperature 23.0 °C
 2830 psi

@Strain 0.210 %,
Temperature 73.4 °F
 ISO 11403-1 -2
34.76 MPa

@Strain 2.48 %,
Temperature 90.0 °C
 5042 psi

@Strain 2.48 %,
Temperature 194 °F
 ISO 11403-1 -2
37.49 MPa

@Strain 4.29 %,
Temperature 90.0 °C
 5437 psi

@Strain 4.29 %,
Temperature 194 °F
 ISO 11403-1 -2
38.1 MPa

@Strain 6.10 %,
Temperature 90.0 °C
 5530 psi

@Strain 6.10 %,
Temperature 194 °F
 ISO 11403-1 -2
50.34 MPa

@Strain 0.800 %,
Temperature 40.0 °C
 7301 psi

@Strain 0.800 %,
Temperature 104 °F
 ISO 11403-1 -2
50.98 MPa

@Strain 0.680 %,
Temperature 23.0 °C
 7394 psi

@Strain 0.680 %,
Temperature 73.4 °F
 ISO 11403-1 -2
62.0 MPa

@Strain 1.40 %,
Temperature 40.0 °C
 8990 psi

@Strain 1.40 %,
Temperature 104 °F
 ISO 11403-1 -2
65.77 MPa

@Strain 1.20 %,
Temperature 23.0 °C
 9539 psi

@Strain 1.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
71.53 MPa

@Strain 1.71 %,
Temperature 23.0 °C
 10370 psi

@Strain 1.71 %,
Temperature 73.4 °F
 ISO 11403-1 -2
10.0 MPa

@Strain 0.126 %,
Time 3.60e+6 sec
 1450 psi

@Strain 0.126 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.134 %,
Time 1.80e+7 sec
 1450 psi

@Strain 0.134 %,
Time 5000 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.139 %,
Time 3.60e+7 sec
 1450 psi

@Strain 0.139 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.105 %,
Time 3600 sec
 1450 psi

@Strain 0.105 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.109 %,
Time 36000 sec
 1450 psi

@Strain 0.109 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.116 %,
Time 360000 sec
 1450 psi

@Strain 0.116 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
40.0 MPa

@Strain 0.624 %,
Time 360000 sec
 5800 psi

@Strain 0.624 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
40.0 MPa

@Strain 0.537 %,
Time 36000 sec
 5800 psi

@Strain 0.537 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
40.0 MPa

@Strain 0.489 %,
Time 3600 sec
 5800 psi

@Strain 0.489 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
40.0 MPa

@Strain 0.921 %,
Time 3.60e+7 sec
 5800 psi

@Strain 0.921 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
40.0 MPa

@Strain 0.870 %,
Time 1.80e+7 sec
 5800 psi

@Strain 0.870 %,
Time 5000 hour
 isochronous; ISO 11403-1 -2
40.0 MPa

@Strain 0.749 %,
Time 3.60e+6 sec
 5800 psi

@Strain 0.749 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
Elongation at Break 2.0 %
2.0 %
ISO 527-1/-2
Tensile Modulus 10.2 GPa
1480 ksi
ISO 527-1/-2
Flexural Modulus 9.10 GPa
1320 ksi
ISO 178
Shear Strength 0.0650 MPa

@Shear Rate 500 1/s,
Temperature 315 °C
 9.43 psi

@Shear Rate 500 1/s,
Temperature 599 °F
 ISO 11403-1 -2
0.1015 MPa

@Shear Rate 500 1/s,
Temperature 295 °C
 14.72 psi

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
0.1635 MPa

@Shear Rate 500 1/s,
Temperature 275 °C
 23.71 psi

@Shear Rate 500 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Secant Modulus 3.98 GPa

@Strain 1.60 %,
Temperature 40.0 °C
 577 ksi

@Strain 1.60 %,
Temperature 104 °F
 ISO 11403-1 -2
4.94 GPa

@Strain 1.39 %,
Temperature 23.0 °C
 716 ksi

@Strain 1.39 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.2925 GPa

@Strain 0.800 %,
Temperature 40.0 °C
 912.66 ksi

@Strain 0.800 %,
Temperature 104 °F
 ISO 11403-1 -2
7.50 GPa

@Strain 0.680 %,
Temperature 23.0 °C
 1090 ksi

@Strain 0.680 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.45 GPa

@Strain 0.200 %,
Temperature 40.0 °C
 1230 ksi

@Strain 0.200 %,
Temperature 104 °F
 ISO 11403-1 -2
9.29 GPa

@Strain 0.210 %,
Temperature 23.0 °C
 1350 ksi

@Strain 0.210 %,
Temperature 73.4 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
ISO 179/1eU
2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 6620 MPa

@Pressure 50.0 MPa,
Temperature 23.0 °C
 961000 psi

@Pressure 7250 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
8180 MPa

@Pressure 40.0 MPa,
Temperature 23.0 °C
 1.19e+6 psi

@Pressure 5800 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
8900 MPa

@Pressure 30.0 MPa,
Temperature 23.0 °C
 1.29e+6 psi

@Pressure 4350 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
9260 MPa

@Pressure 20.0 MPa,
Temperature 23.0 °C
 1.34e+6 psi

@Pressure 2900 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
9520 MPa

@Pressure 10.0 MPa,
Temperature 23.0 °C
 1.38e+6 psi

@Pressure 1450 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
9350 MPa

@Time 3600 sec
 1.36e+6 psi

@Time 1.00 hour
 ISO 899-1
Tensile Creep Modulus, 1000 hours 3420 MPa

@Pressure 50.0 MPa,
Temperature 23.0 °C
 497000 psi

@Pressure 7250 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
5340 MPa

@Pressure 40.0 MPa,
Temperature 23.0 °C
 775000 psi

@Pressure 5800 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
6420 MPa

@Pressure 30.0 MPa,
Temperature 23.0 °C
 932000 psi

@Pressure 4350 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
7270 MPa

@Pressure 20.0 MPa,
Temperature 23.0 °C
 1.05e+6 psi

@Pressure 2900 psi,
Temperature 73.4 °F
 ISO 11403-1 -2