DuPont Performance Polymers Rynite® 545 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 50% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® 545 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
45% Glass Reinforced Polyethylene Terephthalate Rynite 545 NC010 is a 45% glass reinforced modified polyethylene terephthalate with greater strength and stiffness excellent dimensional stability and creep resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.69 g/cc
0.0611 lb/in³
ISO 1183
Water Absorption 0.62 %

@Thickness 2.00 mm
 0.62 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.140 %

@Thickness 2.00 mm
 0.140 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 43000 cP

@Shear Rate 5000 1/s,
Temperature 305 °C
 43000 cP

@Shear Rate 5000 1/s,
Temperature 581 °F
 ISO 11403-1 -2
55000 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
 55000 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
 ISO 11403-1 -2
70000 cP

@Shear Rate 5000 1/s,
Temperature 285 °C
 70000 cP

@Shear Rate 5000 1/s,
Temperature 545 °F
 ISO 11403-1 -2
139000 cP

@Shear Rate 500 1/s,
Temperature 305 °C
 139000 cP

@Shear Rate 500 1/s,
Temperature 581 °F
 ISO 11403-1 -2
175000 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 175000 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
223000 cP

@Shear Rate 500 1/s,
Temperature 285 °C
 223000 cP

@Shear Rate 500 1/s,
Temperature 545 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 280 °C
 2.5 g/10 min

@Load 4.76 lb,
Temperature 536 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Strength at Break 182 MPa
26400 psi
ISO 527-1/-2
Tensile Stress 23.4 MPa

@Strain 0.520 %,
Temperature 150 °C
 3390 psi

@Strain 0.520 %,
Temperature 302 °F
 ISO 11403-1 -2
30.7 MPa

@Strain 0.460 %,
Temperature 90.0 °C
 4450 psi

@Strain 0.460 %,
Temperature 194 °F
 ISO 11403-1 -2
34.7 MPa

@Strain 0.190 %,
Temperature 0.000 °C
 5030 psi

@Strain 0.190 %,
Temperature 32.0 °F
 ISO 11403-1 -2
35.0 MPa

@Strain 0.220 %,
Temperature 40.0 °C
 5080 psi

@Strain 0.220 %,
Temperature 104 °F
 ISO 11403-1 -2
37.6 MPa

@Strain 0.200 %,
Temperature -40.0 °C
 5450 psi

@Strain 0.200 %,
Temperature -40.0 °F
 ISO 11403-1 -2
50.7 MPa

@Strain 2.07 %,
Temperature 150 °C
 7350 psi

@Strain 2.07 %,
Temperature 302 °F
 ISO 11403-1 -2
61.3 MPa

@Strain 3.63 %,
Temperature 150 °C
 8890 psi

@Strain 3.63 %,
Temperature 302 °F
 ISO 11403-1 -2
68.5 MPa

@Strain 5.19 %,
Temperature 150 °C
 9940 psi

@Strain 5.19 %,
Temperature 302 °F
 ISO 11403-1 -2
72.5 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 10500 psi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
75.6 MPa

@Strain 1.84 %,
Temperature 90.0 °C
 11000 psi

@Strain 1.84 %,
Temperature 194 °F
 ISO 11403-1 -2
92.0 MPa

@Strain 3.22 %,
Temperature 90.0 °C
 13300 psi

@Strain 3.22 %,
Temperature 194 °F
 ISO 11403-1 -2
99.5 MPa

@Strain 4.61 %,
Temperature 90.0 °C
 14400 psi

@Strain 4.61 %,
Temperature 194 °F
 ISO 11403-1 -2
110 MPa

@Strain 0.900 %,
Temperature 40.0 °C
 16000 psi

@Strain 0.900 %,
Temperature 104 °F
 ISO 11403-1 -2
120 MPa

@Strain 0.760 %,
Temperature 0.000 °C
 17400 psi

@Strain 0.760 %,
Temperature 32.0 °F
 ISO 11403-1 -2
135 MPa

@Strain 0.810 %,
Temperature -40.0 °C
 19600 psi

@Strain 0.810 %,
Temperature -40.0 °F
 ISO 11403-1 -2
147 MPa

@Strain 1.57 %,
Temperature 40.0 °C
 21300 psi

@Strain 1.57 %,
Temperature 104 °F
 ISO 11403-1 -2
162 MPa

@Strain 2.24 %,
Temperature 40.0 °C
 23500 psi

@Strain 2.24 %,
Temperature 104 °F
 ISO 11403-1 -2
179 MPa

@Strain 1.33 %,
Temperature 0.000 °C
 26000 psi

@Strain 1.33 %,
Temperature 32.0 °F
 ISO 11403-1 -2
180 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 26100 psi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
209 MPa

@Strain 1.41 %,
Temperature -40.0 °C
 30300 psi

@Strain 1.41 %,
Temperature -40.0 °F
 ISO 11403-1 -2
213 MPa

@Strain 1.90 %,
Temperature 0.000 °C
 30900 psi

@Strain 1.90 %,
Temperature 32.0 °F
 ISO 11403-1 -2
260 MPa

@Strain 2.02 %,
Temperature -40.0 °C
 37700 psi

@Strain 2.02 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Elongation at Break 2.0 %
2.0 %
ISO 527-1/-2
Tensile Modulus 15.5 GPa
2250 ksi
ISO 527-1/-2
Flexural Modulus 13.5 GPa
1960 ksi
ISO 178
Shear Modulus 0.593 GPa

@Temperature 160 °C
 86.0 ksi

@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.716 GPa

@Temperature 120 °C
 104 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
1.576 GPa

@Temperature 70.0 °C
 228.6 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
2.561 GPa

@Temperature 20.0 °C
 371.4 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
2.827 GPa

@Temperature -20.0 °C
 410.0 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
3.017 GPa

@Temperature -50.0 °C
 437.6 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Shear Strength 0.0695 MPa

@Shear Rate 500 1/s,
Temperature 305 °C
 10.1 psi

@Shear Rate 500 1/s,
Temperature 581 °F
 ISO 11403-1 -2
0.0875 MPa

@Shear Rate 500 1/s,
Temperature 295 °C
 12.7 psi

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
0.1115 MPa

@Shear Rate 500 1/s,
Temperature 285 °C
 16.17 psi

@Shear Rate 500 1/s,
Temperature 545 °F
 ISO 11403-1 -2
Secant Modulus 8.60 GPa

@Strain 1.79 %,
Temperature 40.0 °C
 1250 ksi

@Strain 1.79 %,
Temperature 104 °F
 ISO 11403-1 -2
9.00 GPa

@Strain 2.00 %,
Temperature 23.0 °C
 1310 ksi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
12.2 GPa

@Strain 0.900 %,
Temperature 40.0 °C
 1770 ksi

@Strain 0.900 %,
Temperature 104 °F
 ISO 11403-1 -2
12.7 GPa

@Strain 1.52 %,
Temperature 0.000 °C
 1840 ksi

@Strain 1.52 %,
Temperature 32.0 °F
 ISO 11403-1 -2
14.2 GPa

@Strain 1.61 %,
Temperature -40.0 °C
 2050 ksi

@Strain 1.61 %,
Temperature -40.0 °F
 ISO 11403-1 -2
14.5 GPa

@Strain 0.500 %,
Temperature 23.0 °C
 2100 ksi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
15.8 GPa

@Strain 0.760 %,
Temperature 0.000 °C
 2290 ksi

@Strain 0.760 %,
Temperature 32.0 °F
 ISO 11403-1 -2
15.9 GPa

@Strain 0.220 %,
Temperature 40.0 °C
 2310 ksi

@Strain 0.220 %,
Temperature 104 °F
 ISO 11403-1 -2
16.7 GPa

@Strain 0.810 %,
Temperature -40.0 °C
 2420 ksi

@Strain 0.810 %,
Temperature -40.0 °F
 ISO 11403-1 -2
18.3 GPa

@Strain 0.190 %,
Temperature 0.000 °C
 2650 ksi

@Strain 0.190 %,
Temperature 32.0 °F
 ISO 11403-1 -2
18.8 GPa

@Strain 0.200 %,
Temperature -40.0 °C
 2730 ksi

@Strain 0.200 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/1eU
4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
ISO 179/1eA
1.10 J/cm²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 15600 MPa

@Time 3600 sec
 2.26e+6 psi

@Time 1.00 hour
 ISO 899-1