DuPont Performance Polymers Minlon® 22C NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled
Manufacturer DuPont Performance Polymers
Trade Name Minlon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Minlon® 22C NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
38% Mineral/Glass Reinforced Polyamide 66 Minlon 22C NC010 is a 38% mineral/glass reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
1.45 g/cc
0.0524 lb/in³
DAM; ISO 1183
Water Absorption 5.4 %

@Thickness 2.00 mm
 5.4 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.40 %

@Thickness 2.00 mm
 1.40 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Water Absorption at Saturation 1.0 %
1.0 %
DAM; Immersion 24h; ASTM D570
Viscosity 65520 cP

@Shear Rate 5000 1/s,
Temperature 305 °C
 65520 cP

@Shear Rate 5000 1/s,
Temperature 581 °F
 ISO 11403-1 -2
80210 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
 80210 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
 ISO 11403-1 -2
99512 cP

@Shear Rate 5000 1/s,
Temperature 285 °C
 99512 cP

@Shear Rate 5000 1/s,
Temperature 545 °F
 ISO 11403-1 -2
174500 cP

@Shear Rate 500 1/s,
Temperature 305 °C
 174500 cP

@Shear Rate 500 1/s,
Temperature 581 °F
 ISO 11403-1 -2
232900 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 232900 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
311100 cP

@Shear Rate 500 1/s,
Temperature 285 °C
 311100 cP

@Shear Rate 500 1/s,
Temperature 545 °F
 ISO 11403-1 -2
Viscosity Test 150 cm³/g
150 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 82.0 MPa
11900 psi
50%RH; ISO 527-1/-2
130 MPa
18900 psi
DAM; ISO 527-1/-2
Tensile Stress 4.30 MPa

@Strain 0.200 %,
Temperature 150 °C
 624 psi

@Strain 0.200 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
4.60 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 667 psi

@Strain 0.100 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
7.20 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 1040 psi

@Strain 0.100 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
7.60 MPa

@Strain 0.100 %,
Temperature 0.000 °C
 1100 psi

@Strain 0.100 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
8.90 MPa

@Strain 0.400 %,
Temperature 150 °C
 1290 psi

@Strain 0.400 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
17.3 MPa

@Strain 0.900 %,
Temperature 150 °C
 2510 psi

@Strain 0.900 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
17.45 MPa

@Strain 0.200 %,
Temperature -40.0 °C
 2531 psi

@Strain 0.200 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
17.6 MPa

@Strain 0.900 %,
Temperature 150 °C
 2550 psi

@Strain 0.900 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
18.3 MPa

@Strain 0.200 %,
Temperature 0.000 °C
 2650 psi

@Strain 0.200 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
19.87 MPa

@Strain 0.200 %,
Temperature -40.0 °C
 2882 psi

@Strain 0.200 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
22.9 MPa

@Strain 1.30 %,
Temperature 150 °C
 3320 psi

@Strain 1.30 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
26.0 MPa

@Strain 0.600 %,
Temperature 23.0 °C
 3770 psi

@Strain 0.600 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
32.2 MPa

@Strain 2.10 %,
Temperature 150 °C
 4670 psi

@Strain 2.10 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
34.3 MPa

@Strain 2.60 %,
Temperature 150 °C
 4970 psi

@Strain 2.60 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
39.2 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 5690 psi

@Strain 1.00 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
40.2 MPa

@Strain 3.20 %,
Temperature 150 °C
 5830 psi

@Strain 3.20 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
41.5 MPa

@Strain 0.500 %,
Temperature 0.000 °C
 6020 psi

@Strain 0.500 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
51.7 MPa

@Strain 1.50 %,
Temperature 23.0 °C
 7500 psi

@Strain 1.50 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
55.50 MPa

@Strain 0.700 %,
Temperature -40.0 °C
 8050 psi

@Strain 0.700 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
57.12 MPa

@Strain 0.600 %,
Temperature -40.0 °C
 8285 psi

@Strain 0.600 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
60.1 MPa

@Strain 0.800 %,
Temperature 0.000 °C
 8720 psi

@Strain 0.800 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
62.24 MPa

@Strain 0.900 %,
Temperature 23.0 °C
 9027 psi

@Strain 0.900 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
64.1 MPa

@Strain 0.900 %,
Temperature 0.000 °C
 9300 psi

@Strain 0.900 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
79.97 MPa

@Strain 0.900 %,
Temperature -40.0 °C
 11600 psi

@Strain 0.900 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
80.3 MPa

@Strain 1.30 %,
Temperature 0.000 °C
 11600 psi

@Strain 1.30 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
84.53 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 12260 psi

@Strain 1.30 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
86.6 MPa

@Strain 1.20 %,
Temperature 0.000 °C
 12600 psi

@Strain 1.20 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
93.49 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 13560 psi

@Strain 1.30 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
101.13 MPa

@Strain 1.70 %,
Temperature 23.0 °C
 14668 psi

@Strain 1.70 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
103 MPa

@Strain 1.50 %,
Temperature 0.000 °C
 14900 psi

@Strain 1.50 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
104.54 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 15162 psi

@Strain 1.30 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
114.7 MPa

@Strain 1.70 %,
Temperature -40.0 °C
 16640 psi

@Strain 1.70 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
126.42 MPa

@Strain 3.30 %,
Temperature 23.0 °C
 18336 psi

@Strain 3.30 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
149.8 MPa

@Strain 3.20 %,
Temperature 0.000 °C
 21730 psi

@Strain 3.20 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
160.7 MPa

@Strain 3.20 %,
Temperature -40.0 °C
 23310 psi

@Strain 3.20 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
165.9 MPa

@Strain 3.20 %,
Temperature -40.0 °C
 24050 psi

@Strain 3.20 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
10.0 MPa

@Strain 0.340 %,
Time 3600 sec
 1450 psi

@Strain 0.340 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.370 %,
Time 36000 sec
 1450 psi

@Strain 0.370 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.410 %,
Time 360000 sec
 1450 psi

@Strain 0.410 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.460 %,
Time 3.60e+6 sec
 1450 psi

@Strain 0.460 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break 3.5 %
3.5 %
DAM; ISO 527-1/-2
10 %
10 %
50%RH; ISO 527-1/-2
Tensile Modulus 5.00 GPa
725 ksi
50%RH; ISO 527-1/-2
7.50 GPa
1090 ksi
DAM; ISO 527-1/-2
1.4166 GPa

@Temperature 170 °C
 205.46 ksi

@Temperature 338 °F
 50%RH; Dynamic; ISO 11403-1 -2
1.84 GPa

@Temperature 110 °C
 267 ksi

@Temperature 230 °F
 50%RH; Dynamic; ISO 11403-1 -2
1.965 GPa

@Temperature 170 °C
 285.0 ksi

@Temperature 338 °F
 DAM; Dynamic; ISO 11403-1 -2
2.649 GPa

@Temperature 110 °C
 384.2 ksi

@Temperature 230 °F
 DAM; Dynamic; ISO 11403-1 -2
5.04 GPa

@Temperature 30.0 °C
 731 ksi

@Temperature 86.0 °F
 50%RH; Dynamic; ISO 11403-1 -2
5.88 GPa

@Temperature -20.0 °C
 853 ksi

@Temperature -4.00 °F
 50%RH; Dynamic; ISO 11403-1 -2
Users viewing this material also viewed the following: