DuPont Performance Polymers Minlon® 11C140 BK086 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Minlon® 11C140 BK086 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Minlon® 11C140 BK086 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding. It has very low warpage.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
DAM; ISO 1183
Filler Content 40 %
40 %
DAM
Mechanical Properties Metric English Comments
Tensile Strength at Break 59.0 MPa

@Temperature 23.0 °C
8560 psi

@Temperature 73.4 °F
50%RH; ISO 527
87.0 MPa

@Temperature 23.0 °C
12600 psi

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Break 8.0 %

@Temperature 23.0 °C
8.0 %

@Temperature 73.4 °F
DAM; ISO 527
20 %

@Temperature 23.0 °C
20 %

@Temperature 73.4 °F
50%RH; ISO 527
Tensile Modulus 2.50 GPa

@Temperature 23.0 °C
363 ksi

@Temperature 73.4 °F
50%RH; ISO 527
5.80 GPa

@Temperature 23.0 °C
841 ksi

@Temperature 73.4 °F
DAM; ISO 527
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 180/1A
8.00 kJ/m²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 180/1A
Charpy Impact Unnotched 11.5 J/cm²

@Temperature 23.0 °C
54.7 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
50%RH; ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²

@Temperature 23.0 °C
2.62 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
0.800 J/cm²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 256 °C
493 °F
10°C/min; DAM; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
DAM; ISO 75-1/-2
UL RTI, Electrical 65.0 °C

@Thickness 0.810 mm
149 °F

@Thickness 0.0319 in
DAM; UL 746B
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
DAM; UL 746B
65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
DAM; UL 746B
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.810 mm
149 °F

@Thickness 0.0319 in
DAM; UL 746B
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
DAM; UL 746B
65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
DAM; UL 746B
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
DAM; UL 746B
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
DAM; UL 746B
65.0 °C

@Thickness 0.810 mm
149 °F

@Thickness 0.0319 in
DAM; UL 746B
Flammability, UL94 HB

@Thickness 0.810 mm
HB

@Thickness 0.0319 in
DAM; IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
DAM; IEC 60695-11-10
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; IEC 60695-11-10
HB

@Thickness 0.810 mm
HB

@Thickness 0.0319 in
DAM; UL94
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
DAM; UL94
Processing Properties Metric English Comments
Melt Temperature 295 °C
563 °F
DAM; Optimum
285 - 305 °C
545 - 581 °F
DAM
Mold Temperature 70.0 - 120 °C
158 - 248 °F
DAM
100 °C
212 °F
DAM; optimum
Drying Temperature 80.0 °C
176 °F
DAM
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
DAM
Moisture Content <= 0.20 %
<= 0.20 %
DAM
Descriptive Properties Value Comments
Appearance Black Color
DAM
Drying Recommended Yes, if moisture content of resin exceeds recommended level
DAM
Filler Mineral filler
DAM
Forms Pellets
DAM
Generic Nylon 66
DAM
Material Status Current
DAM
Part Marking Code >PA66-IMD40<
ISO 11469; DAM
Polymer Family Polyamide
DAM
Polymer Type PA66
DAM
Processing Method Injection Molding
DAM
Product Category Low Warp Resins
DAM
Mineral Reinforced Resins
DAM
Resin Identification PA66-IMD40
ISO 1043; DAM
RoHS Compliance Contact Manufacturer
DAM