DuPont Performance Polymers Minlon® 10B40 NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled
Manufacturer DuPont Performance Polymers
Trade Name Minlon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Minlon® 10B40 NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40% Mineral Reinforced Polyamide 66Minlon 10B40 NC010 is a 40% mineral reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
DAM; ISO 1183
Water Absorption 0.45 %

@Thickness 2.00 mm
 0.45 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 0.180 %

@Thickness 2.00 mm
 0.180 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.0 MPa
8410 psi
50%RH; ISO 527-1/-2
92.0 MPa
13300 psi
DAM; ISO 527-1/-2
Tensile Stress 5.36 MPa

@Strain 0.400 %,
Temperature 150 °C
 777 psi

@Strain 0.400 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
8.33 MPa

@Strain 0.500 %,
Temperature 150 °C
 1210 psi

@Strain 0.500 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
9.50 MPa

@Strain 0.800 %,
Temperature 150 °C
 1380 psi

@Strain 0.800 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
10.36 MPa

@Strain 0.100 %,
Temperature -40.0 °C
 1503 psi

@Strain 0.100 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
12.5 MPa

@Strain 0.800 %,
Temperature 150 °C
 1810 psi

@Strain 0.800 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
18.42 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 2672 psi

@Strain 0.200 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
18.92 MPa

@Strain 1.50 %,
Temperature 150 °C
 2744 psi

@Strain 1.50 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
18.98 MPa

@Strain 2.70 %,
Temperature 150 °C
 2753 psi

@Strain 2.70 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
19.85 MPa

@Strain 0.200 %,
Temperature 0.000 °C
 2879 psi

@Strain 0.200 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
20.13 MPa

@Strain 0.200 %,
Temperature 0.000 °C
 2920 psi

@Strain 0.200 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
22.57 MPa

@Strain 4.70 %,
Temperature 150 °C
 3274 psi

@Strain 4.70 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
23.65 MPa

@Strain 2.40 %,
Temperature 150 °C
 3430 psi

@Strain 2.40 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
25.37 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 3680 psi

@Strain 0.500 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
35.71 MPa

@Strain 0.800 %,
Temperature 23.0 °C
 5179 psi

@Strain 0.800 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
42.75 MPa

@Strain 1.10 %,
Temperature 23.0 °C
 6200 psi

@Strain 1.10 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
47.23 MPa

@Strain 1.40 %,
Temperature 23.0 °C
 6850 psi

@Strain 1.40 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
48.0 MPa

@Strain 0.500 %,
Temperature 0.000 °C
 6960 psi

@Strain 0.500 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
53.59 MPa

@Strain 0.600 %,
Temperature 0.000 °C
 7773 psi

@Strain 0.600 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
53.92 MPa

@Strain 0.500 %,
Temperature -40.0 °C
 7820 psi

@Strain 0.500 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
57.8 MPa

@Strain 0.700 %,
Temperature 23.0 °C
 8380 psi

@Strain 0.700 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
58.76 MPa

@Strain 0.600 %,
Temperature -40.0 °C
 8522 psi

@Strain 0.600 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
59.55 MPa

@Strain 8.00 %,
Temperature 23.0 °C
 8637 psi

@Strain 8.00 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
68.01 MPa

@Strain 0.800 %,
Temperature 0.000 °C
 9864 psi

@Strain 0.800 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
70.53 MPa

@Strain 0.900 %,
Temperature 0.000 °C
 10230 psi

@Strain 0.900 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
71.16 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 10320 psi

@Strain 1.00 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
80.05 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 11610 psi

@Strain 1.30 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
80.32 MPa

@Strain 1.20 %,
Temperature 0.000 °C
 11650 psi

@Strain 1.20 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
82.0 MPa

@Strain 0.800 %,
Temperature -40.0 °C
 11900 psi

@Strain 0.800 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
82.42 MPa

@Strain 1.10 %,
Temperature 0.000 °C
 11950 psi

@Strain 1.10 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
82.82 MPa

@Strain 0.900 %,
Temperature -40.0 °C
 12010 psi

@Strain 0.900 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
102.55 MPa

@Strain 1.10 %,
Temperature -40.0 °C
 14874 psi

@Strain 1.10 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
106.14 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 15394 psi

@Strain 1.30 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
117.55 MPa

@Strain 1.50 %,
Temperature -40.0 °C
 17049 psi

@Strain 1.50 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
Elongation at Break 2.5 %
2.5 %
DAM; ISO 527-1/-2
8.0 %
8.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 5.40 GPa
783 ksi
50%RH; ISO 527-1/-2
9.60 GPa
1390 ksi
DAM; ISO 527-1/-2
Flexural Modulus 4.80 GPa
696 ksi
50%RH; ISO 178
9.00 GPa
1310 ksi
DAM; ISO 178
Secant Modulus 0.520 GPa

@Strain 6.00 %,
Temperature 100 °C
 75.4 ksi

@Strain 6.00 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
0.543 GPa

@Strain 6.50 %,
Temperature 80.0 °C
 78.7 ksi

@Strain 6.50 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
0.5968 GPa

@Strain 7.50 %,
Temperature 80.0 °C
 86.56 ksi

@Strain 7.50 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
0.645 GPa

@Strain 6.00 %,
Temperature 100 °C
 93.6 ksi

@Strain 6.00 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
0.855 GPa

@Strain 3.80 %,
Temperature 80.0 °C
 124 ksi

@Strain 3.80 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
1.07 GPa

@Strain 3.00 %,
Temperature 100 °C
 155 ksi

@Strain 3.00 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
1.14 GPa

@Strain 2.20 %,
Temperature 100 °C
 165 ksi

@Strain 2.20 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
1.43 GPa

@Strain 2.60 %,
Temperature 80.0 °C
 208 ksi

@Strain 2.60 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
1.446 GPa

@Strain 4.00 %,
Temperature 23.0 °C
 209.7 ksi

@Strain 4.00 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1.45 GPa

@Strain 1.80 %,
Temperature 80.0 °C
 210 ksi

@Strain 1.80 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
1.49 GPa

@Strain 1.70 %,
Temperature 100 °C
 217 ksi

@Strain 1.70 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
1.50 GPa

@Strain 1.40 %,
Temperature 100 °C
 217 ksi

@Strain 1.40 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
1.82 GPa

@Strain 0.900 %,
Temperature 100 °C
 264 ksi

@Strain 0.900 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
1.92 GPa

@Strain 0.900 %,
Temperature 100 °C
 279 ksi

@Strain 0.900 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2.02 GPa

@Strain 0.900 %,
Temperature 80.0 °C
 293 ksi

@Strain 0.900 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
2.116 GPa

@Strain 0.500 %,
Temperature 100 °C
 306.9 ksi

@Strain 0.500 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
2.14 GPa

@Strain 1.40 %,
Temperature 80.0 °C
 310 ksi

@Strain 1.40 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
2.226 GPa

@Strain 0.500 %,
Temperature 100 °C
 322.9 ksi

@Strain 0.500 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2.34 GPa

@Strain 0.500 %,
Temperature 80.0 °C
 339 ksi

@Strain 0.500 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
2.63 GPa

@Strain 0.900 %,
Temperature 80.0 °C
 382 ksi

@Strain 0.900 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
Users viewing this material also viewed the following: