DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Minlon® 10B140 BK061 is a 40% mineral reinforced, black polyamide 66 resin for injection molding. It has very low warpage.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | DAM; ISO 1183 |
| Filler Content | 40 % | 40 % | DAM |
| Water Absorption | 1.6 % @Temperature 23.0 °C |
1.6 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa @Temperature 23.0 °C |
7830 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 82.0 MPa @Temperature 23.0 °C |
11900 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 9.0 % @Temperature 23.0 °C |
9.0 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 3.80 GPa @Temperature 23.0 °C |
551 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 6.60 GPa @Temperature 23.0 °C |
957 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 0.350 J/cm² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| 0.450 J/cm² @Temperature 23.0 °C |
2.14 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | DAM; ISO 75-1/-2 |
| UL RTI, Electrical | 105 °C @Thickness 0.710 mm |
221 °F @Thickness 0.0280 in |
DAM; UL 746B |
| 120 °C @Thickness 3.00 mm |
248 °F @Thickness 0.118 in |
DAM; UL 746B | |
| 120 °C @Thickness 1.50 mm |
248 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.710 mm |
149 °F @Thickness 0.0280 in |
DAM; UL 746B |
| 105 °C @Thickness 1.50 mm |
221 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 115 °C @Thickness 3.00 mm |
239 °F @Thickness 0.118 in |
DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.710 mm |
149 °F @Thickness 0.0280 in |
DAM; UL 746B |
| 115 °C @Thickness 1.50 mm |
239 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 115 °C @Thickness 3.00 mm |
239 °F @Thickness 0.118 in |
DAM; UL 746B | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; UL94 |
| HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
DAM; UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
DAM; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V @Temperature 23.0 °C |
>= 600 V @Temperature 73.4 °F |
DAM; UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 285 - 305 °C | 545 - 581 °F | DAM |
| 295 °C | 563 °F | DAM; Optimum | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Mineral filler | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA66-MD40< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Low Warp Resins | DAM |
| Mineral Reinforced Resins | DAM | |
| Mineral Reinforced Resins | DAM | |
| Resin Identification | PA66-MD40 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
Users viewing this material also viewed the following:
- Osprey Metals 440C Stainless Steel Powder (Grade 90% - 16)
- Honeywell Capran® Oxyshield™ M-OPA (0.75 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film
- H.C. Starck NiAl 97/3 Atomized Powder
- SABIC Innovative Plastics LNP Thermotuf PC006I PA 6
- Zoltek Pyron® Satin Weave & Knit Fabric Oxidized Pan Fiber
- Arlon LW401Y##-M1 0.040" (1.02 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Ineos Nova 5500 High Impact Polystyrene (discontinued **)
- Chase Plastics CP Pryme® PPC100-35M Polypropylene Copolymer
- RheTech Products HP506-01B 22% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black
Copyright © lookpolymers.com All Rights Reserved