DuPont Performance Polymers Hytrel® HTR6108 TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR6108 TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hytrel® HTR6108 is a medium modulus grade, specially designed for good flexibility and low permeability to hydrocarbon fuels and oils. It has nominal hardness of 61D and can be processed by various thermoplastic processing techniques.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D792
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
Water Absorption 0.20 %

@Temperature 23.0 °C
0.20 %

@Temperature 73.4 °F
Immersion 24h; ASTM D570
0.20 %

@Temperature 23.0 °C
0.20 %

@Temperature 73.4 °F
Immersion 24h; ISO 62
Melt Flow 5.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
5.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D <= 60
<= 60
ASTM D2240
<= 61
<= 61
ISO 868
58

@Time 15.0 sec
58

@Time 0.00417 hour
ISO 868
Tensile Strength at Break 31.0 MPa

@Temperature 23.0 °C
4500 psi

@Temperature 73.4 °F
ISO 527 (1BA bar)
38.6 MPa

@Temperature 23.0 °C
5600 psi

@Temperature 73.4 °F
ASTM D638
Tensile Stress 7.60 MPa

@Strain 5.00 %,
Temperature 23.0 °C
1100 psi

@Strain 5.00 %,
Temperature 73.4 °F
ASTM D638
9.50 MPa

@Strain 10.0 %,
Temperature 23.0 °C
1380 psi

@Strain 10.0 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
9.60 MPa

@Strain 10.0 %,
Temperature 23.0 °C
1390 psi

@Strain 10.0 %,
Temperature 73.4 °F
ASTM D638
Elongation at Break 250 %

@Temperature 23.0 °C
250 %

@Temperature 73.4 °F
ISO 527 (1BA bar)
400 %

@Temperature 23.0 °C
400 %

@Temperature 73.4 °F
ASTM D638
Tensile Modulus 0.165 GPa

@Temperature 23.0 °C
23.9 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 0.0600 GPa

@Temperature 100 °C
8.70 ksi

@Temperature 212 °F
ASTM D790
0.0600 GPa

@Temperature 100 °C
8.70 ksi

@Temperature 212 °F
ISO 178
0.190 GPa

@Temperature 23.0 °C
27.6 ksi

@Temperature 73.4 °F
ISO 178
0.193 GPa

@Temperature 23.0 °C
28.0 ksi

@Temperature 73.4 °F
ASTM D790
2.01 GPa

@Temperature -40.0 °C
292 ksi

@Temperature -40.0 °F
ASTM D790
2.01 GPa

@Temperature -40.0 °C
292 ksi

@Temperature -40.0 °F
ISO 178
Izod Impact, Notched 0.200 J/cm

@Temperature -40.0 °C
0.375 ft-lb/in

@Temperature -40.0 °F
ASTM D256
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 162 °C
324 °F
10°C/min; ISO 11357-1/-3
168 °C
334 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 47.0 °C
117 °F
ISO 75-1/-2
50.0 °C
122 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 42.0 °C
108 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 195 °C
383 °F
Optimum; Extrusion
200 °C
392 °F
Optimum; Injection Molding
Mold Temperature 45.0 °C
113 °F
optimum; Injection Molding
45.0 - 55.0 °C
113 - 131 °F
Injection Molding
Drying Temperature 100 °C
212 °F
Extrusion
100 °C
212 °F
Injection Molding
Dry Time 2.00 - 3.00 hour
2.00 - 3.00 hour
Extrusion
2.00 - 3.00 hour
2.00 - 3.00 hour
Injection Molding
Moisture Content <= 0.080 %
<= 0.080 %
Extrusion
<= 0.080 %
<= 0.080 %
Injection Molding
Descriptive Properties Value Comments
Additive Antioxidant
Appearance Beige, Light
Drying Recommended Yes
Extrudable - Cast Film Yes
Extrudable - Coating Yes
Extrudable - Filament Yes
Extrudable - Hose Yes
Extrudable - Sheet Yes
Extrudable - Tubing Yes
Extrudable - Wire and Cable Yes
Features Barrier Resin
Chemical Resistance, Good
Copolymer, Block
Hardness, Medium
Liquid Permeability, Low
Generic TPC-ET
Heat Stabilized Yes
Material Status Current
Melt Castable Yes
Part Marking Code >TPC-ET<
ISO 11469
Polymer Family TPC-ET
Polymer Type TPC-ET
Processing Method Extrusion
Injection Molding
Product Category Extrusion Resins
Transparent/Translucent Resins
Resin Identification TPC-ET
ISO 1043
RoHS Compliance Contact Manufacturer
Uses Cable Jacketing
Coating Applications
Hose