DuPont Performance Polymers Hytrel® HTR5612BK TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR5612BK TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hytrel® HTR5612BK HTR5612BK is designed for blow molding or processing techniques requiring high melt viscosity. It has nominal durometer hardness of 54D, is pigmented black with fine particle size carbon black, and contains a general purpose stabilizer.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
Water Absorption 0.20 %

@Temperature 23.0 °C
0.20 %

@Temperature 73.4 °F
Equilibrium 50%RH; ISO 62
0.60 %

@Temperature 23.0 °C
0.60 %

@Temperature 73.4 °F
Saturation, immersed; ISO 62
0.40 %

@Thickness 1.00 mm,
Temperature 23.0 °C
0.40 %

@Thickness 0.0394 in,
Temperature 73.4 °F
Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.012 cm/cm

@Thickness 2.00 mm
0.012 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Thickness 2.00 mm
0.015 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Flow 2.9 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.9 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
9.6 g/10 min

@Load 5.00 kg,
Temperature 230 °C
9.6 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 48

@Time 15.0 sec
48

@Time 0.00417 hour
ISO 868
54

@Time 1.00 sec
54

@Time 0.000278 hour
ISO 868
Tensile Strength at Break 32.0 MPa

@Temperature 23.0 °C
4640 psi

@Temperature 73.4 °F
ISO 527 (1BA bar)
Tensile Stress 5.10 MPa

@Strain 5.00 %,
Temperature 23.0 °C
740 psi

@Strain 5.00 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
8.30 MPa

@Strain 10.0 %,
Temperature 23.0 °C
1200 psi

@Strain 10.0 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
14.1 MPa

@Strain 50.0 %,
Temperature 23.0 °C
2050 psi

@Strain 50.0 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
Elongation at Break >= 50 %

@Temperature 23.0 °C
>= 50 %

@Temperature 73.4 °F
nominal; ISO 527 (1BA bar)
440 %

@Temperature 23.0 °C
440 %

@Temperature 73.4 °F
ISO 527 (1BA bar)
540 %

@Temperature 23.0 °C
540 %

@Temperature 73.4 °F
nominal; ISO 527 (1BA bar)
Tensile Modulus 0.114 GPa

@Temperature 23.0 °C
16.5 ksi

@Temperature 73.4 °F
ISO 527
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 15.7 J/cm²

@Temperature -40.0 °C
74.7 ft-lb/in²

@Temperature -40.0 °F
partial break; ISO 179/1eA
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 200 °C
392 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 53.0 °C
127 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL94
Processing Properties Metric English Comments
Melt Temperature 230 °C
446 °F
Optimum; Blow Molding
230 °C
446 °F
Optimum; Injection Molding
Mold Temperature 45.0 °C
113 °F
optimum; Injection Molding
Drying Temperature 110 °C
230 °F
Blow Molding
110 °C
230 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
3.00 - 4.00 hour
3.00 - 4.00 hour
Blow Molding
Moisture Content 0.020 %
0.020 %
Blow Molding
0.080 %
0.080 %
Injection Molding
Descriptive Properties Value Comments
Generic TPC-ET
Material Status Current
Part Marking Code >TPC-ET<
ISO 11469
Product Category Blow Moldable Resins
High Performance Hytrel®® Resins
Unreinforced Resins
Resin Identification TPC-ET
ISO 1043