DuPont Performance Polymers Hytrel® DYM500BK TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® DYM500BK TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hytrel® DYM500BK is a medium modulus polyester alloy suited for injection molding of Air Bag Deployment Doors. It has a nominal durometer hardness of 55D and contains fine particle size carbon black.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 0.20 %

@Temperature 23.0 °C
 0.20 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62
0.60 %

@Temperature 23.0 °C
 0.60 %

@Temperature 73.4 °F
 Immersion 24h; ISO 62
0.60 %

@Temperature 23.0 °C
 0.60 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62
0.70 %

@Temperature 23.0 °C
 0.70 %

@Temperature 73.4 °F
 Immersion 168h; ASTM D570
Linear Mold Shrinkage 0.015 cm/cm

@Thickness 1.27 mm
 0.015 in/in

@Thickness 0.0500 in
 Transverse; ASTM D955
0.017 cm/cm

@Thickness 1.27 mm
 0.017 in/in

@Thickness 0.0500 in
 Flow; ASTM D955
Linear Mold Shrinkage, Flow 0.012 cm/cm

@Thickness 2.00 mm
 0.012 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm

@Thickness 2.00 mm
 0.013 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Flow 14 g/10 min

@Load 2.16 kg,
Temperature 240 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 464 °F
 ASTM D1238
14 g/10 min

@Load 2.16 kg,
Temperature 240 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 464 °F
 ISO 1133
Melt Index of Compound 12.7 g/10 min

@Load 2.16 kg,
Temperature 240 °C
 12.7 g/10 min

@Load 4.76 lb,
Temperature 464 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D <= 55
<= 55
ASTM D2240
<= 55
<= 55
ISO 868
50

@Time 15.0 sec
 50

@Time 0.00417 hour
 ISO 868
Tensile Strength at Break 26.0 MPa

@Temperature 23.0 °C
 3770 psi

@Temperature 73.4 °F
 ASTM D638
35.0 MPa

@Temperature 23.0 °C
 5080 psi

@Temperature 73.4 °F
 ISO 527 (1BA bar)
Tensile Stress 3.35 MPa

@Strain 5.00 %,
Temperature 100 °C
 486 psi

@Strain 5.00 %,
Temperature 212 °F
 ISO 527
3.57 MPa

@Strain 5.00 %,
Temperature 80.0 °C
 518 psi

@Strain 5.00 %,
Temperature 176 °F
 ISO 527
5.70 MPa

@Strain 10.0 %,
Temperature 100 °C
 827 psi

@Strain 10.0 %,
Temperature 212 °F
 ISO 527
6.13 MPa

@Strain 10.0 %,
Temperature 80.0 °C
 889 psi

@Strain 10.0 %,
Temperature 176 °F
 ISO 527
6.85 MPa

@Strain 15.0 %,
Temperature 100 °C
 994 psi

@Strain 15.0 %,
Temperature 212 °F
 ISO 527
7.44 MPa

@Strain 15.0 %,
Temperature 80.0 °C
 1080 psi

@Strain 15.0 %,
Temperature 176 °F
 ISO 527
7.52 MPa

@Strain 20.0 %,
Temperature 100 °C
 1090 psi

@Strain 20.0 %,
Temperature 212 °F
 ISO 527
8.00 MPa

@Strain 25.0 %,
Temperature 100 °C
 1160 psi

@Strain 25.0 %,
Temperature 212 °F
 ISO 527
8.28 MPa

@Strain 20.0 %,
Temperature 80.0 °C
 1200 psi

@Strain 20.0 %,
Temperature 176 °F
 ISO 527
8.31 MPa

@Strain 30.0 %,
Temperature 100 °C
 1210 psi

@Strain 30.0 %,
Temperature 212 °F
 ISO 527
8.51 MPa

@Strain 35.0 %,
Temperature 100 °C
 1230 psi

@Strain 35.0 %,
Temperature 212 °F
 ISO 527
8.67 MPa

@Strain 40.0 %,
Temperature 100 °C
 1260 psi

@Strain 40.0 %,
Temperature 212 °F
 ISO 527
8.78 MPa

@Strain 25.0 %,
Temperature 80.0 °C
 1270 psi

@Strain 25.0 %,
Temperature 176 °F
 ISO 527
8.80 MPa

@Strain 45.0 %,
Temperature 100 °C
 1280 psi

@Strain 45.0 %,
Temperature 212 °F
 ISO 527
8.91 MPa

@Strain 50.0 %,
Temperature 100 °C
 1290 psi

@Strain 50.0 %,
Temperature 212 °F
 ISO 527
9.06 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 1310 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 527
9.12 MPa

@Strain 30.0 %,
Temperature 80.0 °C
 1320 psi

@Strain 30.0 %,
Temperature 176 °F
 ISO 527
9.36 MPa

@Strain 35.0 %,
Temperature 80.0 °C
 1360 psi

@Strain 35.0 %,
Temperature 176 °F
 ISO 527
9.52 MPa

@Strain 40.0 %,
Temperature 80.0 °C
 1380 psi

@Strain 40.0 %,
Temperature 176 °F
 ISO 527
9.66 MPa

@Strain 45.0 %,
Temperature 80.0 °C
 1400 psi

@Strain 45.0 %,
Temperature 176 °F
 ISO 527
9.77 MPa

@Strain 50.0 %,
Temperature 80.0 °C
 1420 psi

@Strain 50.0 %,
Temperature 176 °F
 ISO 527
12.0 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 1740 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ASTM D638
12.0 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 1740 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
13.0 MPa

@Strain 10.0 %,
Temperature 23.0 °C
 1890 psi

@Strain 10.0 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
13.6 MPa

@Strain 10.0 %,
Temperature 23.0 °C
 1970 psi

@Strain 10.0 %,
Temperature 73.4 °F
 ISO 527
14.0 MPa

@Strain 10.0 %,
Temperature 23.0 °C
 2030 psi

@Strain 10.0 %,
Temperature 73.4 °F
 ASTM D638
15.1 MPa

@Strain 15.0 %,
Temperature 23.0 °C
 2190 psi

@Strain 15.0 %,
Temperature 73.4 °F
 ISO 527
15.8 MPa

@Strain 20.0 %,
Temperature 23.0 °C
 2290 psi

@Strain 20.0 %,
Temperature 73.4 °F
 ISO 527
16.1 MPa

@Strain 5.00 %,
Temperature 0.000 °C
 2340 psi

@Strain 5.00 %,
Temperature 32.0 °F
 ISO 527
16.2 MPa

@Strain 5.00 %,
Temperature -30.0 °C
 2350 psi

@Strain 5.00 %,
Temperature -22.0 °F
 ISO 527
16.2 MPa

@Strain 25.0 %,
Temperature 23.0 °C
 2350 psi

@Strain 25.0 %,
Temperature 73.4 °F
 ISO 527
16.4 MPa

@Strain 30.0 %,
Temperature 23.0 °C
 2380 psi

@Strain 30.0 %,
Temperature 73.4 °F
 ISO 527
16.6 MPa

@Strain 35.0 %,
Temperature 23.0 °C
 2410 psi

@Strain 35.0 %,
Temperature 73.4 °F
 ISO 527
16.6 MPa

@Strain 40.0 %,
Temperature 23.0 °C
 2410 psi

@Strain 40.0 %,
Temperature 73.4 °F
 ISO 527
16.6 MPa

@Strain 45.0 %,
Temperature 23.0 °C
 2410 psi

@Strain 45.0 %,
Temperature 73.4 °F
 ISO 527
16.6 MPa

@Strain 50.0 %,
Temperature 23.0 °C
 2410 psi

@Strain 50.0 %,
Temperature 73.4 °F
 ISO 527
18.7 MPa

@Strain 10.0 %,
Temperature 0.000 °C
 2710 psi

@Strain 10.0 %,
Temperature 32.0 °F
 ISO 527
19.5 MPa

@Strain 5.00 %,
Temperature -40.0 °C
 2830 psi

@Strain 5.00 %,
Temperature -40.0 °F
 ISO 527
19.7 MPa

@Strain 15.0 %,
Temperature 0.000 °C
 2860 psi

@Strain 15.0 %,
Temperature 32.0 °F
 ISO 527
20.0 MPa

@Strain 15.0 %,
Temperature 23.0 °C
 2900 psi

@Strain 15.0 %,
Temperature 73.4 °F
 ASTM D638
20.2 MPa

@Strain 20.0 %,
Temperature 0.000 °C
 2930 psi

@Strain 20.0 %,
Temperature 32.0 °F
 ISO 527
20.4 MPa

@Strain 25.0 %,
Temperature 0.000 °C
 2960 psi

@Strain 25.0 %,
Temperature 32.0 °F
 ISO 527
20.5 MPa

@Strain 30.0 %,
Temperature 0.000 °C
 2970 psi

@Strain 30.0 %,
Temperature 32.0 °F
 ISO 527
20.6 MPa

@Strain 35.0 %,
Temperature 0.000 °C
 2990 psi

@Strain 35.0 %,
Temperature 32.0 °F
 ISO 527
20.6 MPa

@Strain 40.0 %,
Temperature 0.000 °C
 2990 psi

@Strain 40.0 %,
Temperature 32.0 °F
 ISO 527
20.6 MPa

@Strain 45.0 %,
Temperature 0.000 °C
 2990 psi

@Strain 45.0 %,
Temperature 32.0 °F
 ISO 527
20.6 MPa

@Strain 50.0 %,
Temperature 0.000 °C
 2990 psi

@Strain 50.0 %,
Temperature 32.0 °F
 ISO 527
22.6 MPa

@Strain 10.0 %,
Temperature -30.0 °C
 3280 psi

@Strain 10.0 %,
Temperature -22.0 °F
 ISO 527