DuPont Performance Polymers Hytrel® 6359FG NC010 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 6359FG NC010 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
63 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
1.22 g/cc
0.0441 lb/in³
ISO 1183
Water Absorption 0.60 %

@Thickness 2.00 mm
0.60 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
0.200 %

@Thickness 0.0787 in
Sim. to ISO 62
Viscosity 94540 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
94540 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
ISO 11403-1 -2
101600 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
101600 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
ISO 11403-1 -2
109200 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
109200 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
ISO 11403-1 -2
323400 cP

@Shear Rate 500 1/s,
Temperature 250 °C
323400 cP

@Shear Rate 500 1/s,
Temperature 482 °F
ISO 11403-1 -2
383700 cP

@Shear Rate 500 1/s,
Temperature 240 °C
383700 cP

@Shear Rate 500 1/s,
Temperature 464 °F
ISO 11403-1 -2
454000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
454000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Melt Flow 8.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
cm³/10min; ISO 1133
9.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 58
58
15s; ISO 868
<= 63
<= 63
ISO 868
Tensile Strength at Break 41.0 MPa
5950 psi
ISO 527-1/-2
Tensile Stress 12.0 MPa

@Strain 5.00 %
1740 psi

@Strain 5.00 %
ISO 527-1/-2
15.0 MPa

@Strain 10.0 %
2180 psi

@Strain 10.0 %
ISO 527-1/-2
4.36 MPa

@Strain 7.48 %,
Temperature 150 °C
632 psi

@Strain 7.48 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
5.56 MPa

@Strain 7.10 %,
Temperature 120 °C
806 psi

@Strain 7.10 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
5.70 MPa

@Strain 17.16 %,
Temperature 150 °C
827 psi

@Strain 17.16 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
5.83 MPa

@Strain 47.08 %,
Temperature 150 °C
846 psi

@Strain 47.08 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
5.86 MPa

@Strain 60.28 %,
Temperature 150 °C
850 psi

@Strain 60.28 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
5.92 MPa

@Strain 73.48 %,
Temperature 150 °C
859 psi

@Strain 73.48 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
5.93 MPa

@Strain 37.4 %,
Temperature 150 °C
860 psi

@Strain 37.4 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
5.96 MPa

@Strain 86.68 %,
Temperature 150 °C
864 psi

@Strain 86.68 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
5.99 MPa

@Strain 26.84 %,
Temperature 150 °C
869 psi

@Strain 26.84 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
6.01 MPa

@Strain 100.76 %,
Temperature 150 °C
872 psi

@Strain 100.76 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
6.03 MPa

@Strain 120.12 %,
Temperature 150 °C
875 psi

@Strain 120.12 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
6.12 MPa

@Strain 134.2 %,
Temperature 150 °C
888 psi

@Strain 134.2 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
6.27 MPa

@Strain 150.04 %,
Temperature 150 °C
909 psi

@Strain 150.04 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
6.35 MPa

@Strain 7.08 %,
Temperature 100 °C
921 psi

@Strain 7.08 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
6.98 MPa

@Strain 7.03 %,
Temperature 90.0 °C
1010 psi

@Strain 7.03 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
7.64 MPa

@Strain 17.13 %,
Temperature 120 °C
1110 psi

@Strain 17.13 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
7.98 MPa

@Strain 60.59 %,
Temperature 120 °C
1160 psi

@Strain 60.59 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
7.99 MPa

@Strain 47.22 %,
Temperature 120 °C
1160 psi

@Strain 47.22 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.04 MPa

@Strain 37.19 %,
Temperature 120 °C
1170 psi

@Strain 37.19 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.08 MPa

@Strain 73.96 %,
Temperature 120 °C
1170 psi

@Strain 73.96 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.11 MPa

@Strain 27.16 %,
Temperature 120 °C
1180 psi

@Strain 27.16 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.13 MPa

@Strain 87.33 %,
Temperature 120 °C
1180 psi

@Strain 87.33 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.19 MPa

@Strain 100.7 %,
Temperature 120 °C
1190 psi

@Strain 100.7 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.31 MPa

@Strain 120.76 %,
Temperature 120 °C
1210 psi

@Strain 120.76 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.41 MPa

@Strain 134.13 %,
Temperature 120 °C
1220 psi

@Strain 134.13 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.53 MPa

@Strain 150.01 %,
Temperature 120 °C
1240 psi

@Strain 150.01 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.78 MPa

@Strain 17.08 %,
Temperature 100 °C
1270 psi

@Strain 17.08 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.20 MPa

@Strain 47.92 %,
Temperature 100 °C
1330 psi

@Strain 47.92 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.22 MPa

@Strain 61.25 %,
Temperature 100 °C
1340 psi

@Strain 61.25 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.29 MPa

@Strain 7.83 %,
Temperature 60.0 °C
1350 psi

@Strain 7.83 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
9.34 MPa

@Strain 37.92 %,
Temperature 100 °C
1350 psi

@Strain 37.92 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.35 MPa

@Strain 27.92 %,
Temperature 100 °C
1360 psi

@Strain 27.92 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.35 MPa

@Strain 75.42 %,
Temperature 100 °C
1360 psi

@Strain 75.42 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.44 MPa

@Strain 88.76 %,
Temperature 100 °C
1370 psi

@Strain 88.76 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.52 MPa

@Strain 102.09 %,
Temperature 100 °C
1380 psi

@Strain 102.09 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.67 MPa

@Strain 122.92 %,
Temperature 100 °C
1400 psi

@Strain 122.92 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.74 MPa

@Strain 17.77 %,
Temperature 90.0 °C
1410 psi

@Strain 17.77 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
9.79 MPa

@Strain 136.26 %,
Temperature 100 °C
1420 psi

@Strain 136.26 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.92 MPa

@Strain 48.35 %,
Temperature 90.0 °C
1440 psi

@Strain 48.35 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
9.96 MPa

@Strain 61.58 %,
Temperature 90.0 °C
1440 psi

@Strain 61.58 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
10.07 MPa

@Strain 74.8 %,
Temperature 90.0 °C
1461 psi

@Strain 74.8 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
10.14 MPa

@Strain 37.61 %,
Temperature 90.0 °C
1471 psi

@Strain 37.61 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
10.17 MPa

@Strain 88.85 %,
Temperature 90.0 °C
1475 psi

@Strain 88.85 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
10.21 MPa

@Strain 27.69 %,
Temperature 90.0 °C
1481 psi

@Strain 27.69 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
10.26 MPa

@Strain 102.08 %,
Temperature 90.0 °C
1488 psi

@Strain 102.08 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
10.39 MPa

@Strain 122.74 %,
Temperature 90.0 °C
1507 psi

@Strain 122.74 %,
Temperature 194 °F
TPE; ISO 11403-1 -2