DuPont Performance Polymers Hytrel® 5555HS Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 5555HS Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
55 Shore D High Performance Polyester Elastomer with Heat Ageing ProtectionInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Water Absorption 0.60 %

@Thickness 2.00 mm
0.60 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
0.200 %

@Thickness 0.0787 in
Sim. to ISO 62
Water Absorption at Saturation 0.70 %
0.70 %
Immersion 24h; ASTM D570
Viscosity 75000 cP

@Shear Rate 5000 1/s,
Temperature 255 °C
75000 cP

@Shear Rate 5000 1/s,
Temperature 491 °F
ISO 11403-1 -2
81000 cP

@Shear Rate 5000 1/s,
Temperature 235 °C
81000 cP

@Shear Rate 5000 1/s,
Temperature 455 °F
ISO 11403-1 -2
86000 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
86000 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
ISO 11403-1 -2
171000 cP

@Shear Rate 500 1/s,
Temperature 255 °C
171000 cP

@Shear Rate 500 1/s,
Temperature 491 °F
ISO 11403-1 -2
217000 cP

@Shear Rate 500 1/s,
Temperature 235 °C
217000 cP

@Shear Rate 500 1/s,
Temperature 455 °F
ISO 11403-1 -2
271000 cP

@Shear Rate 500 1/s,
Temperature 215 °C
271000 cP

@Shear Rate 500 1/s,
Temperature 419 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Melt Flow 8.5 g/10 min

@Load 2.16 kg,
Temperature 220 °C
8.5 g/10 min

@Load 4.76 lb,
Temperature 428 °F
cm³/10min; ISO 1133
8.5 g/10 min

@Load 2.16 kg,
Temperature 220 °C
8.5 g/10 min

@Load 4.76 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 52
52
15s; ISO 868
<= 55
<= 55
ISO 868
Tensile Strength at Break 35.0 MPa
5080 psi
ISO 527-1/-2
Tensile Stress 6.90 MPa

@Strain 5.00 %
1000 psi

@Strain 5.00 %
ISO 527-1/-2
11.1 MPa

@Strain 10.0 %
1610 psi

@Strain 10.0 %
ISO 527-1/-2
14.7 MPa

@Strain 50.0 %
2130 psi

@Strain 50.0 %
ISO 527-1/-2
16.0 MPa

@Strain 100 %
2320 psi

@Strain 100 %
ISO 527-1/-2
2.81 MPa

@Strain 4.00 %,
Temperature 120 °C
408 psi

@Strain 4.00 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
3.27 MPa

@Strain 3.93 %,
Temperature 100 °C
474 psi

@Strain 3.93 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
3.52 MPa

@Strain 3.88 %,
Temperature 90.0 °C
511 psi

@Strain 3.88 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
4.39 MPa

@Strain 3.78 %,
Temperature 60.0 °C
637 psi

@Strain 3.78 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
5.46 MPa

@Strain 13.47 %,
Temperature 120 °C
792 psi

@Strain 13.47 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
5.54 MPa

@Strain 3.77 %,
Temperature 40.0 °C
804 psi

@Strain 3.77 %,
Temperature 104 °F
TPE; ISO 11403-1 -2
6.26 MPa

@Strain 23.66 %,
Temperature 120 °C
908 psi

@Strain 23.66 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
6.54 MPa

@Strain 33.86 %,
Temperature 120 °C
949 psi

@Strain 33.86 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
6.63 MPa

@Strain 44.05 %,
Temperature 120 °C
962 psi

@Strain 44.05 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
6.71 MPa

@Strain 57.16 %,
Temperature 120 °C
973 psi

@Strain 57.16 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
6.79 MPa

@Strain 13.93 %,
Temperature 100 °C
985 psi

@Strain 13.93 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
6.81 MPa

@Strain 70.26 %,
Temperature 120 °C
988 psi

@Strain 70.26 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
6.95 MPa

@Strain 83.37 %,
Temperature 120 °C
1010 psi

@Strain 83.37 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
7.12 MPa

@Strain 97.2 %,
Temperature 120 °C
1030 psi

@Strain 97.2 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
7.18 MPa

@Strain 0.750 %,
Temperature -40.0 °C
1040 psi

@Strain 0.750 %,
Temperature -40.0 °F
TPE; ISO 11403-1 -2
7.36 MPa

@Strain 13.77 %,
Temperature 90.0 °C
1070 psi

@Strain 13.77 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
7.39 MPa

@Strain 116.86 %,
Temperature 120 °C
1070 psi

@Strain 116.86 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
7.64 MPa

@Strain 130.69 %,
Temperature 120 °C
1110 psi

@Strain 130.69 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
7.78 MPa

@Strain 23.93 %,
Temperature 100 °C
1130 psi

@Strain 23.93 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
7.85 MPa

@Strain 4.57 %,
Temperature 23.0 °C
1140 psi

@Strain 4.57 %,
Temperature 73.4 °F
TPE; ISO 11403-1 -2
7.93 MPa

@Strain 3.49 %,
Temperature 0.000 °C
1150 psi

@Strain 3.49 %,
Temperature 32.0 °F
TPE; ISO 11403-1 -2
7.99 MPa

@Strain 146.71 %,
Temperature 120 °C
1160 psi

@Strain 146.71 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.11 MPa

@Strain 34.64 %,
Temperature 100 °C
1180 psi

@Strain 34.64 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
8.21 MPa

@Strain 44.65 %,
Temperature 100 °C
1190 psi

@Strain 44.65 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
8.32 MPa

@Strain 58.22 %,
Temperature 100 °C
1210 psi

@Strain 58.22 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
8.45 MPa

@Strain 23.65 %,
Temperature 90.0 °C
1230 psi

@Strain 23.65 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
8.47 MPa

@Strain 71.79 %,
Temperature 100 °C
1230 psi

@Strain 71.79 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
8.61 MPa

@Strain 170.01 %,
Temperature 120 °C
1250 psi

@Strain 170.01 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
8.64 MPa

@Strain 85.36 %,
Temperature 100 °C
1250 psi

@Strain 85.36 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
8.81 MPa

@Strain 33.53 %,
Temperature 90.0 °C
1280 psi

@Strain 33.53 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
8.83 MPa

@Strain 98.93 %,
Temperature 100 °C
1280 psi

@Strain 98.93 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
8.93 MPa

@Strain 43.42 %,
Temperature 90.0 °C
1300 psi

@Strain 43.42 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
9.04 MPa

@Strain 56.83 %,
Temperature 90.0 °C
1310 psi

@Strain 56.83 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
9.18 MPa

@Strain 119.65 %,
Temperature 100 °C
1330 psi

@Strain 119.65 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.19 MPa

@Strain 70.25 %,
Temperature 90.0 °C
1330 psi

@Strain 70.25 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
9.37 MPa

@Strain 83.66 %,
Temperature 90.0 °C
1360 psi

@Strain 83.66 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
9.40 MPa

@Strain 196.95 %,
Temperature 120 °C
1360 psi

@Strain 196.95 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
9.45 MPa

@Strain 133.22 %,
Temperature 100 °C
1370 psi

@Strain 133.22 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.53 MPa

@Strain 14.11 %,
Temperature 60.0 °C
1380 psi

@Strain 14.11 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
9.58 MPa

@Strain 97.07 %,
Temperature 90.0 °C
1390 psi

@Strain 97.07 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
9.86 MPa

@Strain 149.65 %,
Temperature 100 °C
1430 psi

@Strain 149.65 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
9.92 MPa

@Strain 116.84 %,
Temperature 90.0 °C
1440 psi

@Strain 116.84 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
10.21 MPa

@Strain 130.25 %,
Temperature 90.0 °C
1481 psi

@Strain 130.25 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
10.53 MPa

@Strain 173.94 %,
Temperature 100 °C
1527 psi

@Strain 173.94 %,
Temperature 212 °F
TPE; ISO 11403-1 -2