DuPont Performance Polymers Hytrel® 4556 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 4556 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
45 Shore D High Performance Polyester ElastomerInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Water Absorption 0.60 %

@Thickness 2.00 mm
 0.60 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Melt Flow 7.5 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 7.5 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 cm³/10min; ISO 1133
8.5 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 8.5 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 42
42
15s; ISO 868
<= 45
<= 45
ISO 868
Tensile Strength at Break 34.0 MPa
4930 psi
ISO 527-1/-2
Tensile Stress 5.70 MPa

@Strain 10.0 %
 827 psi

@Strain 10.0 %
 ISO 527-1/-2
9.80 MPa

@Strain 50.0 %
 1420 psi

@Strain 50.0 %
 ISO 527-1/-2
11.0 MPa

@Strain 100 %
 1600 psi

@Strain 100 %
 ISO 527-1/-2
17.0 MPa

@Strain 300 %
 2470 psi

@Strain 300 %
 ISO 527-1/-2
0.490 MPa

@Strain 0.220 %,
Temperature 120 °C
 71.1 psi

@Strain 0.220 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
0.520 MPa

@Strain 0.230 %,
Temperature 100 °C
 75.4 psi

@Strain 0.230 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
0.540 MPa

@Strain 0.230 %,
Temperature 90.0 °C
 78.3 psi

@Strain 0.230 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
0.570 MPa

@Strain 0.240 %,
Temperature 60.0 °C
 82.7 psi

@Strain 0.240 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
0.590 MPa

@Strain 0.240 %,
Temperature 40.0 °C
 85.6 psi

@Strain 0.240 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
0.650 MPa

@Strain 0.250 %,
Temperature 23.0 °C
 94.3 psi

@Strain 0.250 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
0.660 MPa

@Strain 0.220 %,
Temperature 0.000 °C
 95.7 psi

@Strain 0.220 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
0.740 MPa

@Strain 0.230 %,
Temperature -20.0 °C
 107 psi

@Strain 0.230 %,
Temperature -4.00 °F
 TPE; ISO 11403-1 -2
0.790 MPa

@Strain 0.230 %,
Temperature -40.0 °C
 115 psi

@Strain 0.230 %,
Temperature -40.0 °F
 TPE; ISO 11403-1 -2
3.57 MPa

@Strain 13.66 %,
Temperature 120 °C
 518 psi

@Strain 13.66 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.35 MPa

@Strain 36.25 %,
Temperature 120 °C
 631 psi

@Strain 36.25 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.51 MPa

@Strain 16.88 %,
Temperature 100 °C
 654 psi

@Strain 16.88 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.55 MPa

@Strain 59.97 %,
Temperature 120 °C
 660 psi

@Strain 59.97 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.68 MPa

@Strain 13.76 %,
Temperature 90.0 °C
 679 psi

@Strain 13.76 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.75 MPa

@Strain 82.17 %,
Temperature 120 °C
 689 psi

@Strain 82.17 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.08 MPa

@Strain 108.54 %,
Temperature 120 °C
 737 psi

@Strain 108.54 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.28 MPa

@Strain 39.03 %,
Temperature 100 °C
 766 psi

@Strain 39.03 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.48 MPa

@Strain 131.34 %,
Temperature 120 °C
 795 psi

@Strain 131.34 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.51 MPa

@Strain 62.75 %,
Temperature 100 °C
 799 psi

@Strain 62.75 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.74 MPa

@Strain 15.77 %,
Temperature 60.0 °C
 833 psi

@Strain 15.77 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
5.79 MPa

@Strain 85.8 %,
Temperature 100 °C
 840 psi

@Strain 85.8 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.82 MPa

@Strain 34.96 %,
Temperature 90.0 °C
 844 psi

@Strain 34.96 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
5.93 MPa

@Strain 151.87 %,
Temperature 120 °C
 860 psi

@Strain 151.87 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.08 MPa

@Strain 57.62 %,
Temperature 90.0 °C
 882 psi

@Strain 57.62 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.21 MPa

@Strain 112.58 %,
Temperature 100 °C
 901 psi

@Strain 112.58 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
6.21 MPa

@Strain 13.8 %,
Temperature 40.0 °C
 901 psi

@Strain 13.8 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
6.36 MPa

@Strain 80.48 %,
Temperature 90.0 °C
 922 psi

@Strain 80.48 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.40 MPa

@Strain 171.15 %,
Temperature 120 °C
 928 psi

@Strain 171.15 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.70 MPa

@Strain 135.53 %,
Temperature 100 °C
 972 psi

@Strain 135.53 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
6.81 MPa

@Strain 108.12 %,
Temperature 90.0 °C
 988 psi

@Strain 108.12 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.97 MPa

@Strain 35.94 %,
Temperature 60.0 °C
 1010 psi

@Strain 35.94 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
7.13 MPa

@Strain 198.69 %,
Temperature 120 °C
 1030 psi

@Strain 198.69 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.22 MPa

@Strain 156.5 %,
Temperature 100 °C
 1050 psi

@Strain 156.5 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.33 MPa

@Strain 132.05 %,
Temperature 90.0 °C
 1060 psi

@Strain 132.05 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.33 MPa

@Strain 14.02 %,
Temperature 23.0 °C
 1060 psi

@Strain 14.02 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
7.37 MPa

@Strain 57.56 %,
Temperature 60.0 °C
 1070 psi

@Strain 57.56 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
7.59 MPa

@Strain 215.82 %,
Temperature 120 °C
 1100 psi

@Strain 215.82 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.77 MPa

@Strain 176.38 %,
Temperature 100 °C
 1130 psi

@Strain 176.38 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.77 MPa

@Strain 78.7 %,
Temperature 60.0 °C
 1130 psi

@Strain 78.7 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
7.89 MPa

@Strain 33.37 %,
Temperature 40.0 °C
 1140 psi

@Strain 33.37 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
7.89 MPa

@Strain 153.83 %,
Temperature 90.0 °C
 1140 psi

@Strain 153.83 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.96 MPa

@Strain 232.29 %,
Temperature 120 °C
 1150 psi

@Strain 232.29 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.35 MPa

@Strain 104.31 %,
Temperature 60.0 °C
 1210 psi

@Strain 104.31 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
8.42 MPa

@Strain 54.54 %,
Temperature 40.0 °C
 1220 psi

@Strain 54.54 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
8.47 MPa

@Strain 174.29 %,
Temperature 90.0 °C
 1230 psi

@Strain 174.29 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.50 MPa

@Strain 249.44 %,
Temperature 120 °C
 1230 psi

@Strain 249.44 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.62 MPa

@Strain 204.54 %,
Temperature 100 °C
 1250 psi

@Strain 204.54 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.83 MPa

@Strain 15.27 %,
Temperature 0.000 °C
 1280 psi

@Strain 15.27 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
8.87 MPa

@Strain 75.25 %,
Temperature 40.0 °C
 1290 psi

@Strain 75.25 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
8.95 MPa

@Strain 127.48 %,
Temperature 60.0 °C
 1300 psi

@Strain 127.48 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
9.14 MPa

@Strain 221.82 %,
Temperature 100 °C
 1330 psi

@Strain 221.82 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2