DuPont Performance Polymers Hytrel® 4056 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 4056 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40 Shore D High Performance Polyester ElastomerInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
1.16 g/cc
0.0419 lb/in³
ISO 1183
Water Absorption 0.70 %

@Thickness 2.00 mm
 0.70 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
Immersion 24h; ASTM D570
Viscosity 102000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 102000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
117000 cP

@Shear Rate 5000 1/s,
Temperature 210 °C
 117000 cP

@Shear Rate 5000 1/s,
Temperature 410 °F
 ISO 11403-1 -2
134000 cP

@Shear Rate 5000 1/s,
Temperature 190 °C
 134000 cP

@Shear Rate 5000 1/s,
Temperature 374 °F
 ISO 11403-1 -2
267000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 267000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
352000 cP

@Shear Rate 500 1/s,
Temperature 210 °C
 352000 cP

@Shear Rate 500 1/s,
Temperature 410 °F
 ISO 11403-1 -2
461000 cP

@Shear Rate 500 1/s,
Temperature 190 °C
 461000 cP

@Shear Rate 500 1/s,
Temperature 374 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ISO 294-4 2577
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
5.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 37
37
15s; ISO 868
<= 43
<= 43
ISO 868
Tensile Strength at Break 26.0 MPa
3770 psi
ISO 527-1/-2
Tensile Stress 2.40 MPa

@Strain 5.00 %
 348 psi

@Strain 5.00 %
 ISO 527-1/-2
4.60 MPa

@Strain 10.0 %
 667 psi

@Strain 10.0 %
 ISO 527-1/-2
8.40 MPa

@Strain 50.0 %
 1220 psi

@Strain 50.0 %
 ISO 527-1/-2
0.850 MPa

@Strain 6.36 %,
Temperature 120 °C
 123 psi

@Strain 6.36 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.36 MPa

@Strain 14.38 %,
Temperature 120 °C
 197 psi

@Strain 14.38 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.36 MPa

@Strain 5.82 %,
Temperature 100 °C
 197 psi

@Strain 5.82 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
1.56 MPa

@Strain 6.00 %,
Temperature 90.0 °C
 226 psi

@Strain 6.00 %,
Temperature 194 °F
 ISO 11403-1 -2
1.68 MPa

@Strain 23.08 %,
Temperature 120 °C
 244 psi

@Strain 23.08 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.70 MPa

@Strain 6.03 %,
Temperature 90.0 °C
 247 psi

@Strain 6.03 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
1.87 MPa

@Strain 31.78 %,
Temperature 120 °C
 271 psi

@Strain 31.78 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.99 MPa

@Strain 40.48 %,
Temperature 120 °C
 289 psi

@Strain 40.48 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.09 MPa

@Strain 51.85 %,
Temperature 120 °C
 303 psi

@Strain 51.85 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.12 MPa

@Strain 5.92 %,
Temperature 60.0 °C
 307 psi

@Strain 5.92 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
2.16 MPa

@Strain 63.22 %,
Temperature 120 °C
 313 psi

@Strain 63.22 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.23 MPa

@Strain 74.6 %,
Temperature 120 °C
 323 psi

@Strain 74.6 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.30 MPa

@Strain 86.64 %,
Temperature 120 °C
 334 psi

@Strain 86.64 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.35 MPa

@Strain 14.73 %,
Temperature 100 °C
 341 psi

@Strain 14.73 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.40 MPa

@Strain 103.36 %,
Temperature 120 °C
 348 psi

@Strain 103.36 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.46 MPa

@Strain 114.74 %,
Temperature 120 °C
 357 psi

@Strain 114.74 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.56 MPa

@Strain 129.46 %,
Temperature 120 °C
 371 psi

@Strain 129.46 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.64 MPa

@Strain 6.00 %,
Temperature 40.0 °C
 383 psi

@Strain 6.00 %,
Temperature 104 °F
 ISO 11403-1 -2
2.69 MPa

@Strain 149.53 %,
Temperature 120 °C
 390 psi

@Strain 149.53 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.82 MPa

@Strain 22.95 %,
Temperature 100 °C
 409 psi

@Strain 22.95 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.86 MPa

@Strain 172.27 %,
Temperature 120 °C
 415 psi

@Strain 172.27 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.89 MPa

@Strain 15.24 %,
Temperature 90.0 °C
 419 psi

@Strain 15.24 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.90 MPa

@Strain 6.00 %,
Temperature 23.0 °C
 421 psi

@Strain 6.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.97 MPa

@Strain 24.0 %,
Temperature 90.0 °C
 431 psi

@Strain 24.0 %,
Temperature 194 °F
 ISO 11403-1 -2
2.99 MPa

@Strain 6.81 %,
Temperature 40.0 °C
 434 psi

@Strain 6.81 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
3.06 MPa

@Strain 201.04 %,
Temperature 120 °C
 444 psi

@Strain 201.04 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.08 MPa

@Strain 31.86 %,
Temperature 100 °C
 447 psi

@Strain 31.86 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.21 MPa

@Strain 40.77 %,
Temperature 100 °C
 466 psi

@Strain 40.77 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.22 MPa

@Strain 42.0 %,
Temperature 90.0 °C
 467 psi

@Strain 42.0 %,
Temperature 194 °F
 ISO 11403-1 -2
3.30 MPa

@Strain 51.73 %,
Temperature 100 °C
 479 psi

@Strain 51.73 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.38 MPa

@Strain 63.38 %,
Temperature 100 °C
 490 psi

@Strain 63.38 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.39 MPa

@Strain 23.75 %,
Temperature 90.0 °C
 492 psi

@Strain 23.75 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.44 MPa

@Strain 75.03 %,
Temperature 100 °C
 499 psi

@Strain 75.03 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.52 MPa

@Strain 86.68 %,
Temperature 100 °C
 511 psi

@Strain 86.68 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.56 MPa

@Strain 6.00 %,
Temperature 0.000 °C
 516 psi

@Strain 6.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
3.65 MPa

@Strain 103.81 %,
Temperature 100 °C
 529 psi

@Strain 103.81 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.66 MPa

@Strain 32.97 %,
Temperature 90.0 °C
 531 psi

@Strain 32.97 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.67 MPa

@Strain 14.98 %,
Temperature 60.0 °C
 532 psi

@Strain 14.98 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
3.74 MPa

@Strain 114.77 %,
Temperature 100 °C
 542 psi

@Strain 114.77 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.76 MPa

@Strain 41.48 %,
Temperature 90.0 °C
 545 psi

@Strain 41.48 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.86 MPa

@Strain 52.82 %,
Temperature 90.0 °C
 560 psi

@Strain 52.82 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.87 MPa

@Strain 129.16 %,
Temperature 100 °C
 561 psi

@Strain 129.16 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.92 MPa

@Strain 64.88 %,
Temperature 90.0 °C
 569 psi

@Strain 64.88 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.98 MPa

@Strain 76.93 %,
Temperature 90.0 °C
 577 psi

@Strain 76.93 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.07 MPa

@Strain 88.28 %,
Temperature 90.0 °C
 590 psi

@Strain 88.28 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2