DuPont Performance Polymers Delrin® FG570 NC000 Acetal Homopolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® FG570 NC000 Acetal Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® FG570 NC000 is a medium viscosity acetal homopolymer containing 20% glass fiber for injection molding. It has high stiffness and low warpage. It has been developed for consideration in applications and parts for the food industry.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
ISO 1183
Water Absorption 0.10 %

@Temperature 23.0 °C
0.10 %

@Temperature 73.4 °F
Equilibrium 50%RH; ISO 62, Similar to
0.80 %

@Temperature 23.0 °C
0.80 %

@Temperature 73.4 °F
Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.016 cm/cm

@Thickness 2.00 mm
0.016 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.012 cm/cm

@Thickness 2.00 mm
0.012 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Index of Compound 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa

@Temperature 23.0 °C
7690 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 12 %

@Temperature 23.0 °C
12 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 4.90 GPa

@Temperature 23.0 °C
711 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 4.60 GPa

@Temperature 23.0 °C
667 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact Unnotched 5.00 J/cm²

@Temperature -30.0 °C
23.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
5.40 J/cm²

@Temperature 23.0 °C
25.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.350 J/cm²

@Temperature 23.0 °C
1.67 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature 23.0 - 55.0 °C
278 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 85.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
47.2 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
ISO 75-1/-2
Processing Properties Metric English Comments
Melt Temperature 215 °C
419 °F
Optimum; Injection Molding
210 - 220 °C
410 - 428 °F
Injection Molding
Mold Temperature 90.0 °C
194 °F
optimum; Injection Molding
80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Moisture Content <= 0.10 %
<= 0.10 %
Injection Molding
Descriptive Properties Value Comments
Appearance Natural Color
Forms Pellets
Generic POM
Material Status Preliminary Data
Part Marking Code >POM-GF20<
ISO 11469
Processing Method Injection Molding
Product Category Food Contact Resins
Glass or Mineral Filled Resins
Region Available - Global Yes
Resin Identification POM-GF20
ISO 1043
RoHS Compliance Contact Manufacturer
Uses Food Applications, Non-specific