DuPont Performance Polymers Delrin® FG511DP NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® FG511DP NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nucleated Medium Viscosity Acetal Homopolymer Developed for Food Contact Applications Delrin FG511DP is a medium viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding. It has been developed for considerInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.90 %

@Thickness 2.00 mm
 0.90 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
14 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 15.4 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 2230 psi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
17.8 MPa

@Strain 0.500 %,
Temperature 0.000 °C
 2580 psi

@Strain 0.500 %,
Temperature 32.0 °F
 ISO 11403-1 -2
21.0 MPa

@Strain 0.500 %,
Temperature -40.0 °C
 3050 psi

@Strain 0.500 %,
Temperature -40.0 °F
 ISO 11403-1 -2
50.3 MPa

@Strain 2.20 %,
Temperature 23.0 °C
 7300 psi

@Strain 2.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
56.4 MPa

@Strain 2.20 %,
Temperature 0.000 °C
 8180 psi

@Strain 2.20 %,
Temperature 32.0 °F
 ISO 11403-1 -2
63.0 MPa

@Strain 3.80 %,
Temperature 23.0 °C
 9140 psi

@Strain 3.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
67.8 MPa

@Strain 2.00 %,
Temperature -40.0 °C
 9830 psi

@Strain 2.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
68.8 MPa

@Strain 6.00 %,
Temperature 23.0 °C
 9980 psi

@Strain 6.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
70.7 MPa

@Strain 3.80 %,
Temperature 0.000 °C
 10300 psi

@Strain 3.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
75.1 MPa

@Strain 5.00 %,
Temperature 0.000 °C
 10900 psi

@Strain 5.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
88.3 MPa

@Strain 3.60 %,
Temperature -40.0 °C
 12800 psi

@Strain 3.60 %,
Temperature -40.0 °F
 ISO 11403-1 -2
94.6 MPa

@Strain 5.00 %,
Temperature -40.0 °C
 13700 psi

@Strain 5.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 73.0 MPa
10600 psi
ISO 527-1/-2
Elongation at Break 25 %
25 %
Nominal; ISO 527-1/-2
Elongation at Yield 12 %
12 %
ISO 527-1/-2
Tensile Modulus 3.40 GPa
493 ksi
ISO 527-1/-2
Flexural Strength 87.0 MPa

@Strain 3.50 %
 12600 psi

@Strain 3.50 %
 ISO 178
Flexural Modulus 3.20 GPa
464 ksi
ISO 178
Secant Modulus 0.365 GPa

@Strain 8.00 %,
Temperature 100 °C
 52.9 ksi

@Strain 8.00 %,
Temperature 212 °F
 ISO 11403-1 -2
0.575 GPa

@Strain 4.80 %,
Temperature 100 °C
 83.4 ksi

@Strain 4.80 %,
Temperature 212 °F
 ISO 11403-1 -2
0.637 GPa

@Strain 6.00 %,
Temperature 80.0 °C
 92.3 ksi

@Strain 6.00 %,
Temperature 176 °F
 ISO 11403-1 -2
0.747 GPa

@Strain 3.20 %,
Temperature 100 °C
 108 ksi

@Strain 3.20 %,
Temperature 212 °F
 ISO 11403-1 -2
0.87875 GPa

@Strain 8.00 %,
Temperature 23.0 °C
 127.45 ksi

@Strain 8.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.889 GPa

@Strain 3.80 %,
Temperature 80.0 °C
 129 ksi

@Strain 3.80 %,
Temperature 176 °F
 ISO 11403-1 -2
0.975 GPa

@Strain 1.60 %,
Temperature 100 °C
 141 ksi

@Strain 1.60 %,
Temperature 212 °F
 ISO 11403-1 -2
1.11 GPa

@Strain 7.00 %,
Temperature 0.000 °C
 162 ksi

@Strain 7.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
1.15 GPa

@Strain 0.400 %,
Temperature 100 °C
 167 ksi

@Strain 0.400 %,
Temperature 212 °F
 ISO 11403-1 -2
1.23 GPa

@Strain 1.90 %,
Temperature 80.0 °C
 179 ksi

@Strain 1.90 %,
Temperature 176 °F
 ISO 11403-1 -2
1.38 GPa

@Strain 7.00 %,
Temperature -40.0 °C
 201 ksi

@Strain 7.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.49 GPa

@Strain 4.40 %,
Temperature 23.0 °C
 216 ksi

@Strain 4.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.60 GPa

@Strain 0.400 %,
Temperature 80.0 °C
 232 ksi

@Strain 0.400 %,
Temperature 176 °F
 ISO 11403-1 -2
1.67 GPa

@Strain 4.40 %,
Temperature 0.000 °C
 242 ksi

@Strain 4.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
2.23 GPa

@Strain 4.10 %,
Temperature -40.0 °C
 323 ksi

@Strain 4.10 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.29 GPa

@Strain 2.20 %,
Temperature 23.0 °C
 332 ksi

@Strain 2.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.56 GPa

@Strain 2.20 %,
Temperature 0.000 °C
 372 ksi

@Strain 2.20 %,
Temperature 32.0 °F
 ISO 11403-1 -2
3.08 GPa

@Strain 0.500 %,
Temperature 23.0 °C
 447 ksi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.39 GPa

@Strain 2.00 %,
Temperature -40.0 °C
 492 ksi

@Strain 2.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
3.56 GPa

@Strain 0.500 %,
Temperature 0.000 °C
 516 ksi

@Strain 0.500 %,
Temperature 32.0 °F
 ISO 11403-1 -2
4.20 GPa

@Strain 0.500 %,
Temperature -40.0 °C
 609 ksi

@Strain 0.500 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 22.0 J/cm²
105 ft-lb/in²
ISO 179/1eU
20.0 J/cm²

@Temperature -30.0 °C
 95.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/1eA
0.650 J/cm²

@Temperature -30.0 °C
 3.09 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
ISO 75-1/-2
Vicat Softening Point 160 °C
320 °F
50°C/h 50N; ISO 306
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >POM<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM