DuPont Performance Polymers Delrin® FG500TL NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® FG500TL NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Teflon® Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Developed for Food Contact ApplicationsDelrin FG500TL medium viscosity acetal homopolymer resin containing 1.5% Teflon PTFE Micropowder. It has been developed for conInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Water Absorption 0.90 %

@Thickness 2.00 mm
 0.90 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.170 %

@Thickness 2.00 mm
 0.170 %

@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.017 cm/cm
0.017 in/in
ISO 294-4 2577
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
14 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 31.8 MPa

@Strain 1.10 %,
Temperature 23.0 °C
 4610 psi

@Strain 1.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
34.3 MPa

@Strain 1.10 %,
Temperature 0.000 °C
 4970 psi

@Strain 1.10 %,
Temperature 32.0 °F
 ISO 11403-1 -2
36.6 MPa

@Strain 0.900 %,
Temperature -40.0 °C
 5310 psi

@Strain 0.900 %,
Temperature -40.0 °F
 ISO 11403-1 -2
62.6 MPa

@Strain 4.40 %,
Temperature 23.0 °C
 9080 psi

@Strain 4.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
66.6 MPa

@Strain 7.70 %,
Temperature 23.0 °C
 9660 psi

@Strain 7.70 %,
Temperature 73.4 °F
 ISO 11403-1 -2
67.2 MPa

@Strain 11.0 %,
Temperature 23.0 °C
 9750 psi

@Strain 11.0 %,
Temperature 73.4 °F
 ISO 11403-1 -2
71.7 MPa

@Strain 4.30 %,
Temperature 0.000 °C
 10400 psi

@Strain 4.30 %,
Temperature 32.0 °F
 ISO 11403-1 -2
76.7 MPa

@Strain 7.60 %,
Temperature 0.000 °C
 11100 psi

@Strain 7.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
77.5 MPa

@Strain 10.8 %,
Temperature 0.000 °C
 11200 psi

@Strain 10.8 %,
Temperature 32.0 °F
 ISO 11403-1 -2
88.1 MPa

@Strain 3.70 %,
Temperature -40.0 °C
 12800 psi

@Strain 3.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
96.6 MPa

@Strain 6.50 %,
Temperature -40.0 °C
 14000 psi

@Strain 6.50 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 71.0 MPa
10300 psi
ISO 527-1/-2
Elongation at Break 20 %
20 %
Nominal; ISO 527-1/-2
Elongation at Yield 13 %
13 %
ISO 527-1/-2
Tensile Modulus 3.30 GPa
479 ksi
ISO 527-1/-2
Flexural Modulus 3.10 GPa
450 ksi
ISO 178
Secant Modulus 0.425 GPa

@Strain 7.10 %,
Temperature 100 °C
 61.7 ksi

@Strain 7.10 %,
Temperature 212 °F
 ISO 11403-1 -2
0.532 GPa

@Strain 7.50 %,
Temperature 80.0 °C
 77.2 ksi

@Strain 7.50 %,
Temperature 176 °F
 ISO 11403-1 -2
0.689 GPa

@Strain 3.50 %,
Temperature 100 °C
 99.9 ksi

@Strain 3.50 %,
Temperature 212 °F
 ISO 11403-1 -2
0.760 GPa

@Strain 8.80 %,
Temperature 23.0 °C
 110 ksi

@Strain 8.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.882 GPa

@Strain 3.80 %,
Temperature 80.0 °C
 128 ksi

@Strain 3.80 %,
Temperature 176 °F
 ISO 11403-1 -2
0.897 GPa

@Strain 8.60 %,
Temperature 0.000 °C
 130 ksi

@Strain 8.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.944 GPa

@Strain 0.900 %,
Temperature 100 °C
 137 ksi

@Strain 0.900 %,
Temperature 212 °F
 ISO 11403-1 -2
1.31 GPa

@Strain 7.40 %,
Temperature -40.0 °C
 190 ksi

@Strain 7.40 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.38 GPa

@Strain 0.900 %,
Temperature 80.0 °C
 200 ksi

@Strain 0.900 %,
Temperature 176 °F
 ISO 11403-1 -2
1.42 GPa

@Strain 4.40 %,
Temperature 23.0 °C
 206 ksi

@Strain 4.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.67 GPa

@Strain 4.30 %,
Temperature 0.000 °C
 242 ksi

@Strain 4.30 %,
Temperature 32.0 °F
 ISO 11403-1 -2
2.38 GPa

@Strain 3.70 %,
Temperature -40.0 °C
 345 ksi

@Strain 3.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.89 GPa

@Strain 1.10 %,
Temperature 23.0 °C
 419 ksi

@Strain 1.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.12 GPa

@Strain 1.10 %,
Temperature 0.000 °C
 452 ksi

@Strain 1.10 %,
Temperature 32.0 °F
 ISO 11403-1 -2
4.07 GPa

@Strain 0.900 %,
Temperature -40.0 °C
 590 ksi

@Strain 0.900 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180/1A
6.00 kJ/m²

@Temperature -40.0 °C
 2.86 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Charpy Impact Unnotched 17.0 J/cm²
80.9 ft-lb/in²
ISO 179/1eU
16.0 J/cm²

@Temperature -30.0 °C
 76.1 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 103 °C
217 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >POM-SD<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM-SD
ISO 1043