DuPont Performance Polymers Delrin® FG500P NC010 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® FG500P NC010 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® FG500P is a medium viscosity acetal homopolymer, with improved thermal stability. It has been developed for consideration into applications such as parts for the food industry.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.30 %

@Temperature 23.0 °C
0.30 %

@Temperature 73.4 °F
Equilibrium 50%RH; ISO 62, Similar to
0.60 %

@Temperature 23.0 °C
0.60 %

@Temperature 73.4 °F
Immersion 24h; ISO 62, Similar to
1.4 %

@Temperature 23.0 °C
1.4 %

@Temperature 73.4 °F
Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.020 cm/cm

@Thickness 2.00 mm
0.020 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.019 cm/cm

@Thickness 2.00 mm
0.019 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Melt Index of Compound 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 70.0 MPa

@Temperature 23.0 °C
10200 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 30 %

@Temperature 23.0 °C
30 %

@Temperature 73.4 °F
nominal; ISO 527
Elongation at Yield 17 %

@Temperature 23.0 °C
17 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 3.10 GPa

@Temperature 23.0 °C
450 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 2.90 GPa

@Temperature 23.0 °C
421 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact Unnotched 24.0 J/cm²

@Temperature -30.0 °C
114 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
30.0 J/cm²

@Temperature 23.0 °C
143 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature -40.0 °C
3.81 ft-lb/in²

@Temperature -40.0 °F
ISO 179/1eA
0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 2800 MPa

@Temperature 23.0 °C
406000 psi

@Temperature 73.4 °F
ISO 899
Tensile Creep Modulus, 1000 hours 1600 MPa

@Temperature 23.0 °C
232000 psi

@Temperature 73.4 °F
ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
278 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
278 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 100 °C
278 µin/in-°F

@Temperature 131 - 212 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature -40.0 - 23.0 °C
55.6 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
110 µm/m-°C

@Temperature 23.0 - 55.0 °C
61.1 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
160 µm/m-°C

@Temperature 55.0 - 100 °C
88.9 µin/in-°F

@Temperature 131 - 212 °F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 158 °C
316 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
ISO 75-1/-2
Processing Properties Metric English Comments
Melt Temperature 215 °C
419 °F
Optimum; Injection Molding
210 - 220 °C
410 - 428 °F
Injection Molding
Mold Temperature 90.0 °C
194 °F
optimum; Injection Molding
80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Moisture Content <= 0.20 %
<= 0.20 %
Injection Molding
Descriptive Properties Value Comments
Appearance Natural Color
Features Creep Resistance, Good
Dimensional Stability, Good
Fatigue Resistant
Homopolymer
Impact Resistance, Good
Stiffness, High
Strength, High
Viscosity, Medium
Forms Pellets
Generic Acetal (POM) Homopolymer
Material Status Preliminary Data
Part Marking Code >POM<
ISO 11469
Processing Method Injection Molding
Product Category Food Contact Resins
Unreinforced Resins
Region Available - Global Yes
Resin Identification POM
ISO 1043
RoHS Compliance Contact Manufacturer
Uses Fasteners
Food Applications, Non-specific
Gears
General Purpose
Parts, Engineering