DuPont Performance Polymers Delrin® FG311DP NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® FG311DP NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nucleated Medium-high Viscosity Acetal Homopolymer Developed for Food Contact Applications Delrin FG311DP is a medium-high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding. It has been developed foInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.90 %

@Thickness 2.00 mm
0.90 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
0.200 %

@Thickness 0.0787 in
Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm³/10min; ISO 1133
7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 4.47 MPa

@Strain 0.150 %,
Temperature 40.0 °C
648 psi

@Strain 0.150 %,
Temperature 104 °F
ISO 11403-1 -2
6.31 MPa

@Strain 0.460 %,
Temperature 90.0 °C
915 psi

@Strain 0.460 %,
Temperature 194 °F
ISO 11403-1 -2
9.92 MPa

@Strain 0.290 %,
Temperature 23.0 °C
1440 psi

@Strain 0.290 %,
Temperature 73.4 °F
ISO 11403-1 -2
21.3 MPa

@Strain 0.611 %,
Temperature 0.000 °C
3090 psi

@Strain 0.611 %,
Temperature 32.0 °F
ISO 11403-1 -2
24.56 MPa

@Strain 2.58 %,
Temperature 90.0 °C
3562 psi

@Strain 2.58 %,
Temperature 194 °F
ISO 11403-1 -2
27.19 MPa

@Strain 0.730 %,
Temperature -20.0 °C
3944 psi

@Strain 0.730 %,
Temperature -4.00 °F
ISO 11403-1 -2
27.45 MPa

@Strain 0.690 %,
Temperature -40.0 °C
3981 psi

@Strain 0.690 %,
Temperature -40.0 °F
ISO 11403-1 -2
32.21 MPa

@Strain 4.88 %,
Temperature 90.0 °C
4672 psi

@Strain 4.88 %,
Temperature 194 °F
ISO 11403-1 -2
37.04 MPa

@Strain 1.71 %,
Temperature 40.0 °C
5372 psi

@Strain 1.71 %,
Temperature 104 °F
ISO 11403-1 -2
50.17 MPa

@Strain 2.29 %,
Temperature 23.0 °C
7277 psi

@Strain 2.29 %,
Temperature 73.4 °F
ISO 11403-1 -2
54.39 MPa

@Strain 3.93 %,
Temperature 40.0 °C
7889 psi

@Strain 3.93 %,
Temperature 104 °F
ISO 11403-1 -2
56.48 MPa

@Strain 2.29 %,
Temperature 0.000 °C
8192 psi

@Strain 2.29 %,
Temperature 32.0 °F
ISO 11403-1 -2
60.28 MPa

@Strain 6.41 %,
Temperature 40.0 °C
8743 psi

@Strain 6.41 %,
Temperature 104 °F
ISO 11403-1 -2
64.31 MPa

@Strain 4.58 %,
Temperature 23.0 °C
9327 psi

@Strain 4.58 %,
Temperature 73.4 °F
ISO 11403-1 -2
68.72 MPa

@Strain 7.21 %,
Temperature 23.0 °C
9967 psi

@Strain 7.21 %,
Temperature 73.4 °F
ISO 11403-1 -2
72.85 MPa

@Strain 4.53 %,
Temperature 0.000 °C
10570 psi

@Strain 4.53 %,
Temperature 32.0 °F
ISO 11403-1 -2
75.19 MPa

@Strain 3.25 %,
Temperature -20.0 °C
10910 psi

@Strain 3.25 %,
Temperature -4.00 °F
ISO 11403-1 -2
77.78 MPa

@Strain 7.12 %,
Temperature 0.000 °C
11280 psi

@Strain 7.12 %,
Temperature 32.0 °F
ISO 11403-1 -2
80.68 MPa

@Strain 3.12 %,
Temperature -40.0 °C
11700 psi

@Strain 3.12 %,
Temperature -40.0 °F
ISO 11403-1 -2
85.65 MPa

@Strain 5.67 %,
Temperature -20.0 °C
12420 psi

@Strain 5.67 %,
Temperature -4.00 °F
ISO 11403-1 -2
88.5 MPa

@Strain 8.47 %,
Temperature -20.0 °C
12800 psi

@Strain 8.47 %,
Temperature -4.00 °F
ISO 11403-1 -2
93.8 MPa

@Strain 5.11 %,
Temperature -40.0 °C
13600 psi

@Strain 5.11 %,
Temperature -40.0 °F
ISO 11403-1 -2
97.6 MPa

@Strain 7.38 %,
Temperature -40.0 °C
14200 psi

@Strain 7.38 %,
Temperature -40.0 °F
ISO 11403-1 -2
Tensile Strength, Yield 74.0 MPa
10700 psi
ISO 527-1/-2
Elongation at Break 35 %
35 %
Nominal; ISO 527-1/-2
Elongation at Yield 15 %
15 %
ISO 527-1/-2
Tensile Modulus 3.30 GPa
479 ksi
ISO 527-1/-2
Flexural Strength 86.0 MPa

@Strain 3.50 %
12500 psi

@Strain 3.50 %
ISO 178
Flexural Modulus 3.10 GPa
450 ksi
ISO 178
Secant Modulus 0.570 GPa

@Strain 5.00 %,
Temperature 100 °C
82.7 ksi

@Strain 5.00 %,
Temperature 212 °F
ISO 11403-1 -2
0.591 GPa

@Strain 7.00 %,
Temperature 80.0 °C
85.8 ksi

@Strain 7.00 %,
Temperature 176 °F
ISO 11403-1 -2
0.736 GPa

@Strain 3.30 %,
Temperature 100 °C
107 ksi

@Strain 3.30 %,
Temperature 212 °F
ISO 11403-1 -2
0.754 GPa

@Strain 8.18 %,
Temperature 40.0 °C
109 ksi

@Strain 8.18 %,
Temperature 104 °F
ISO 11403-1 -2
0.9075 GPa

@Strain 4.00 %,
Temperature 80.0 °C
131.6 ksi

@Strain 4.00 %,
Temperature 176 °F
ISO 11403-1 -2
0.99375 GPa

@Strain 1.60 %,
Temperature 100 °C
144.13 ksi

@Strain 1.60 %,
Temperature 212 °F
ISO 11403-1 -2
1.15 GPa

@Strain 0.400 %,
Temperature 100 °C
167 ksi

@Strain 0.400 %,
Temperature 212 °F
ISO 11403-1 -2
1.2163 GPa

@Strain 5.46 %,
Temperature 23.0 °C
176.41 ksi

@Strain 5.46 %,
Temperature 73.4 °F
ISO 11403-1 -2
1.22 GPa

@Strain 4.70 %,
Temperature 40.0 °C
176 ksi

@Strain 4.70 %,
Temperature 104 °F
ISO 11403-1 -2
1.255 GPa

@Strain 2.00 %,
Temperature 80.0 °C
182.0 ksi

@Strain 2.00 %,
Temperature 176 °F
ISO 11403-1 -2
1.33 GPa

@Strain 6.56 %,
Temperature -20.0 °C
192 ksi

@Strain 6.56 %,
Temperature -4.00 °F
ISO 11403-1 -2
1.40 GPa

@Strain 5.38 %,
Temperature 0.000 °C
203 ksi

@Strain 5.38 %,
Temperature 32.0 °F
ISO 11403-1 -2
1.63 GPa

@Strain 5.86 %,
Temperature -40.0 °C
237 ksi

@Strain 5.86 %,
Temperature -40.0 °F
ISO 11403-1 -2
1.64 GPa

@Strain 0.500 %,
Temperature 80.0 °C
238 ksi

@Strain 0.500 %,
Temperature 176 °F
ISO 11403-1 -2
2.17 GPa

@Strain 1.71 %,
Temperature 40.0 °C
314 ksi

@Strain 1.71 %,
Temperature 104 °F
ISO 11403-1 -2
2.19 GPa

@Strain 2.29 %,
Temperature 23.0 °C
318 ksi

@Strain 2.29 %,
Temperature 73.4 °F
ISO 11403-1 -2
2.31 GPa

@Strain 3.25 %,
Temperature -20.0 °C
336 ksi

@Strain 3.25 %,
Temperature -4.00 °F
ISO 11403-1 -2
2.47 GPa

@Strain 2.29 %,
Temperature 0.000 °C
358 ksi

@Strain 2.29 %,
Temperature 32.0 °F
ISO 11403-1 -2
2.5859 GPa

@Strain 3.12 %,
Temperature -40.0 °C
375.06 ksi

@Strain 3.12 %,
Temperature -40.0 °F
ISO 11403-1 -2
2.98 GPa

@Strain 0.150 %,
Temperature 40.0 °C
432 ksi

@Strain 0.150 %,
Temperature 104 °F
ISO 11403-1 -2
3.42 GPa

@Strain 0.290 %,
Temperature 23.0 °C
496 ksi

@Strain 0.290 %,
Temperature 73.4 °F
ISO 11403-1 -2
3.49 GPa

@Strain 0.611 %,
Temperature 0.000 °C
506 ksi

@Strain 0.611 %,
Temperature 32.0 °F
ISO 11403-1 -2
3.72 GPa

@Strain 0.730 %,
Temperature -20.0 °C
540 ksi

@Strain 0.730 %,
Temperature -4.00 °F
ISO 11403-1 -2
3.98 GPa

@Strain 0.690 %,
Temperature -40.0 °C
577 ksi

@Strain 0.690 %,
Temperature -40.0 °F
ISO 11403-1 -2
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180/1A
8.00 kJ/m²

@Temperature -40.0 °C
3.81 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
Charpy Impact Unnotched 30.0 J/cm²
143 ft-lb/in²
ISO 179/1eU
25.0 J/cm²

@Temperature -30.0 °C
119 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA