DuPont Performance Polymers Delrin® FG100AL NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® FG100AL NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lubricated High Viscosity Acetal Homopolymer with Low Wear and Low Friction Developed for Food Contact Applications Delrin FG100AL is a high viscosity lubricated acetal homopolymer resin containing an advanced system of lubrication. It has been developInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Viscosity 111000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 111000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
129000 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
 129000 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
 ISO 11403-1 -2
152000 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
 152000 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
 ISO 11403-1 -2
432000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 432000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
502000 cP

@Shear Rate 500 1/s,
Temperature 215 °C
 502000 cP

@Shear Rate 500 1/s,
Temperature 419 °F
 ISO 11403-1 -2
593000 cP

@Shear Rate 500 1/s,
Temperature 200 °C
 593000 cP

@Shear Rate 500 1/s,
Temperature 392 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 44.9 MPa

@Strain 2.20 %,
Temperature 23.0 °C
 6510 psi

@Strain 2.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
57.6 MPa

@Strain 1.80 %,
Temperature -40.0 °C
 8350 psi

@Strain 1.80 %,
Temperature -40.0 °F
 ISO 11403-1 -2
64.5 MPa

@Strain 8.00 %,
Temperature 23.0 °C
 9350 psi

@Strain 8.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
65.6 MPa

@Strain 15.0 %,
Temperature 23.0 °C
 9510 psi

@Strain 15.0 %,
Temperature 73.4 °F
 ISO 11403-1 -2
94.1 MPa

@Strain 7.00 %,
Temperature -40.0 °C
 13600 psi

@Strain 7.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
96.0 MPa

@Strain 13.0 %,
Temperature -40.0 °C
 13900 psi

@Strain 13.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 45 %
45 %
Nominal; ISO 527-1/-2
Elongation at Yield 18 %
18 %
ISO 527-1/-2
Tensile Modulus 3.00 GPa
435 ksi
ISO 527-1/-2
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Secant Modulus 0.141 GPa

@Strain 19.0 %,
Temperature 100 °C
 20.4 ksi

@Strain 19.0 %,
Temperature 212 °F
 ISO 11403-1 -2
0.192 GPa

@Strain 19.0 %,
Temperature 80.0 °C
 27.8 ksi

@Strain 19.0 %,
Temperature 176 °F
 ISO 11403-1 -2
0.286 GPa

@Strain 9.00 %,
Temperature 100 °C
 41.4 ksi

@Strain 9.00 %,
Temperature 212 °F
 ISO 11403-1 -2
0.386 GPa

@Strain 17.0 %,
Temperature 23.0 °C
 56.1 ksi

@Strain 17.0 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.393 GPa

@Strain 9.00 %,
Temperature 80.0 °C
 57.0 ksi

@Strain 9.00 %,
Temperature 176 °F
 ISO 11403-1 -2
0.640 GPa

@Strain 15.0 %,
Temperature -40.0 °C
 92.8 ksi

@Strain 15.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.80625 GPa

@Strain 8.00 %,
Temperature 23.0 °C
 116.94 ksi

@Strain 8.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.854 GPa

@Strain 2.40 %,
Temperature 100 °C
 124 ksi

@Strain 2.40 %,
Temperature 212 °F
 ISO 11403-1 -2
1.14 GPa

@Strain 2.40 %,
Temperature 80.0 °C
 166 ksi

@Strain 2.40 %,
Temperature 176 °F
 ISO 11403-1 -2
1.34 GPa

@Strain 7.00 %,
Temperature -40.0 °C
 195 ksi

@Strain 7.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.04 GPa

@Strain 2.20 %,
Temperature 23.0 °C
 296 ksi

@Strain 2.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.20 GPa

@Strain 1.80 %,
Temperature -40.0 °C
 464 ksi

@Strain 1.80 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 25.0 J/cm²
119 ft-lb/in²
ISO 179/1eU
17.0 J/cm²

@Temperature -30.0 °C
 80.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >POM-S<
ISO 11469
Processing Injection Moulding
Other Extrusion
Profile Extrusion
Sheet Extrusion
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM-S
ISO 1043
UL recognition UL