DuPont Performance Polymers Delrin® 900P BK602 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 900P BK602 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low Viscosity Acetal Homopolymer with Improved ProcessingDelrin 900P BK602 is a low viscosity black acetal homopolymer resin for multicavity and thin wall molding. It offers an improved processing thermal stability.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.017 cm/cm
0.017 in/in
ISO 294-4 2577
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 25 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 16.6 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 2410 psi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
35.5 MPa

@Strain 0.900 %,
Temperature -40.0 °C
 5150 psi

@Strain 0.900 %,
Temperature -40.0 °F
 ISO 11403-1 -2
51.4 MPa

@Strain 2.80 %,
Temperature 23.0 °C
 7450 psi

@Strain 2.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
62.2 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 9020 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
65.9 MPa

@Strain 8.00 %,
Temperature 23.0 °C
 9560 psi

@Strain 8.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
83.9 MPa

@Strain 3.70 %,
Temperature -40.0 °C
 12200 psi

@Strain 3.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
92.5 MPa

@Strain 6.00 %,
Temperature -40.0 °C
 13400 psi

@Strain 6.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
94.9 MPa

@Strain 9.00 %,
Temperature -40.0 °C
 13800 psi

@Strain 9.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 17 %
17 %
Nominal; ISO 527-1/-2
Elongation at Yield 12 %
12 %
ISO 527-1/-2
Tensile Modulus 3.30 GPa
479 ksi
ISO 527-1/-2
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Secant Modulus 0.524 GPa

@Strain 4.60 %,
Temperature 100 °C
 76.0 ksi

@Strain 4.60 %,
Temperature 212 °F
 ISO 11403-1 -2
0.588 GPa

@Strain 6.00 %,
Temperature 80.0 °C
 85.3 ksi

@Strain 6.00 %,
Temperature 176 °F
 ISO 11403-1 -2
0.663 GPa

@Strain 10.0 %,
Temperature 23.0 °C
 96.2 ksi

@Strain 10.0 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.708 GPa

@Strain 2.50 %,
Temperature 100 °C
 103 ksi

@Strain 2.50 %,
Temperature 212 °F
 ISO 11403-1 -2
0.865 GPa

@Strain 11.0 %,
Temperature -40.0 °C
 125 ksi

@Strain 11.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.921 GPa

@Strain 2.80 %,
Temperature 80.0 °C
 134 ksi

@Strain 2.80 %,
Temperature 176 °F
 ISO 11403-1 -2
0.9375 GPa

@Strain 0.800 %,
Temperature 100 °C
 136.0 ksi

@Strain 0.800 %,
Temperature 212 °F
 ISO 11403-1 -2
1.07 GPa

@Strain 6.00 %,
Temperature 23.0 °C
 155 ksi

@Strain 6.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.34 GPa

@Strain 7.00 %,
Temperature -40.0 °C
 194 ksi

@Strain 7.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.36 GPa

@Strain 0.900 %,
Temperature 80.0 °C
 197 ksi

@Strain 0.900 %,
Temperature 176 °F
 ISO 11403-1 -2
1.84 GPa

@Strain 2.80 %,
Temperature 23.0 °C
 266 ksi

@Strain 2.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.27 GPa

@Strain 3.70 %,
Temperature -40.0 °C
 329 ksi

@Strain 3.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
3.32 GPa

@Strain 0.500 %,
Temperature 23.0 °C
 482 ksi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.94 GPa

@Strain 0.900 %,
Temperature -40.0 °C
 572 ksi

@Strain 0.900 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/1A
7.00 kJ/m²

@Temperature -40.0 °C
 3.33 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Charpy Impact Unnotched 13.0 J/cm²
61.9 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
92.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 51.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
92.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 51.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 161 °C
322 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >POM<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM
ISO 1043
UL recognition UL