DuPont Performance Polymers Delrin® 500T NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced, Impact Grade
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500T NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Toughened Medium Viscosity Acetal Homopolymer Delrin 500T NC010 is a toughened medium viscosity acetal homopolymer resin with impact resistance similar to Delrin 100. It can be used in parts requiring noise reduction.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Water Absorption 0.82 %

@Thickness 2.00 mm
 0.82 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.210 %

@Thickness 2.00 mm
 0.210 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 69000 cP

@Shear Rate 5000 1/s,
Temperature 220 °C
 69000 cP

@Shear Rate 5000 1/s,
Temperature 428 °F
 ISO 11403-1 -2
83000 cP

@Shear Rate 5000 1/s,
Temperature 205 °C
 83000 cP

@Shear Rate 5000 1/s,
Temperature 401 °F
 ISO 11403-1 -2
102000 cP

@Shear Rate 5000 1/s,
Temperature 190 °C
 102000 cP

@Shear Rate 5000 1/s,
Temperature 374 °F
 ISO 11403-1 -2
211000 cP

@Shear Rate 500 1/s,
Temperature 220 °C
 211000 cP

@Shear Rate 500 1/s,
Temperature 428 °F
 ISO 11403-1 -2
277000 cP

@Shear Rate 500 1/s,
Temperature 205 °C
 277000 cP

@Shear Rate 500 1/s,
Temperature 401 °F
 ISO 11403-1 -2
365000 cP

@Shear Rate 500 1/s,
Temperature 190 °C
 365000 cP

@Shear Rate 500 1/s,
Temperature 374 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.017 cm/cm
0.017 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 10 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 79
79
ISO 2039-2
Hardness, Rockwell R 117
117
ISO 2039-2
Tensile Stress 8.20 MPa

@Strain 1.10 %,
Temperature 90.0 °C
 1190 psi

@Strain 1.10 %,
Temperature 194 °F
 ISO 11403-1 -2
21.0 MPa

@Strain 4.40 %,
Temperature 90.0 °C
 3050 psi

@Strain 4.40 %,
Temperature 194 °F
 ISO 11403-1 -2
21.7 MPa

@Strain 1.40 %,
Temperature 40.0 °C
 3150 psi

@Strain 1.40 %,
Temperature 104 °F
 ISO 11403-1 -2
25.8 MPa

@Strain 7.70 %,
Temperature 90.0 °C
 3740 psi

@Strain 7.70 %,
Temperature 194 °F
 ISO 11403-1 -2
26.1 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 3790 psi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
26.5 MPa

@Strain 11.0 %,
Temperature 90.0 °C
 3840 psi

@Strain 11.0 %,
Temperature 194 °F
 ISO 11403-1 -2
33.0 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 4790 psi

@Strain 1.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
40.5 MPa

@Strain 1.90 %,
Temperature 0.000 °C
 5870 psi

@Strain 1.90 %,
Temperature 32.0 °F
 ISO 11403-1 -2
44.2 MPa

@Strain 5.50 %,
Temperature 40.0 °C
 6410 psi

@Strain 5.50 %,
Temperature 104 °F
 ISO 11403-1 -2
46.5 MPa

@Strain 2.10 %,
Temperature -20.0 °C
 6740 psi

@Strain 2.10 %,
Temperature -4.00 °F
 ISO 11403-1 -2
47.5 MPa

@Strain 9.60 %,
Temperature 40.0 °C
 6890 psi

@Strain 9.60 %,
Temperature 104 °F
 ISO 11403-1 -2
50.1 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 7270 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
54.0 MPa

@Strain 8.80 %,
Temperature 23.0 °C
 7830 psi

@Strain 8.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
54.6 MPa

@Strain 12.6 %,
Temperature 23.0 °C
 7920 psi

@Strain 12.6 %,
Temperature 73.4 °F
 ISO 11403-1 -2
61.7 MPa

@Strain 7.60 %,
Temperature 0.000 °C
 8950 psi

@Strain 7.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
63.7 MPa

@Strain 13.2 %,
Temperature 0.000 °C
 9240 psi

@Strain 13.2 %,
Temperature 32.0 °F
 ISO 11403-1 -2
64.4 MPa

@Strain 18.4 %,
Temperature 0.000 °C
 9340 psi

@Strain 18.4 %,
Temperature 32.0 °F
 ISO 11403-1 -2
70.2 MPa

@Strain 8.30 %,
Temperature -20.0 °C
 10200 psi

@Strain 8.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
71.9 MPa

@Strain 14.5 %,
Temperature -20.0 °C
 10400 psi

@Strain 14.5 %,
Temperature -4.00 °F
 ISO 11403-1 -2
72.7 MPa

@Strain 19.9 %,
Temperature -20.0 °C
 10500 psi

@Strain 19.9 %,
Temperature -4.00 °F
 ISO 11403-1 -2
77.2 MPa

@Strain 9.60 %,
Temperature -40.0 °C
 11200 psi

@Strain 9.60 %,
Temperature -40.0 °F
 ISO 11403-1 -2
81.0 MPa

@Strain 19.2 %,
Temperature -40.0 °C
 11700 psi

@Strain 19.2 %,
Temperature -40.0 °F
 ISO 11403-1 -2
82.5 MPa

@Strain 28.8 %,
Temperature -40.0 °C
 12000 psi

@Strain 28.8 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 56.0 MPa
8120 psi
ISO 527-1/-2
Elongation at Break 35 %
35 %
Nominal; ISO 527-1/-2
Elongation at Yield 18 %
18 %
ISO 527-1/-2
Tensile Modulus 2.30 GPa
334 ksi
ISO 527-1/-2
Flexural Strength 60.0 MPa

@Strain 3.50 %
 8700 psi

@Strain 3.50 %
 ISO 178
Flexural Modulus 2.10 GPa
305 ksi
ISO 178
Shear Modulus 0.394 GPa

@Temperature 110 °C
 57.1 ksi

@Temperature 230 °F
 Dynamic; ISO 11403-1 -2
0.7691 GPa

@Temperature 60.0 °C
 111.6 ksi

@Temperature 140 °F
 Dynamic; ISO 11403-1 -2
1.0753 GPa

@Temperature 10.0 °C
 155.96 ksi

@Temperature 50.0 °F
 Dynamic; ISO 11403-1 -2
1.1915 GPa

@Temperature -20.0 °C
 172.82 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.3674 GPa

@Temperature -50.0 °C
 198.33 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.199 GPa

@Strain 11.1 %,
Temperature 100 °C
 28.9 ksi

@Strain 11.1 %,
Temperature 212 °F
 ISO 11403-1 -2
0.322 GPa

@Strain 9.20 %,
Temperature 80.0 °C
 46.7 ksi

@Strain 9.20 %,
Temperature 176 °F
 ISO 11403-1 -2
0.334 GPa

@Strain 5.60 %,
Temperature 100 °C
 48.4 ksi

@Strain 5.60 %,
Temperature 212 °F
 ISO 11403-1 -2
0.365 GPa

@Strain 22.4 %,
Temperature -40.0 °C
 53.0 ksi

@Strain 22.4 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.425 GPa

@Strain 15.1 %,
Temperature 0.000 °C
 61.6 ksi

@Strain 15.1 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.434 GPa

@Strain 11.0 %,
Temperature 40.0 °C
 62.9 ksi

@Strain 11.0 %,
Temperature 104 °F
 ISO 11403-1 -2
0.436 GPa

@Strain 16.6 %,
Temperature -20.0 °C
 63.2 ksi

@Strain 16.6 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.530 GPa

@Strain 4.60 %,
Temperature 80.0 °C
 76.9 ksi

@Strain 4.60 %,
Temperature 176 °F
 ISO 11403-1 -2
0.536 GPa

@Strain 1.40 %,
Temperature 100 °C
 77.7 ksi

@Strain 1.40 %,
Temperature 212 °F
 ISO 11403-1 -2
0.538 GPa

@Strain 10.1 %,
Temperature 23.0 °C
 78.0 ksi

@Strain 10.1 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.804 GPa

@Strain 5.50 %,
Temperature 40.0 °C
 117 ksi

@Strain 5.50 %,
Temperature 104 °F
 ISO 11403-1 -2
0.804 GPa

@Strain 9.60 %,
Temperature -40.0 °C
 117 ksi

@Strain 9.60 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.812 GPa

@Strain 7.60 %,
Temperature 0.000 °C
 118 ksi

@Strain 7.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.846 GPa

@Strain 8.30 %,
Temperature -20.0 °C
 123 ksi

@Strain 8.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.855 GPa

@Strain 1.10 %,
Temperature 80.0 °C
 124 ksi

@Strain 1.10 %,
Temperature 176 °F
 ISO 11403-1 -2
1.002 GPa

@Strain 5.00 %,
Temperature 23.0 °C
 145.3 ksi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.55 GPa

@Strain 1.40 %,
Temperature 40.0 °C
 225 ksi

@Strain 1.40 %,
Temperature 104 °F
 ISO 11403-1 -2