DuPont Performance Polymers Delrin® 500P NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500P NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium Viscosity Acetal Homopolymer with Improved Processing Delrin 500P is a medium viscosity acetal homopolymer for injection molding. It has improved processing thermal stability good mechanical properties and low volatile emissions.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 1.4 %

@Thickness 2.00 mm
1.4 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.300 %

@Thickness 2.00 mm
0.300 %

@Thickness 0.0787 in
Sim. to ISO 62
Viscosity 92857 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
92857 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
ISO 11403-1 -2
100600 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
100600 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
ISO 11403-1 -2
107100 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
107100 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
ISO 11403-1 -2
260530 cP

@Shear Rate 500 1/s,
Temperature 230 °C
260530 cP

@Shear Rate 500 1/s,
Temperature 446 °F
ISO 11403-1 -2
298700 cP

@Shear Rate 500 1/s,
Temperature 215 °C
298700 cP

@Shear Rate 500 1/s,
Temperature 419 °F
ISO 11403-1 -2
348640 cP

@Shear Rate 500 1/s,
Temperature 200 °C
348640 cP

@Shear Rate 500 1/s,
Temperature 392 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm³/10min; ISO 1133
15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Stress 5.40 MPa

@Strain 0.400 %,
Temperature 90.0 °C
783 psi

@Strain 0.400 %,
Temperature 194 °F
ISO 11403-1 -2
19.4 MPa

@Strain 0.600 %,
Temperature 23.0 °C
2810 psi

@Strain 0.600 %,
Temperature 73.4 °F
ISO 11403-1 -2
19.8 MPa

@Strain 1.90 %,
Temperature 90.0 °C
2870 psi

@Strain 1.90 %,
Temperature 194 °F
ISO 11403-1 -2
21.7 MPa

@Strain 0.700 %,
Temperature 0.000 °C
3150 psi

@Strain 0.700 %,
Temperature 32.0 °F
ISO 11403-1 -2
27.7 MPa

@Strain 3.30 %,
Temperature 90.0 °C
4020 psi

@Strain 3.30 %,
Temperature 194 °F
ISO 11403-1 -2
32.0 MPa

@Strain 4.70 %,
Temperature 90.0 °C
4640 psi

@Strain 4.70 %,
Temperature 194 °F
ISO 11403-1 -2
36.5 MPa

@Strain 1.00 %,
Temperature -40.0 °C
5290 psi

@Strain 1.00 %,
Temperature -40.0 °F
ISO 11403-1 -2
52.2 MPa

@Strain 2.60 %,
Temperature 23.0 °C
7570 psi

@Strain 2.60 %,
Temperature 73.4 °F
ISO 11403-1 -2
63.5 MPa

@Strain 4.70 %,
Temperature 23.0 °C
9210 psi

@Strain 4.70 %,
Temperature 73.4 °F
ISO 11403-1 -2
63.8 MPa

@Strain 2.90 %,
Temperature 0.000 °C
9250 psi

@Strain 2.90 %,
Temperature 32.0 °F
ISO 11403-1 -2
67.3 MPa

@Strain 7.00 %,
Temperature 23.0 °C
9760 psi

@Strain 7.00 %,
Temperature 73.4 °F
ISO 11403-1 -2
77.1 MPa

@Strain 5.00 %,
Temperature 0.000 °C
11200 psi

@Strain 5.00 %,
Temperature 32.0 °F
ISO 11403-1 -2
81.8 MPa

@Strain 8.00 %,
Temperature 0.000 °C
11900 psi

@Strain 8.00 %,
Temperature 32.0 °F
ISO 11403-1 -2
87.5 MPa

@Strain 4.20 %,
Temperature -40.0 °C
12700 psi

@Strain 4.20 %,
Temperature -40.0 °F
ISO 11403-1 -2
94.4 MPa

@Strain 7.00 %,
Temperature -40.0 °C
13700 psi

@Strain 7.00 %,
Temperature -40.0 °F
ISO 11403-1 -2
95.9 MPa

@Strain 10.0 %,
Temperature -40.0 °C
13900 psi

@Strain 10.0 %,
Temperature -40.0 °F
ISO 11403-1 -2
Tensile Strength, Yield 70.5 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 30 %
30 %
Nominal; ISO 527-1/-2
Elongation at Yield 17 %
17 %
ISO 527-1/-2
Tensile Modulus 3.10 GPa
450 ksi
ISO 527-1/-2
Flexural Strength 80.0 MPa

@Strain 3.50 %
11600 psi

@Strain 3.50 %
ISO 178
Flexural Modulus 2.95 GPa
428 ksi
ISO 178
Shear Modulus 0.275 GPa

@Temperature 120 °C
39.9 ksi

@Temperature 248 °F
Dynamic; ISO 11403-1 -2
0.5547 GPa

@Temperature 70.0 °C
80.45 ksi

@Temperature 158 °F
Dynamic; ISO 11403-1 -2
0.9459 GPa

@Temperature 20.0 °C
137.2 ksi

@Temperature 68.0 °F
Dynamic; ISO 11403-1 -2
1.1421 GPa

@Temperature -20.0 °C
165.65 ksi

@Temperature -4.00 °F
Dynamic; ISO 11403-1 -2
1.3715 GPa

@Temperature -50.0 °C
198.92 ksi

@Temperature -58.0 °F
Dynamic; ISO 11403-1 -2
Secant Modulus 0.538 GPa

@Strain 12.8 %,
Temperature 23.0 °C
78.1 ksi

@Strain 12.8 %,
Temperature 73.4 °F
ISO 11403-1 -2
0.603 GPa

@Strain 13.8 %,
Temperature 0.000 °C
87.4 ksi

@Strain 13.8 %,
Temperature 32.0 °F
ISO 11403-1 -2
0.760 GPa

@Strain 9.00 %,
Temperature 23.0 °C
110 ksi

@Strain 9.00 %,
Temperature 73.4 °F
ISO 11403-1 -2
0.8025 GPa

@Strain 12.0 %,
Temperature -40.0 °C
116.4 ksi

@Strain 12.0 %,
Temperature -40.0 °F
ISO 11403-1 -2
0.828 GPa

@Strain 10.0 %,
Temperature 0.000 °C
120 ksi

@Strain 10.0 %,
Temperature 32.0 °F
ISO 11403-1 -2
1.19 GPa

@Strain 8.00 %,
Temperature -40.0 °C
172 ksi

@Strain 8.00 %,
Temperature -40.0 °F
ISO 11403-1 -2
1.284 GPa

@Strain 5.00 %,
Temperature 23.0 °C
186.2 ksi

@Strain 5.00 %,
Temperature 73.4 °F
ISO 11403-1 -2
1.32 GPa

@Strain 6.00 %,
Temperature 0.000 °C
192 ksi

@Strain 6.00 %,
Temperature 32.0 °F
ISO 11403-1 -2
2.01 GPa

@Strain 2.60 %,
Temperature 23.0 °C
291 ksi

@Strain 2.60 %,
Temperature 73.4 °F
ISO 11403-1 -2
2.08 GPa

@Strain 4.20 %,
Temperature -40.0 °C
302 ksi

@Strain 4.20 %,
Temperature -40.0 °F
ISO 11403-1 -2
2.20 GPa

@Strain 2.90 %,
Temperature 0.000 °C
319 ksi

@Strain 2.90 %,
Temperature 32.0 °F
ISO 11403-1 -2
3.10 GPa

@Strain 0.700 %,
Temperature 0.000 °C
450 ksi

@Strain 0.700 %,
Temperature 32.0 °F
ISO 11403-1 -2
3.23 GPa

@Strain 0.600 %,
Temperature 23.0 °C
469 ksi

@Strain 0.600 %,
Temperature 73.4 °F
ISO 11403-1 -2
3.65 GPa

@Strain 1.00 %,
Temperature -40.0 °C
529 ksi

@Strain 1.00 %,
Temperature -40.0 °F
ISO 11403-1 -2
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
Charpy Impact Unnotched 32.5 J/cm²
155 ft-lb/in²
ISO 179/1eU
27.5 J/cm²

@Temperature -30.0 °C
131 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 2800 MPa

@Time 3600 sec
406000 psi

@Time 1.00 hour
ISO 899-1
Tensile Creep Modulus, 1000 hours 1600 MPa

@Time 3.60e+6 sec
232000 psi

@Time 1000 hour
ISO 899-1
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+14 ohm-cm
2.00e+14 ohm-cm
IEC 60093
Surface Resistance 4.00e+14 ohm
4.00e+14 ohm
IEC 60093