DuPont Performance Polymers Delrin® 127UV NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 127UV NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
UV Stabilized High Viscosity Acetal HomopolymerDelrin 127UV is a high viscosity acetal homopolymer with UV stabilizers developed for automotive interior applications. It has improvements in UV aging characteristics and thermal stability over Delrin 107Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 1.2 %

@Thickness 2.00 mm
 1.2 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.300 %

@Thickness 2.00 mm
 0.300 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 138000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 138000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
147000 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
 147000 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
 ISO 11403-1 -2
157000 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
 157000 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
 ISO 11403-1 -2
649000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 649000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
723000 cP

@Shear Rate 500 1/s,
Temperature 215 °C
 723000 cP

@Shear Rate 500 1/s,
Temperature 419 °F
 ISO 11403-1 -2
804000 cP

@Shear Rate 500 1/s,
Temperature 200 °C
 804000 cP

@Shear Rate 500 1/s,
Temperature 392 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.021 cm/cm
0.021 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Melt Flow 1.9 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 1.9 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
2.4 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.4 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Stress 10.0 MPa

@Strain 1.00 %,
Temperature 90.0 °C
 1450 psi

@Strain 1.00 %,
Temperature 194 °F
 ISO 11403-1 -2
27.0 MPa

@Strain 4.20 %,
Temperature 90.0 °C
 3920 psi

@Strain 4.20 %,
Temperature 194 °F
 ISO 11403-1 -2
32.5 MPa

@Strain 7.30 %,
Temperature 90.0 °C
 4710 psi

@Strain 7.30 %,
Temperature 194 °F
 ISO 11403-1 -2
33.4 MPa

@Strain 10.4 %,
Temperature 90.0 °C
 4840 psi

@Strain 10.4 %,
Temperature 194 °F
 ISO 11403-1 -2
33.9 MPa

@Strain 1.40 %,
Temperature 23.0 °C
 4920 psi

@Strain 1.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
35.9 MPa

@Strain 1.90 %,
Temperature 40.0 °C
 5210 psi

@Strain 1.90 %,
Temperature 104 °F
 ISO 11403-1 -2
50.1 MPa

@Strain 2.20 %,
Temperature 0.000 °C
 7270 psi

@Strain 2.20 %,
Temperature 32.0 °F
 ISO 11403-1 -2
55.0 MPa

@Strain 2.10 %,
Temperature -40.0 °C
 7980 psi

@Strain 2.10 %,
Temperature -40.0 °F
 ISO 11403-1 -2
57.1 MPa

@Strain 7.70 %,
Temperature 40.0 °C
 8280 psi

@Strain 7.70 %,
Temperature 104 °F
 ISO 11403-1 -2
59.8 MPa

@Strain 2.60 %,
Temperature -20.0 °C
 8670 psi

@Strain 2.60 %,
Temperature -4.00 °F
 ISO 11403-1 -2
60.1 MPa

@Strain 13.4 %,
Temperature 40.0 °C
 8720 psi

@Strain 13.4 %,
Temperature 104 °F
 ISO 11403-1 -2
60.8 MPa

@Strain 5.40 %,
Temperature 23.0 °C
 8820 psi

@Strain 5.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
66.0 MPa

@Strain 9.50 %,
Temperature 23.0 °C
 9570 psi

@Strain 9.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
67.3 MPa

@Strain 13.6 %,
Temperature 23.0 °C
 9760 psi

@Strain 13.6 %,
Temperature 73.4 °F
 ISO 11403-1 -2
73.2 MPa

@Strain 8.80 %,
Temperature 0.000 °C
 10600 psi

@Strain 8.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
76.1 MPa

@Strain 15.4 %,
Temperature 0.000 °C
 11000 psi

@Strain 15.4 %,
Temperature 32.0 °F
 ISO 11403-1 -2
77.1 MPa

@Strain 21.4 %,
Temperature 0.000 °C
 11200 psi

@Strain 21.4 %,
Temperature 32.0 °F
 ISO 11403-1 -2
81.4 MPa

@Strain 10.4 %,
Temperature -20.0 °C
 11800 psi

@Strain 10.4 %,
Temperature -4.00 °F
 ISO 11403-1 -2
84.5 MPa

@Strain 18.2 %,
Temperature -20.0 °C
 12300 psi

@Strain 18.2 %,
Temperature -4.00 °F
 ISO 11403-1 -2
85.3 MPa

@Strain 26.0 %,
Temperature -20.0 °C
 12400 psi

@Strain 26.0 %,
Temperature -4.00 °F
 ISO 11403-1 -2
96.0 MPa

@Strain 12.6 %,
Temperature -40.0 °C
 13900 psi

@Strain 12.6 %,
Temperature -40.0 °F
 ISO 11403-1 -2
97.9 MPa

@Strain 25.1 %,
Temperature -40.0 °C
 14200 psi

@Strain 25.1 %,
Temperature -40.0 °F
 ISO 11403-1 -2
98.8 MPa

@Strain 37.7 %,
Temperature -40.0 °C
 14300 psi

@Strain 37.7 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 45 %
45 %
Nominal; ISO 527-1/-2
Elongation at Yield 23 %
23 %
ISO 527-1/-2
Tensile Modulus 3.00 GPa
435 ksi
ISO 527-1/-2
Flexural Modulus 2.70 GPa
392 ksi
ISO 178
Shear Modulus 0.2165 GPa

@Temperature 120 °C
 31.40 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.4832 GPa

@Temperature 70.0 °C
 70.08 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.8266 GPa

@Temperature 20.0 °C
 119.9 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
0.980 GPa

@Temperature -20.0 °C
 142 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.1339 GPa

@Temperature -50.0 °C
 164.46 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.31978 GPa

@Strain 9.10 %,
Temperature 100 °C
 46.381 ksi

@Strain 9.10 %,
Temperature 212 °F
 ISO 11403-1 -2
0.336 GPa

@Strain 29.3 %,
Temperature -40.0 °C
 48.7 ksi

@Strain 29.3 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.37551 GPa

@Strain 9.80 %,
Temperature 80.0 °C
 54.464 ksi

@Strain 9.80 %,
Temperature 176 °F
 ISO 11403-1 -2
0.392 GPa

@Strain 15.4 %,
Temperature 40.0 °C
 56.8 ksi

@Strain 15.4 %,
Temperature 104 °F
 ISO 11403-1 -2
0.408 GPa

@Strain 20.8 %,
Temperature -20.0 °C
 59.2 ksi

@Strain 20.8 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.435 GPa

@Strain 17.6 %,
Temperature 0.000 °C
 63.0 ksi

@Strain 17.6 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.520 GPa

@Strain 4.50 %,
Temperature 100 °C
 75.4 ksi

@Strain 4.50 %,
Temperature 212 °F
 ISO 11403-1 -2
0.611 GPa

@Strain 10.9 %,
Temperature 23.0 °C
 88.6 ksi

@Strain 10.9 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.639 GPa

@Strain 4.90 %,
Temperature 80.0 °C
 92.6 ksi

@Strain 4.90 %,
Temperature 176 °F
 ISO 11403-1 -2
0.742 GPa

@Strain 7.70 %,
Temperature 40.0 °C
 108 ksi

@Strain 7.70 %,
Temperature 104 °F
 ISO 11403-1 -2
0.762 GPa

@Strain 12.6 %,
Temperature -40.0 °C
 111 ksi

@Strain 12.6 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.783 GPa

@Strain 10.4 %,
Temperature -20.0 °C
 114 ksi

@Strain 10.4 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.827 GPa

@Strain 1.10 %,
Temperature 100 °C
 120 ksi

@Strain 1.10 %,
Temperature 212 °F
 ISO 11403-1 -2
0.832 GPa

@Strain 8.80 %,
Temperature 0.000 °C
 121 ksi

@Strain 8.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
1.05 GPa

@Strain 1.20 %,
Temperature 80.0 °C
 152 ksi

@Strain 1.20 %,
Temperature 176 °F
 ISO 11403-1 -2
1.13 GPa

@Strain 5.40 %,
Temperature 23.0 °C
 163 ksi

@Strain 5.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.89 GPa

@Strain 1.90 %,
Temperature 40.0 °C
 274 ksi

@Strain 1.90 %,
Temperature 104 °F
 ISO 11403-1 -2
2.28 GPa

@Strain 2.20 %,
Temperature 0.000 °C
 330 ksi

@Strain 2.20 %,
Temperature 32.0 °F
 ISO 11403-1 -2