DuPont Performance Polymers Delrin® 100ST NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced, Impact Grade
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 100ST NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Super Toughened High Viscosity Acetal Homopolymer Delrin 100ST NC010 is a super tough high viscosity acetal homopolymer grade with superior impact resistance. It is designed for highly stressed parts where outstanding toughness is essential.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Water Absorption 0.90 %

@Thickness 2.00 mm
 0.90 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.350 %

@Thickness 2.00 mm
 0.350 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 148000 cP

@Shear Rate 5000 1/s,
Temperature 220 °C
 148000 cP

@Shear Rate 5000 1/s,
Temperature 428 °F
 ISO 11403-1 -2
171000 cP

@Shear Rate 5000 1/s,
Temperature 205 °C
 171000 cP

@Shear Rate 5000 1/s,
Temperature 401 °F
 ISO 11403-1 -2
201000 cP

@Shear Rate 5000 1/s,
Temperature 190 °C
 201000 cP

@Shear Rate 5000 1/s,
Temperature 374 °F
 ISO 11403-1 -2
688000 cP

@Shear Rate 500 1/s,
Temperature 220 °C
 688000 cP

@Shear Rate 500 1/s,
Temperature 428 °F
 ISO 11403-1 -2
856000 cP

@Shear Rate 500 1/s,
Temperature 205 °C
 856000 cP

@Shear Rate 500 1/s,
Temperature 401 °F
 ISO 11403-1 -2
1.058e+6 cP

@Shear Rate 500 1/s,
Temperature 190 °C
 1.058e+6 cP

@Shear Rate 500 1/s,
Temperature 374 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
ISO 294-4 2577
Melt Flow 1.7 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 1.7 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 58
58
ISO 2039-2
Hardness, Rockwell R 105
105
ISO 2039-2
Tensile Stress 6.10 MPa

@Strain 2.00 %,
Temperature 90.0 °C
 885 psi

@Strain 2.00 %,
Temperature 194 °F
 ISO 11403-1 -2
14.3 MPa

@Strain 7.90 %,
Temperature 90.0 °C
 2070 psi

@Strain 7.90 %,
Temperature 194 °F
 ISO 11403-1 -2
15.5 MPa

@Strain 2.00 %,
Temperature 40.0 °C
 2250 psi

@Strain 2.00 %,
Temperature 104 °F
 ISO 11403-1 -2
16.9 MPa

@Strain 13.9 %,
Temperature 90.0 °C
 2450 psi

@Strain 13.9 %,
Temperature 194 °F
 ISO 11403-1 -2
17.6 MPa

@Strain 19.8 %,
Temperature 90.0 °C
 2550 psi

@Strain 19.8 %,
Temperature 194 °F
 ISO 11403-1 -2
18.3 MPa

@Strain 2.10 %,
Temperature 23.0 °C
 2650 psi

@Strain 2.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
27.5 MPa

@Strain 3.00 %,
Temperature 0.000 °C
 3990 psi

@Strain 3.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
29.8 MPa

@Strain 7.80 %,
Temperature 40.0 °C
 4320 psi

@Strain 7.80 %,
Temperature 104 °F
 ISO 11403-1 -2
33.5 MPa

@Strain 13.7 %,
Temperature 40.0 °C
 4860 psi

@Strain 13.7 %,
Temperature 104 °F
 ISO 11403-1 -2
34.6 MPa

@Strain 19.5 %,
Temperature 40.0 °C
 5020 psi

@Strain 19.5 %,
Temperature 104 °F
 ISO 11403-1 -2
34.7 MPa

@Strain 3.70 %,
Temperature -20.0 °C
 5030 psi

@Strain 3.70 %,
Temperature -4.00 °F
 ISO 11403-1 -2
35.0 MPa

@Strain 8.50 %,
Temperature 23.0 °C
 5080 psi

@Strain 8.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
39.2 MPa

@Strain 14.8 %,
Temperature 23.0 °C
 5690 psi

@Strain 14.8 %,
Temperature 73.4 °F
 ISO 11403-1 -2
40.3 MPa

@Strain 21.2 %,
Temperature 23.0 °C
 5850 psi

@Strain 21.2 %,
Temperature 73.4 °F
 ISO 11403-1 -2
44.9 MPa

@Strain 12.1 %,
Temperature 0.000 °C
 6510 psi

@Strain 12.1 %,
Temperature 32.0 °F
 ISO 11403-1 -2
47.5 MPa

@Strain 21.2 %,
Temperature 0.000 °C
 6890 psi

@Strain 21.2 %,
Temperature 32.0 °F
 ISO 11403-1 -2
48.3 MPa

@Strain 30.3 %,
Temperature 0.000 °C
 7010 psi

@Strain 30.3 %,
Temperature 32.0 °F
 ISO 11403-1 -2
51.6 MPa

@Strain 14.8 %,
Temperature -20.0 °C
 7480 psi

@Strain 14.8 %,
Temperature -4.00 °F
 ISO 11403-1 -2
54.9 MPa

@Strain 25.9 %,
Temperature -20.0 °C
 7960 psi

@Strain 25.9 %,
Temperature -4.00 °F
 ISO 11403-1 -2
56.0 MPa

@Strain 34.5 %,
Temperature -20.0 °C
 8120 psi

@Strain 34.5 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Tensile Strength, Yield 41.0 MPa
5950 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
Nominal; ISO 527-1/-2
Elongation at Yield 30 %
30 %
ISO 527-1/-2
Tensile Modulus 1.40 GPa
203 ksi
ISO 527-1/-2
0.363 GPa

@Temperature 110 °C
 52.7 ksi

@Temperature 230 °F
 Dynamic; ISO 11403-1 -2
1.3427 GPa

@Temperature 30.0 °C
 194.74 ksi

@Temperature 86.0 °F
 Dynamic; ISO 11403-1 -2
2.03 GPa

@Temperature -20.0 °C
 294 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
5.48 GPa

@Temperature -70.0 °C
 794 ksi

@Temperature -94.0 °F
 Dynamic; ISO 11403-1 -2
8.17 GPa

@Temperature -100 °C
 1180 ksi

@Temperature -148 °F
 Dynamic; ISO 11403-1 -2
Flexural Strength 34.0 MPa

@Strain 3.50 %
 4930 psi

@Strain 3.50 %
 ISO 178
Flexural Modulus 1.10 GPa
160 ksi
ISO 178
Shear Modulus 0.0911 GPa

@Temperature 120 °C
 13.2 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.2153 GPa

@Temperature 70.0 °C
 31.23 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.4067 GPa

@Temperature 20.0 °C
 58.99 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
0.6135 GPa

@Temperature -20.0 °C
 88.98 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.1443 GPa

@Temperature -50.0 °C
 165.97 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.187 GPa

@Strain 29.6 %,
Temperature -20.0 °C
 27.1 ksi

@Strain 29.6 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.198 GPa

@Strain 24.2 %,
Temperature 0.000 °C
 28.6 ksi

@Strain 24.2 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.21859 GPa

@Strain 15.6 %,
Temperature 40.0 °C
 31.704 ksi

@Strain 15.6 %,
Temperature 104 °F
 ISO 11403-1 -2
0.234 GPa

@Strain 17.0 %,
Temperature 23.0 °C
 34.0 ksi

@Strain 17.0 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.349 GPa

@Strain 14.8 %,
Temperature -20.0 °C
 50.6 ksi

@Strain 14.8 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.371 GPa

@Strain 12.1 %,
Temperature 0.000 °C
 53.8 ksi

@Strain 12.1 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.382 GPa

@Strain 7.80 %,
Temperature 40.0 °C
 55.4 ksi

@Strain 7.80 %,
Temperature 104 °F
 ISO 11403-1 -2
0.412 GPa

@Strain 8.50 %,
Temperature 23.0 °C
 59.7 ksi

@Strain 8.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.775 GPa

@Strain 2.00 %,
Temperature 40.0 °C
 112 ksi

@Strain 2.00 %,
Temperature 104 °F
 ISO 11403-1 -2
0.871 GPa

@Strain 2.10 %,
Temperature 23.0 °C
 126 ksi

@Strain 2.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.917 GPa

@Strain 3.00 %,
Temperature 0.000 °C
 133 ksi

@Strain 3.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.938 GPa

@Strain 3.70 %,
Temperature -20.0 °C
 136 ksi

@Strain 3.70 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 90.0 kJ/m²
42.8 ft-lb/in²
ISO 180/1A
20.0 kJ/m²

@Temperature -40.0 °C
 9.52 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU