DuPont Performance Polymers Delrin® 100ST BK602 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced, Impact Grade
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 100ST BK602 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Super Toughened High Viscosity Acetal Homopolymer Delrin 100ST BK602 is a super tough high viscosity acetal homopolymer grade with superior impact resistance. It is designed for highly stressed parts where outstanding toughness is essential.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
ISO 294-4 2577
Melt Flow 2.1 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.1 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 40.0 MPa
5800 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
Nominal; ISO 527-1/-2
Elongation at Yield 30 %
30 %
ISO 527-1/-2
Tensile Modulus 1.20 GPa
174 ksi
ISO 527-1/-2
Flexural Modulus 1.10 GPa
160 ksi
ISO 178
Shear Modulus 0.0351 GPa

@Temperature 160 °C
5.09 ksi

@Temperature 320 °F
Dynamic; ISO 11403-1 -2
0.0816 GPa

@Temperature 120 °C
11.8 ksi

@Temperature 248 °F
Dynamic; ISO 11403-1 -2
0.1884 GPa

@Temperature 70.0 °C
27.33 ksi

@Temperature 158 °F
Dynamic; ISO 11403-1 -2
0.3691 GPa

@Temperature 20.0 °C
53.53 ksi

@Temperature 68.0 °F
Dynamic; ISO 11403-1 -2
0.5982 GPa

@Temperature -20.0 °C
86.76 ksi

@Temperature -4.00 °F
Dynamic; ISO 11403-1 -2
1.1904 GPa

@Temperature -50.0 °C
172.66 ksi

@Temperature -58.0 °F
Dynamic; ISO 11403-1 -2
Charpy Impact, Notched 8.00 J/cm²
38.1 ft-lb/in²
ISO 179/1eA
1.40 J/cm²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 102 °C
216 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Emissions <8 mg/kg
VDA 275
Part Marking Code >POM-HI<
ISO 11469
Processing Blow Moulding
Coatable
Injection Moulding
Other Extrusion
Profile Extrusion
Sheet Extrusion
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM-HI
ISO 1043