DuPont Performance Polymers Delrin® 100PE NC010A Acetal Homopolymer

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	DuPont Performance Polymers
Trade Name	Delrin®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 100PE NC010A Acetal Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Delrin® 100PE NC010A is a high viscosity acetal homopolymer, an enhanced version of Delrin® 100P with extremely low VOC emissions. It has improved processing thermal stability, good mechanical properties, and toughness.Information provided by DuPont

Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/in³	ISO 1183
Water Absorption	0.30 % @Temperature 23.0 °C	0.30 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62, Similar to
	0.60 % @Temperature 23.0 °C	0.60 % @Temperature 73.4 °F	Immersion 24h; ISO 62, Similar to
	1.4 % @Temperature 23.0 °C	1.4 % @Temperature 73.4 °F	Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage	0.020 cm/cm @Thickness 2.00 mm	0.020 in/in @Thickness 0.0787 in	Normal; ISO 294-4
	0.022 cm/cm @Thickness 2.00 mm	0.022 in/in @Thickness 0.0787 in	Parallel; ISO 294-4
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	70.0 MPa @Temperature 23.0 °C	10200 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	45 % @Temperature 23.0 °C	45 % @Temperature 73.4 °F	ISO 527
Elongation at Yield	22 % @Temperature 23.0 °C	22 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	2.90 GPa @Temperature 23.0 °C	421 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	2.60 GPa @Temperature 23.0 °C	377 ksi @Temperature 73.4 °F	ISO 178
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	1.40 J/cm² @Temperature 23.0 °C	6.66 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1 hour	2700 MPa @Temperature 23.0 °C	392000 psi @Temperature 73.4 °F	ISO 899
Tensile Creep Modulus, 1000 hours	1500 MPa @Temperature 23.0 °C	218000 psi @Temperature 73.4 °F	ISO 899

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 µm/m-°C @Temperature -40.0 - 23.0 °C	55.6 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	110 µm/m-°C @Temperature 23.0 - 55.0 °C	61.1 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	160 µm/m-°C @Temperature 55.0 - 100 °C	88.9 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C @Temperature -40.0 - 23.0 °C	55.6 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	110 µm/m-°C @Temperature 23.0 - 55.0 °C	61.1 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	160 µm/m-°C @Temperature 55.0 - 100 °C	88.9 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	92.0 °C	198 °F	ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	205 °C	401 °F	Optimum; Injection Molding
	200 - 210 °C	392 - 410 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	Optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.20 %	<= 0.20 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Natural Color
Features	Creep Resistance, Good
	Dimensional Stability, Good
	Fatigue Resistant
	Homopolymer
	Impact Resistance, High
	Molecular Wt., High
	Stiffness, High
	Strength, High
	Toughness, Good
	Viscosity, High
	VOC, Low
Forms	Pellets
Generic	Acetal (POM) Homopolymer
Material Status	Preliminary Data
Part Marking Code	>POM<	ISO 11469
Polymer Family	POM
Polymer Type	POM Homopolymer
Processing Method	Extrusion
	Injection Molding
Product Category	Extrusion Resins
	Low Emissions Resins
	Unreinforced Resins
Region Available - Global	Yes
Resin Identification	POM	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Automotive Interior Parts
	Fasteners
	Gears
	Parts, Engineering