DuPont Performance Polymers Delrin® 100KM NC000 Acetal (POM) (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer	DuPont Performance Polymers
Trade Name	Delrin®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 100KM NC000 Acetal (POM) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Kevlar® Modified High Viscosity Acetal Homopolymer with Low Wear and Low FrictionDelrin 100KM is a high viscosity acetal homopolymer resin modified with Kevlar aramid resin. It is designed for applications requiring low wear in abrasive environments.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³
	1.41 g/cc	0.0509 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.018 cm/cm	0.018 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.015 cm/cm	0.015 in/in	ISO 294-4 2577
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	cm³/10min; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	65.0 MPa	9430 psi	ISO 527-1/-2
Elongation at Break	15 %	15 %	ISO 527-1/-2
Tensile Modulus	3.10 GPa	450 ksi	ISO 527-1/-2
Flexural Modulus	3.00 GPa	435 ksi	ISO 178
Charpy Impact Unnotched	5.00 J/cm²	23.8 ft-lb/in²	ISO 179/1eU
	6.00 J/cm² @Temperature -30.0 °C	28.6 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.450 J/cm²	2.14 ft-lb/in²	ISO 179/1eA
	0.350 J/cm² @Temperature -30.0 °C	1.67 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	110 µm/m-°C	61.1 µin/in-°F	ISO 11359-1/-2
	94.0 µm/m-°C @Temperature -40.0 - 23.0 °C	52.2 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-1/-2
	92.0 µm/m-°C @Temperature -40.0 - 23.0 °C	51.1 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	160 °C	320 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	98.0 °C	208 °F	ISO 75-1/-2

Descriptive Properties	Value	Comments
Additives	Lubricants
	Release agent
Delivery Form	Pellets
Part Marking Code	>POM-AG<	ISO 11469
Processing	Injection Moulding
	Other Extrusion
	Profile Extrusion
	Sheet Extrusion
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	POM-AG	ISO 1043