DuPont Performance Polymers Delrin® 100 NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 100 NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Viscosity Acetal Homopolymer Delrin 100 is a high viscosity acetal homopolymer for use in easy to fill molds. Delrin 100 provides maximum toughness in the product line without modification and optimum mechanical performance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.90 %

@Thickness 2.00 mm
0.90 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
0.200 %

@Thickness 0.0787 in
Sim. to ISO 62
Viscosity 143400 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
143400 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
ISO 11403-1 -2
162300 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
162300 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
ISO 11403-1 -2
171900 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
171900 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
ISO 11403-1 -2
721700 cP

@Shear Rate 500 1/s,
Temperature 230 °C
721700 cP

@Shear Rate 500 1/s,
Temperature 446 °F
ISO 11403-1 -2
793400 cP

@Shear Rate 500 1/s,
Temperature 215 °C
793400 cP

@Shear Rate 500 1/s,
Temperature 419 °F
ISO 11403-1 -2
804400 cP

@Shear Rate 500 1/s,
Temperature 200 °C
804400 cP

@Shear Rate 500 1/s,
Temperature 392 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.022 cm/cm
0.022 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Melt Flow 1.9 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.9 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm³/10min; ISO 1133
2.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90
90
ISO 2039-2
Hardness, Rockwell R 121
121
ISO 2039-2
Tensile Stress 9.90 MPa

@Strain 1.00 %,
Temperature 90.0 °C
1440 psi

@Strain 1.00 %,
Temperature 194 °F
ISO 11403-1 -2
20.0 MPa

@Strain 0.500 %,
Temperature -20.0 °C
2900 psi

@Strain 0.500 %,
Temperature -4.00 °F
ISO 11403-1 -2
26.8 MPa

@Strain 3.80 %,
Temperature 90.0 °C
3890 psi

@Strain 3.80 %,
Temperature 194 °F
ISO 11403-1 -2
30.7 MPa

@Strain 1.40 %,
Temperature 40.0 °C
4450 psi

@Strain 1.40 %,
Temperature 104 °F
ISO 11403-1 -2
30.9 MPa

@Strain 1.20 %,
Temperature 23.0 °C
4480 psi

@Strain 1.20 %,
Temperature 73.4 °F
ISO 11403-1 -2
32.4 MPa

@Strain 6.60 %,
Temperature 90.0 °C
4700 psi

@Strain 6.60 %,
Temperature 194 °F
ISO 11403-1 -2
33.4 MPa

@Strain 9.50 %,
Temperature 90.0 °C
4840 psi

@Strain 9.50 %,
Temperature 194 °F
ISO 11403-1 -2
41.0 MPa

@Strain 1.50 %,
Temperature 0.000 °C
5950 psi

@Strain 1.50 %,
Temperature 32.0 °F
ISO 11403-1 -2
53.7 MPa

@Strain 5.80 %,
Temperature 40.0 °C
7790 psi

@Strain 5.80 %,
Temperature 104 °F
ISO 11403-1 -2
58.6 MPa

@Strain 10.1 %,
Temperature 40.0 °C
8500 psi

@Strain 10.1 %,
Temperature 104 °F
ISO 11403-1 -2
58.8 MPa

@Strain 4.70 %,
Temperature 23.0 °C
8530 psi

@Strain 4.70 %,
Temperature 73.4 °F
ISO 11403-1 -2
59.6 MPa

@Strain 14.4 %,
Temperature 40.0 °C
8640 psi

@Strain 14.4 %,
Temperature 104 °F
ISO 11403-1 -2
65.4 MPa

@Strain 9.40 %,
Temperature 23.0 °C
9490 psi

@Strain 9.40 %,
Temperature 73.4 °F
ISO 11403-1 -2
66.8 MPa

@Strain 14.0 %,
Temperature 23.0 °C
9690 psi

@Strain 14.0 %,
Temperature 73.4 °F
ISO 11403-1 -2
67.0 MPa

@Strain 4.00 %,
Temperature -20.0 °C
9720 psi

@Strain 4.00 %,
Temperature -4.00 °F
ISO 11403-1 -2
72.1 MPa

@Strain 8.00 %,
Temperature 0.000 °C
10500 psi

@Strain 8.00 %,
Temperature 32.0 °F
ISO 11403-1 -2
75.1 MPa

@Strain 16.0 %,
Temperature 0.000 °C
10900 psi

@Strain 16.0 %,
Temperature 32.0 °F
ISO 11403-1 -2
76.3 MPa

@Strain 24.0 %,
Temperature 0.000 °C
11100 psi

@Strain 24.0 %,
Temperature 32.0 °F
ISO 11403-1 -2
79.5 MPa

@Strain 10.5 %,
Temperature -20.0 °C
11500 psi

@Strain 10.5 %,
Temperature -4.00 °F
ISO 11403-1 -2
81.0 MPa

@Strain 17.0 %,
Temperature -20.0 °C
11700 psi

@Strain 17.0 %,
Temperature -4.00 °F
ISO 11403-1 -2
Tensile Strength, Yield 72.0 MPa
10400 psi
ISO 527-1/-2
Elongation at Break 45 %
45 %
Nominal; ISO 527-1/-2
Elongation at Yield 26 %
26 %
ISO 527-1/-2
Tensile Modulus 3.15 GPa
457 ksi
ISO 527-1/-2
Flexural Strength 79.0 MPa

@Strain 3.50 %
11500 psi

@Strain 3.50 %
ISO 178
Flexural Modulus 2.90 GPa
421 ksi
ISO 178
Shear Modulus 0.0961 GPa

@Temperature 160 °C
13.9 ksi

@Temperature 320 °F
Dynamic; ISO 11403-1 -2
0.2156 GPa

@Temperature 120 °C
31.27 ksi

@Temperature 248 °F
Dynamic; ISO 11403-1 -2
0.4857 GPa

@Temperature 70.0 °C
70.45 ksi

@Temperature 158 °F
Dynamic; ISO 11403-1 -2
0.8779 GPa

@Temperature 20.0 °C
127.3 ksi

@Temperature 68.0 °F
Dynamic; ISO 11403-1 -2
1.079 GPa

@Temperature -20.0 °C
156.5 ksi

@Temperature -4.00 °F
Dynamic; ISO 11403-1 -2
1.286 GPa

@Temperature -50.0 °C
186.5 ksi

@Temperature -58.0 °F
Dynamic; ISO 11403-1 -2
Secant Modulus 0.409 GPa

@Strain 18.5 %,
Temperature 0.000 °C
59.3 ksi

@Strain 18.5 %,
Temperature 32.0 °F
ISO 11403-1 -2
0.515 GPa

@Strain 11.5 %,
Temperature 40.0 °C
74.7 ksi

@Strain 11.5 %,
Temperature 104 °F
ISO 11403-1 -2
0.607 GPa

@Strain 10.9 %,
Temperature 23.0 °C
88.1 ksi

@Strain 10.9 %,
Temperature 73.4 °F
ISO 11403-1 -2
0.6408 GPa

@Strain 12.5 %,
Temperature -20.0 °C
92.94 ksi

@Strain 12.5 %,
Temperature -4.00 °F
ISO 11403-1 -2
0.90125 GPa

@Strain 8.00 %,
Temperature 0.000 °C
130.72 ksi

@Strain 8.00 %,
Temperature 32.0 °F
ISO 11403-1 -2
0.926 GPa

@Strain 5.80 %,
Temperature 40.0 °C
134 ksi

@Strain 5.80 %,
Temperature 104 °F
ISO 11403-1 -2
1.25 GPa

@Strain 4.70 %,
Temperature 23.0 °C
181 ksi

@Strain 4.70 %,
Temperature 73.4 °F
ISO 11403-1 -2
1.675 GPa

@Strain 4.00 %,
Temperature -20.0 °C
242.9 ksi

@Strain 4.00 %,
Temperature -4.00 °F
ISO 11403-1 -2
2.19 GPa

@Strain 1.40 %,
Temperature 40.0 °C
318 ksi

@Strain 1.40 %,
Temperature 104 °F
ISO 11403-1 -2
2.575 GPa

@Strain 1.20 %,
Temperature 23.0 °C
373.5 ksi

@Strain 1.20 %,
Temperature 73.4 °F
ISO 11403-1 -2
2.73 GPa

@Strain 1.50 %,
Temperature 0.000 °C
396 ksi

@Strain 1.50 %,
Temperature 32.0 °F
ISO 11403-1 -2
4.00 GPa

@Strain 0.500 %,
Temperature -20.0 °C
580 ksi

@Strain 0.500 %,
Temperature -4.00 °F
ISO 11403-1 -2
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
ISO 180/1A
13.0 kJ/m²

@Temperature -40.0 °C
6.19 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
42.5 J/cm²

@Temperature -30.0 °C
202 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
ISO 179/1eA
1.40 J/cm²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA